- 密度 [g/cm3]: 1.37
- 缺口冲击强度: 1.1
- 弯曲模量 [MPa]: 5.52
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Specific Gravity | 1.37 g/cc | 1.37 g/cc | DAM; ASTM D792 | ||
Density | 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 | ||
Filler Content | 30 % | 30 % | DAM | ||
Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
Linear Mold Shrinkage, Transverse | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 130 MPa @Temperature 23.0 °C | 18900 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
195 MPa @Temperature 23.0 °C | 28300 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
Tensile Strength | 117 MPa @Temperature 23.0 °C | 17000 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
180 MPa @Temperature 23.0 °C | 26100 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
Tensile Stress | 3.90 MPa @Strain 0.100 %, Temperature 150 °C | 566 psi @Strain 0.100 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | ||
4.797 MPa @Strain 0.100 %, Temperature 120 °C | 695.7 psi @Strain 0.100 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
4.845 MPa @Strain 0.100 %, Temperature 120 °C | 702.7 psi @Strain 0.100 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
5.066 MPa @Strain 0.100 %, Temperature 100 °C | 734.8 psi @Strain 0.100 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
5.404 MPa @Strain 0.100 %, Temperature 100 °C | 783.8 psi @Strain 0.100 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
5.526 MPa @Strain 0.100 %, Temperature 80.0 °C | 801.5 psi @Strain 0.100 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
5.801 MPa @Strain 0.100 %, Temperature 80.0 °C | 841.4 psi @Strain 0.100 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
6.465 MPa @Strain 0.100 %, Temperature 60.0 °C | 937.7 psi @Strain 0.100 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
7.251 MPa @Strain 0.100 %, Temperature 60.0 °C | 1052 psi @Strain 0.100 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
7.293 MPa @Strain 0.100 %, Temperature 23.0 °C | 1058 psi @Strain 0.100 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
8.50 MPa @Strain 0.200 %, Temperature 150 °C | 1230 psi @Strain 0.200 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
8.557 MPa @Strain 0.100 %, Temperature 0.000 °C | 1241 psi @Strain 0.100 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
8.845 MPa @Strain 0.100 %, Temperature -40.0 °C | 1283 psi @Strain 0.100 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
9.808 MPa @Strain 0.100 %, Temperature 23.0 °C | 1423 psi @Strain 0.100 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
9.968 MPa @Strain 0.100 %, Temperature -40.0 °C | 1446 psi @Strain 0.100 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
10.542 MPa @Strain 0.100 %, Temperature 0.000 °C | 1529.0 psi @Strain 0.100 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
10.668 MPa @Strain 0.200 %, Temperature 120 °C | 1547.3 psi @Strain 0.200 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
10.938 MPa @Strain 0.200 %, Temperature 100 °C | 1586.4 psi @Strain 0.200 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
11.219 MPa @Strain 0.200 %, Temperature 120 °C | 1627.2 psi @Strain 0.200 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
12.194 MPa @Strain 0.200 %, Temperature 80.0 °C | 1768.6 psi @Strain 0.200 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
12.373 MPa @Strain 0.200 %, Temperature 80.0 °C | 1794.6 psi @Strain 0.200 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
12.623 MPa @Strain 0.200 %, Temperature 60.0 °C | 1830.8 psi @Strain 0.200 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
12.777 MPa @Strain 0.200 %, Temperature 100 °C | 1853.2 psi @Strain 0.200 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
12.8 MPa @Strain 0.300 %, Temperature 150 °C | 1860 psi @Strain 0.300 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
14.511 MPa @Strain 0.200 %, Temperature 60.0 °C | 2104.6 psi @Strain 0.200 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
14.575 MPa @Strain 0.200 %, Temperature 23.0 °C | 2113.9 psi @Strain 0.200 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
15.496 MPa @Strain 0.300 %, Temperature 120 °C | 2247.5 psi @Strain 0.300 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
16.088 MPa @Strain 0.300 %, Temperature 120 °C | 2333.4 psi @Strain 0.300 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
16.232 MPa @Strain 0.300 %, Temperature 100 °C | 2354.3 psi @Strain 0.300 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
16.3 MPa @Strain 0.400 %, Temperature 150 °C | 2360 psi @Strain 0.400 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
16.858 MPa @Strain 0.200 %, Temperature 0.000 °C | 2445.1 psi @Strain 0.200 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
16.965 MPa @Strain 0.200 %, Temperature -40.0 °C | 2460.6 psi @Strain 0.200 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
17.74 MPa @Strain 0.300 %, Temperature 80.0 °C | 2573 psi @Strain 0.300 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
17.856 MPa @Strain 0.300 %, Temperature 80.0 °C | 2589.8 psi @Strain 0.300 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
18.464 MPa @Strain 0.300 %, Temperature 60.0 °C | 2678.0 psi @Strain 0.300 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
18.531 MPa @Strain 0.300 %, Temperature 100 °C | 2687.7 psi @Strain 0.300 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
19.184 MPa @Strain 0.200 %, Temperature 23.0 °C | 2782.4 psi @Strain 0.200 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
19.348 MPa @Strain 0.400 %, Temperature 120 °C | 2806.2 psi @Strain 0.400 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
19.437 MPa @Strain 0.200 %, Temperature -40.0 °C | 2819.1 psi @Strain 0.200 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
19.691 MPa @Strain 0.400 %, Temperature 120 °C | 2855.9 psi @Strain 0.400 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
20.036 MPa @Strain 0.200 %, Temperature 0.000 °C | 2906.0 psi @Strain 0.200 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
20.212 MPa @Strain 0.400 %, Temperature 100 °C | 2931.5 psi @Strain 0.400 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
20.954 MPa @Strain 0.300 %, Temperature 23.0 °C | 3039.1 psi @Strain 0.300 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
21.292 MPa @Strain 0.300 %, Temperature 60.0 °C | 3088.1 psi @Strain 0.300 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
21.795 MPa @Strain 0.400 %, Temperature 80.0 °C | 3161.1 psi @Strain 0.400 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
22.0 MPa @Strain 0.500 %, Temperature 150 °C | 3190 psi @Strain 0.500 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
22.424 MPa @Strain 0.400 %, Temperature 80.0 °C | 3252.3 psi @Strain 0.400 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
22.931 MPa @Strain 0.400 %, Temperature 60.0 °C | 3325.9 psi @Strain 0.400 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
23.034 MPa @Strain 0.400 %, Temperature 100 °C | 3340.8 psi @Strain 0.400 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
24.253 MPa @Strain 0.500 %, Temperature 120 °C | 3517.6 psi @Strain 0.500 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
24.413 MPa @Strain 0.300 %, Temperature 0.000 °C | 3540.8 psi @Strain 0.300 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
24.614 MPa @Strain 0.500 %, Temperature 120 °C | 3570.0 psi @Strain 0.500 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
25.241 MPa @Strain 0.300 %, Temperature -40.0 °C | 3660.9 psi @Strain 0.300 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
25.981 MPa @Strain 0.400 %, Temperature 23.0 °C | 3768.2 psi @Strain 0.400 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
26.4 MPa @Strain 0.600 %, Temperature 150 °C | 3830 psi @Strain 0.600 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
26.549 MPa @Strain 0.500 %, Temperature 100 °C | 3850.6 psi @Strain 0.500 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
26.808 MPa @Strain 0.400 %, Temperature 60.0 °C | 3888.2 psi @Strain 0.400 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
27.007 MPa @Strain 0.500 %, Temperature 80.0 °C | 3917.0 psi @Strain 0.500 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
27.556 MPa @Strain 0.600 %, Temperature 120 °C | 3996.7 psi @Strain 0.600 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
27.753 MPa @Strain 0.500 %, Temperature 100 °C | 4025.2 psi @Strain 0.500 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
28.181 MPa @Strain 0.300 %, Temperature 23.0 °C | 4087.3 psi @Strain 0.300 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
28.643 MPa @Strain 0.600 %, Temperature 120 °C | 4154.3 psi @Strain 0.600 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
28.757 MPa @Strain 0.500 %, Temperature 80.0 °C | 4170.9 psi @Strain 0.500 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
28.886 MPa @Strain 0.300 %, Temperature -40.0 °C | 4189.6 psi @Strain 0.300 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
28.902 MPa @Strain 0.500 %, Temperature 60.0 °C | 4191.9 psi @Strain 0.500 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
29.778 MPa @Strain 0.300 %, Temperature 0.000 °C | 4318.9 psi @Strain 0.300 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
29.8 MPa @Strain 0.700 %, Temperature 150 °C | 4320 psi @Strain 0.700 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
30.866 MPa @Strain 0.400 %, Temperature 0.000 °C | 4476.7 psi @Strain 0.400 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
30.877 MPa @Strain 0.700 %, Temperature 120 °C | 4478.3 psi @Strain 0.700 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
30.981 MPa @Strain 0.600 %, Temperature 80.0 °C | 4493.4 psi @Strain 0.600 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
30.984 MPa @Strain 0.600 %, Temperature 100 °C | 4493.9 psi @Strain 0.600 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
31.416 MPa @Strain 0.600 %, Temperature 100 °C | 4556.5 psi @Strain 0.600 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
32.41 MPa @Strain 0.400 %, Temperature -40.0 °C | 4701 psi @Strain 0.400 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
32.666 MPa @Strain 0.700 %, Temperature 120 °C | 4737.8 psi @Strain 0.700 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
33.1 MPa @Strain 0.800 %, Temperature 150 °C | 4800 psi @Strain 0.800 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
33.411 MPa @Strain 0.600 %, Temperature 60.0 °C | 4845.9 psi @Strain 0.600 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
33.795 MPa @Strain 0.500 %, Temperature 23.0 °C | 4901.6 psi @Strain 0.500 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
33.843 MPa @Strain 0.600 %, Temperature 80.0 °C | 4908.5 psi @Strain 0.600 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
34.071 MPa @Strain 0.800 %, Temperature 120 °C | 4941.6 psi @Strain 0.800 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
34.809 MPa @Strain 0.700 %, Temperature 80.0 °C | 5048.6 psi @Strain 0.700 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
34.908 MPa @Strain 0.700 %, Temperature 100 °C | 5063.0 psi @Strain 0.700 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
35.008 MPa @Strain 0.500 %, Temperature 60.0 °C | 5077.5 psi @Strain 0.500 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
35.402 MPa @Strain 0.700 %, Temperature 100 °C | 5134.6 psi @Strain 0.700 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
35.868 MPa @Strain 0.400 %, Temperature 23.0 °C | 5202.2 psi @Strain 0.400 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
35.9 MPa @Strain 0.900 %, Temperature 150 °C | 5210 psi @Strain 0.900 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
36.242 MPa @Strain 0.800 %, Temperature 120 °C | 5256.5 psi @Strain 0.800 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
36.777 MPa @Strain 0.400 %, Temperature -40.0 °C | 5334.1 psi @Strain 0.400 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
37.04 MPa @Strain 0.900 %, Temperature 120 °C | 5372 psi @Strain 0.900 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
37.796 MPa @Strain 0.700 %, Temperature 60.0 °C | 5481.9 psi @Strain 0.700 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
37.976 MPa @Strain 0.400 %, Temperature 0.000 °C | 5508.0 psi @Strain 0.400 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
38.218 MPa @Strain 0.800 %, Temperature 100 °C | 5543.1 psi @Strain 0.800 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
38.568 MPa @Strain 0.800 %, Temperature 80.0 °C | 5593.8 psi @Strain 0.800 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
38.67 MPa @Strain 0.700 %, Temperature 80.0 °C | 5609 psi @Strain 0.700 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
39.0 MPa @Strain 1.00 %, Temperature 150 °C | 5660 psi @Strain 1.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
39.456 MPa @Strain 0.800 %, Temperature 100 °C | 5722.6 psi @Strain 0.800 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
39.495 MPa @Strain 0.900 %, Temperature 120 °C | 5728.3 psi @Strain 0.900 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
39.872 MPa @Strain 1.00 %, Temperature 120 °C | 5783.0 psi @Strain 1.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
39.876 MPa @Strain 0.600 %, Temperature 23.0 °C | 5783.5 psi @Strain 0.600 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
41.411 MPa @Strain 0.900 %, Temperature 100 °C | 6006.2 psi @Strain 0.900 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
41.422 MPa @Strain 0.600 %, Temperature 60.0 °C | 6007.8 psi @Strain 0.600 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
41.7 MPa @Strain 1.10 %, Temperature 150 °C | 6050 psi @Strain 1.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
41.712 MPa @Strain 0.500 %, Temperature 0.000 °C | 6049.8 psi @Strain 0.500 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
42.059 MPa @Strain 0.800 %, Temperature 60.0 °C | 6100.2 psi @Strain 0.800 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
42.148 MPa @Strain 0.900 %, Temperature 80.0 °C | 6113.1 psi @Strain 0.900 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
42.456 MPa @Strain 1.10 %, Temperature 120 °C | 6157.7 psi @Strain 1.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
42.755 MPa @Strain 1.00 %, Temperature 120 °C | 6201.1 psi @Strain 1.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
43.071 MPa @Strain 0.800 %, Temperature 80.0 °C | 6246.9 psi @Strain 0.800 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
43.093 MPa @Strain 0.900 %, Temperature 100 °C | 6250.1 psi @Strain 0.900 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
43.931 MPa @Strain 0.500 %, Temperature -40.0 °C | 6371.7 psi @Strain 0.500 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
44.205 MPa @Strain 1.00 %, Temperature 100 °C | 6411.4 psi @Strain 1.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
44.3 MPa @Strain 1.20 %, Temperature 150 °C | 6430 psi @Strain 1.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
45.075 MPa @Strain 1.20 %, Temperature 120 °C | 6537.6 psi @Strain 1.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
45.233 MPa @Strain 1.00 %, Temperature 80.0 °C | 6560.5 psi @Strain 1.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
45.557 MPa @Strain 0.700 %, Temperature 23.0 °C | 6607.5 psi @Strain 0.700 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
45.591 MPa @Strain 0.900 %, Temperature 60.0 °C | 6612.4 psi @Strain 0.900 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
45.967 MPa @Strain 1.10 %, Temperature 120 °C | 6667.0 psi @Strain 1.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
46.246 MPa @Strain 0.500 %, Temperature 23.0 °C | 6707.4 psi @Strain 0.500 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
46.72 MPa @Strain 1.00 %, Temperature 100 °C | 6776 psi @Strain 1.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
46.9 MPa @Strain 1.30 %, Temperature 150 °C | 6800 psi @Strain 1.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
47.117 MPa @Strain 1.10 %, Temperature 100 °C | 6833.8 psi @Strain 1.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
47.474 MPa @Strain 0.900 %, Temperature 80.0 °C | 6885.5 psi @Strain 0.900 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
47.639 MPa @Strain 1.30 %, Temperature 120 °C | 6909.5 psi @Strain 1.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
47.931 MPa @Strain 0.700 %, Temperature 60.0 °C | 6951.8 psi @Strain 0.700 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
48.27 MPa @Strain 0.500 %, Temperature -40.0 °C | 7001 psi @Strain 0.500 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
48.541 MPa @Strain 1.10 %, Temperature 80.0 °C | 7040.3 psi @Strain 1.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
48.951 MPa @Strain 0.500 %, Temperature 0.000 °C | 7099.8 psi @Strain 0.500 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
49.002 MPa @Strain 1.20 %, Temperature 120 °C | 7107.2 psi @Strain 1.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
49.02 MPa @Strain 0.600 %, Temperature 0.000 °C | 7110 psi @Strain 0.600 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
49.2 MPa @Strain 1.40 %, Temperature 150 °C | 7140 psi @Strain 1.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
49.637 MPa @Strain 1.00 %, Temperature 60.0 °C | 7199.3 psi @Strain 1.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
50.014 MPa @Strain 1.20 %, Temperature 100 °C | 7253.9 psi @Strain 1.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
50.14 MPa @Strain 1.40 %, Temperature 120 °C | 7272 psi @Strain 1.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
50.249 MPa @Strain 1.10 %, Temperature 100 °C | 7288.0 psi @Strain 1.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
50.622 MPa @Strain 0.800 %, Temperature 23.0 °C | 7342.1 psi @Strain 0.800 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
51.6 MPa @Strain 1.50 %, Temperature 150 °C | 7480 psi @Strain 1.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
51.678 MPa @Strain 1.00 %, Temperature 80.0 °C | 7495.3 psi @Strain 1.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
51.799 MPa @Strain 1.20 %, Temperature 80.0 °C | 7512.8 psi @Strain 1.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
51.921 MPa @Strain 1.30 %, Temperature 120 °C | 7530.5 psi @Strain 1.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
52.366 MPa @Strain 1.50 %, Temperature 120 °C | 7595.1 psi @Strain 1.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
52.606 MPa @Strain 1.30 %, Temperature 100 °C | 7629.9 psi @Strain 1.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
52.696 MPa @Strain 0.600 %, Temperature -40.0 °C | 7642.9 psi @Strain 0.600 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
53.352 MPa @Strain 1.10 %, Temperature 60.0 °C | 7738.1 psi @Strain 1.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
53.517 MPa @Strain 1.20 %, Temperature 100 °C | 7762.0 psi @Strain 1.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
53.6 MPa @Strain 1.60 %, Temperature 150 °C | 7770 psi @Strain 1.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
54.399 MPa @Strain 0.800 %, Temperature 60.0 °C | 7889.9 psi @Strain 0.800 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
54.561 MPa @Strain 1.60 %, Temperature 120 °C | 7913.4 psi @Strain 1.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
54.774 MPa @Strain 1.40 %, Temperature 120 °C | 7944.3 psi @Strain 1.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
54.847 MPa @Strain 1.30 %, Temperature 80.0 °C | 7954.9 psi @Strain 1.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
54.855 MPa @Strain 0.600 %, Temperature 23.0 °C | 7956.1 psi @Strain 0.600 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
54.971 MPa @Strain 1.40 %, Temperature 100 °C | 7972.9 psi @Strain 1.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
55.378 MPa @Strain 1.10 %, Temperature 80.0 °C | 8031.9 psi @Strain 1.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
55.5 MPa @Strain 1.70 %, Temperature 150 °C | 8050 psi @Strain 1.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
56.261 MPa @Strain 0.900 %, Temperature 23.0 °C | 8160.0 psi @Strain 0.900 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
56.697 MPa @Strain 1.70 %, Temperature 120 °C | 8223.2 psi @Strain 1.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
56.708 MPa @Strain 1.30 %, Temperature 100 °C | 8224.8 psi @Strain 1.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
56.792 MPa @Strain 1.20 %, Temperature 60.0 °C | 8237.0 psi @Strain 1.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
57.233 MPa @Strain 1.50 %, Temperature 100 °C | 8301.0 psi @Strain 1.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
57.4 MPa @Strain 1.80 %, Temperature 150 °C | 8330 psi @Strain 1.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
57.503 MPa @Strain 1.50 %, Temperature 120 °C | 8340.1 psi @Strain 1.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
57.701 MPa @Strain 1.40 %, Temperature 80.0 °C | 8368.8 psi @Strain 1.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
58.167 MPa @Strain 0.600 %, Temperature -40.0 °C | 8436.4 psi @Strain 0.600 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
58.392 MPa @Strain 0.700 %, Temperature 0.000 °C | 8469.1 psi @Strain 0.700 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
58.626 MPa @Strain 1.80 %, Temperature 120 °C | 8503.0 psi @Strain 1.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
58.918 MPa @Strain 1.20 %, Temperature 80.0 °C | 8545.3 psi @Strain 1.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
59.268 MPa @Strain 0.600 %, Temperature 0.000 °C | 8596.1 psi @Strain 0.600 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
59.3 MPa @Strain 1.90 %, Temperature 150 °C | 8600 psi @Strain 1.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
59.449 MPa @Strain 1.60 %, Temperature 100 °C | 8622.4 psi @Strain 1.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
59.764 MPa @Strain 1.40 %, Temperature 100 °C | 8668.1 psi @Strain 1.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
59.995 MPa @Strain 1.30 %, Temperature 60.0 °C | 8701.6 psi @Strain 1.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
60.094 MPa @Strain 1.60 %, Temperature 120 °C | 8715.9 psi @Strain 1.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
60.259 MPa @Strain 0.900 %, Temperature 60.0 °C | 8739.8 psi @Strain 0.900 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
60.484 MPa @Strain 1.50 %, Temperature 80.0 °C | 8772.5 psi @Strain 1.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
60.523 MPa @Strain 1.90 %, Temperature 120 °C | 8778.1 psi @Strain 1.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
61.0 MPa @Strain 2.00 %, Temperature 150 °C | 8850 psi @Strain 2.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
61.386 MPa @Strain 1.00 %, Temperature 23.0 °C | 8903.3 psi @Strain 1.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
61.54 MPa @Strain 1.70 %, Temperature 100 °C | 8926 psi @Strain 1.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
62.196 MPa @Strain 2.00 %, Temperature 120 °C | 9020.8 psi @Strain 2.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
62.223 MPa @Strain 0.700 %, Temperature -40.0 °C | 9024.7 psi @Strain 0.700 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
62.337 MPa @Strain 1.30 %, Temperature 80.0 °C | 9041.2 psi @Strain 1.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
62.576 MPa @Strain 1.70 %, Temperature 120 °C | 9075.9 psi @Strain 1.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
62.634 MPa @Strain 1.50 %, Temperature 100 °C | 9084.3 psi @Strain 1.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
62.7 MPa @Strain 2.10 %, Temperature 150 °C | 9090 psi @Strain 2.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
63.132 MPa @Strain 1.40 %, Temperature 60.0 °C | 9156.5 psi @Strain 1.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
63.173 MPa @Strain 1.60 %, Temperature 80.0 °C | 9162.5 psi @Strain 1.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
63.452 MPa @Strain 0.700 %, Temperature 23.0 °C | 9203.0 psi @Strain 0.700 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
63.497 MPa @Strain 1.80 %, Temperature 100 °C | 9209.5 psi @Strain 1.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
63.881 MPa @Strain 2.10 %, Temperature 120 °C | 9265.2 psi @Strain 2.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
64.1 MPa @Strain 2.20 %, Temperature 150 °C | 9300 psi @Strain 2.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
64.939 MPa @Strain 1.80 %, Temperature 120 °C | 9418.6 psi @Strain 1.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
65.42 MPa @Strain 1.90 %, Temperature 100 °C | 9488 psi @Strain 1.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
65.425 MPa @Strain 1.60 %, Temperature 100 °C | 9489.1 psi @Strain 1.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
65.488 MPa @Strain 2.20 %, Temperature 120 °C | 9498.2 psi @Strain 2.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
65.584 MPa @Strain 1.40 %, Temperature 80.0 °C | 9512.2 psi @Strain 1.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
65.6 MPa @Strain 2.30 %, Temperature 150 °C | 9510 psi @Strain 2.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
65.611 MPa @Strain 1.00 %, Temperature 60.0 °C | 9516.1 psi @Strain 1.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
65.631 MPa @Strain 1.70 %, Temperature 80.0 °C | 9519.0 psi @Strain 1.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
66.177 MPa @Strain 1.50 %, Temperature 60.0 °C | 9598.2 psi @Strain 1.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
66.299 MPa @Strain 1.10 %, Temperature 23.0 °C | 9615.9 psi @Strain 1.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
66.57 MPa @Strain 0.800 %, Temperature 0.000 °C | 9655 psi @Strain 0.800 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
66.985 MPa @Strain 2.30 %, Temperature 120 °C | 9715.4 psi @Strain 2.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
67.0 MPa @Strain 2.40 %, Temperature 150 °C | 9720 psi @Strain 2.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
67.237 MPa @Strain 1.90 %, Temperature 120 °C | 9751.9 psi @Strain 1.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
67.272 MPa @Strain 2.00 %, Temperature 100 °C | 9757.0 psi @Strain 2.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
67.696 MPa @Strain 0.700 %, Temperature -40.0 °C | 9818.5 psi @Strain 0.700 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
68.015 MPa @Strain 1.80 %, Temperature 80.0 °C | 9864.8 psi @Strain 1.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
68.215 MPa @Strain 1.70 %, Temperature 100 °C | 9893.8 psi @Strain 1.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
68.386 MPa @Strain 2.40 %, Temperature 120 °C | 9918.6 psi @Strain 2.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
68.4 MPa @Strain 2.50 %, Temperature 150 °C | 9920 psi @Strain 2.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
68.649 MPa @Strain 0.700 %, Temperature 0.000 °C | 9956.7 psi @Strain 0.700 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
68.847 MPa @Strain 1.50 %, Temperature 80.0 °C | 9985.4 psi @Strain 1.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
69.004 MPa @Strain 2.10 %, Temperature 100 °C | 10008 psi @Strain 2.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
69.043 MPa @Strain 1.60 %, Temperature 60.0 °C | 10014 psi @Strain 1.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
69.467 MPa @Strain 2.00 %, Temperature 120 °C | 10075 psi @Strain 2.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
69.698 MPa @Strain 2.50 %, Temperature 120 °C | 10109 psi @Strain 2.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
69.7 MPa @Strain 2.60 %, Temperature 150 °C | 10100 psi @Strain 2.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
70.315 MPa @Strain 1.90 %, Temperature 80.0 °C | 10198 psi @Strain 1.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
70.56 MPa @Strain 2.20 %, Temperature 100 °C | 10230 psi @Strain 2.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
70.6 MPa @Strain 2.70 %, Temperature 150 °C | 10200 psi @Strain 2.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
70.852 MPa @Strain 1.10 %, Temperature 60.0 °C | 10276 psi @Strain 1.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
70.904 MPa @Strain 1.80 %, Temperature 100 °C | 10284 psi @Strain 1.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
70.935 MPa @Strain 2.60 %, Temperature 120 °C | 10288 psi @Strain 2.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
70.989 MPa @Strain 1.20 %, Temperature 23.0 °C | 10296 psi @Strain 1.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
71.572 MPa @Strain 0.800 %, Temperature -40.0 °C | 10381 psi @Strain 0.800 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
71.611 MPa @Strain 2.10 %, Temperature 120 °C | 10386 psi @Strain 2.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
71.765 MPa @Strain 0.800 %, Temperature 23.0 °C | 10409 psi @Strain 0.800 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
71.808 MPa @Strain 1.70 %, Temperature 60.0 °C | 10415 psi @Strain 1.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
72.0 MPa @Strain 2.80 %, Temperature 150 °C | 10400 psi @Strain 2.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
72.055 MPa @Strain 1.60 %, Temperature 80.0 °C | 10451 psi @Strain 1.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
72.084 MPa @Strain 2.70 %, Temperature 120 °C | 10455 psi @Strain 2.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
72.097 MPa @Strain 2.30 %, Temperature 100 °C | 10457 psi @Strain 2.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
72.557 MPa @Strain 2.00 %, Temperature 80.0 °C | 10524 psi @Strain 2.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
72.7 MPa @Strain 2.90 %, Temperature 150 °C | 10500 psi @Strain 2.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
73.089 MPa @Strain 2.80 %, Temperature 120 °C | 10601 psi @Strain 2.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
73.45 MPa @Strain 2.40 %, Temperature 100 °C | 10650 psi @Strain 2.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
73.457 MPa @Strain 1.90 %, Temperature 100 °C | 10654 psi @Strain 1.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
73.506 MPa @Strain 2.20 %, Temperature 120 °C | 10661 psi @Strain 2.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
74.0 MPa @Strain 3.00 %, Temperature 150 °C | 10700 psi @Strain 3.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
74.063 MPa @Strain 2.90 %, Temperature 120 °C | 10742 psi @Strain 2.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
74.437 MPa @Strain 1.80 %, Temperature 60.0 °C | 10796 psi @Strain 1.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
74.52 MPa @Strain 0.900 %, Temperature 0.000 °C | 10810 psi @Strain 0.900 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
74.561 MPa @Strain 2.10 %, Temperature 80.0 °C | 10814 psi @Strain 2.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
74.7 MPa @Strain 3.10 %, Temperature 150 °C | 10800 psi @Strain 3.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
74.739 MPa @Strain 2.50 %, Temperature 100 °C | 10840 psi @Strain 2.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
74.912 MPa @Strain 3.00 %, Temperature 120 °C | 10865 psi @Strain 3.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
75.155 MPa @Strain 1.70 %, Temperature 80.0 °C | 10900 psi @Strain 1.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
75.484 MPa @Strain 1.30 %, Temperature 23.0 °C | 10948 psi @Strain 1.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
75.5 MPa @Strain 3.20 %, Temperature 150 °C | 11000 psi @Strain 3.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
75.53 MPa @Strain 2.30 %, Temperature 120 °C | 10950 psi @Strain 2.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
75.776 MPa @Strain 3.10 %, Temperature 120 °C | 10990 psi @Strain 3.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
75.868 MPa @Strain 1.20 %, Temperature 60.0 °C | 11004 psi @Strain 1.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
75.882 MPa @Strain 2.60 %, Temperature 100 °C | 11006 psi @Strain 2.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
75.895 MPa @Strain 2.00 %, Temperature 100 °C | 11008 psi @Strain 2.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
76.4 MPa @Strain 3.30 %, Temperature 150 °C | 11100 psi @Strain 3.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
76.493 MPa @Strain 3.20 %, Temperature 120 °C | 11094 psi @Strain 3.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
76.505 MPa @Strain 2.20 %, Temperature 80.0 °C | 11096 psi @Strain 2.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
76.973 MPa @Strain 1.90 %, Temperature 60.0 °C | 11164 psi @Strain 1.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
77.003 MPa @Strain 2.70 %, Temperature 100 °C | 11168 psi @Strain 2.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
77.1 MPa @Strain 3.40 %, Temperature 150 °C | 11200 psi @Strain 3.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
77.223 MPa @Strain 3.30 %, Temperature 120 °C | 11200 psi @Strain 3.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
77.312 MPa @Strain 0.800 %, Temperature -40.0 °C | 11213 psi @Strain 0.800 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
77.434 MPa @Strain 2.40 %, Temperature 120 °C | 11231 psi @Strain 2.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
77.7 MPa @Strain 3.50 %, Temperature 150 °C | 11300 psi @Strain 3.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
77.861 MPa @Strain 3.40 %, Temperature 120 °C | 11293 psi @Strain 3.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
77.972 MPa @Strain 2.80 %, Temperature 100 °C | 11309 psi @Strain 2.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
78.105 MPa @Strain 1.80 %, Temperature 80.0 °C | 11328 psi @Strain 1.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
78.238 MPa @Strain 0.800 %, Temperature 0.000 °C | 11347 psi @Strain 0.800 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
78.294 MPa @Strain 2.10 %, Temperature 100 °C | 11356 psi @Strain 2.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
78.306 MPa @Strain 2.30 %, Temperature 80.0 °C | 11357 psi @Strain 2.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
78.4 MPa @Strain 3.60 %, Temperature 150 °C | 11400 psi @Strain 3.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
78.429 MPa @Strain 3.50 %, Temperature 120 °C | 11375 psi @Strain 3.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
78.874 MPa @Strain 2.90 %, Temperature 100 °C | 11440 psi @Strain 2.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
78.9 MPa @Strain 3.70 %, Temperature 150 °C | 11400 psi @Strain 3.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
79.029 MPa @Strain 3.60 %, Temperature 120 °C | 11462 psi @Strain 3.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
79.251 MPa @Strain 2.50 %, Temperature 120 °C | 11494 psi @Strain 2.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
79.338 MPa @Strain 2.00 %, Temperature 60.0 °C | 11507 psi @Strain 2.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
79.49 MPa @Strain 3.70 %, Temperature 120 °C | 11530 psi @Strain 3.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
79.697 MPa @Strain 3.00 %, Temperature 100 °C | 11559 psi @Strain 3.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
79.7 MPa @Strain 3.80 %, Temperature 150 °C | 11600 psi @Strain 3.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
79.822 MPa @Strain 1.40 %, Temperature 23.0 °C | 11577 psi @Strain 1.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
79.992 MPa @Strain 3.80 %, Temperature 120 °C | 11602 psi @Strain 3.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
80.012 MPa @Strain 2.40 %, Temperature 80.0 °C | 11605 psi @Strain 2.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
80.04 MPa @Strain 0.900 %, Temperature 23.0 °C | 11610 psi @Strain 0.900 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
80.1 MPa @Strain 3.90 %, Temperature 150 °C | 11600 psi @Strain 3.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
80.439 MPa @Strain 3.10 %, Temperature 100 °C | 11667 psi @Strain 3.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
80.443 MPa @Strain 3.90 %, Temperature 120 °C | 11667 psi @Strain 3.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
80.597 MPa @Strain 2.20 %, Temperature 100 °C | 11690 psi @Strain 2.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
80.6 MPa @Strain 4.00 %, Temperature 150 °C | 11700 psi @Strain 4.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
80.611 MPa @Strain 1.30 %, Temperature 60.0 °C | 11692 psi @Strain 1.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
80.739 MPa @Strain 0.900 %, Temperature -40.0 °C | 11710 psi @Strain 0.900 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
80.793 MPa @Strain 4.00 %, Temperature 120 °C | 11718 psi @Strain 4.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
80.889 MPa @Strain 1.90 %, Temperature 80.0 °C | 11732 psi @Strain 1.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
80.9 MPa @Strain 4.10 %, Temperature 150 °C | 11700 psi @Strain 4.10 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
80.922 MPa @Strain 2.60 %, Temperature 120 °C | 11737 psi @Strain 2.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
81.165 MPa @Strain 3.20 %, Temperature 100 °C | 11772 psi @Strain 3.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
81.249 MPa @Strain 4.10 %, Temperature 120 °C | 11784 psi @Strain 4.10 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
81.4 MPa @Strain 4.20 %, Temperature 150 °C | 11800 psi @Strain 4.20 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
81.543 MPa @Strain 2.10 %, Temperature 60.0 °C | 11827 psi @Strain 2.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
81.57 MPa @Strain 4.20 %, Temperature 120 °C | 11830 psi @Strain 4.20 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
81.61 MPa @Strain 2.50 %, Temperature 80.0 °C | 11840 psi @Strain 2.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
81.755 MPa @Strain 3.30 %, Temperature 100 °C | 11858 psi @Strain 3.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
81.866 MPa @Strain 4.30 %, Temperature 120 °C | 11874 psi @Strain 4.30 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
82.1 MPa @Strain 4.30 %, Temperature 150 °C | 11900 psi @Strain 4.30 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
82.18 MPa @Strain 1.00 %, Temperature 0.000 °C | 11920 psi @Strain 1.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
82.24 MPa @Strain 4.40 %, Temperature 120 °C | 11930 psi @Strain 4.40 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
82.363 MPa @Strain 3.40 %, Temperature 100 °C | 11946 psi @Strain 3.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
82.477 MPa @Strain 4.50 %, Temperature 120 °C | 11962 psi @Strain 4.50 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
82.497 MPa @Strain 2.70 %, Temperature 120 °C | 11965 psi @Strain 2.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
82.6 MPa @Strain 4.40 %, Temperature 150 °C | 12000 psi @Strain 4.40 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
82.6 MPa @Strain 4.50 %, Temperature 150 °C | 12000 psi @Strain 4.50 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
82.743 MPa @Strain 4.60 %, Temperature 120 °C | 12001 psi @Strain 4.60 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
82.8 MPa @Strain 4.60 %, Temperature 150 °C | 12000 psi @Strain 4.60 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
82.838 MPa @Strain 2.30 %, Temperature 100 °C | 12015 psi @Strain 2.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
82.89 MPa @Strain 3.50 %, Temperature 100 °C | 12020 psi @Strain 3.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
83.021 MPa @Strain 2.60 %, Temperature 80.0 °C | 12041 psi @Strain 2.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
83.051 MPa @Strain 4.70 %, Temperature 120 °C | 12046 psi @Strain 4.70 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
83.2 MPa @Strain 4.70 %, Temperature 150 °C | 12100 psi @Strain 4.70 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
83.218 MPa @Strain 4.80 %, Temperature 120 °C | 12070 psi @Strain 4.80 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
83.355 MPa @Strain 3.60 %, Temperature 100 °C | 12090 psi @Strain 3.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
83.4 MPa @Strain 4.80 %, Temperature 150 °C | 12100 psi @Strain 4.80 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
83.436 MPa @Strain 4.90 %, Temperature 120 °C | 12101 psi @Strain 4.90 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
83.604 MPa @Strain 2.00 %, Temperature 80.0 °C | 12126 psi @Strain 2.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
83.67 MPa @Strain 5.00 %, Temperature 120 °C | 12140 psi @Strain 5.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
83.726 MPa @Strain 2.20 %, Temperature 60.0 °C | 12143 psi @Strain 2.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
83.865 MPa @Strain 3.70 %, Temperature 100 °C | 12164 psi @Strain 3.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
83.958 MPa @Strain 2.80 %, Temperature 120 °C | 12177 psi @Strain 2.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
84.016 MPa @Strain 1.50 %, Temperature 23.0 °C | 12186 psi @Strain 1.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
84.1 MPa @Strain 4.90 %, Temperature 150 °C | 12200 psi @Strain 4.90 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
84.227 MPa @Strain 3.80 %, Temperature 100 °C | 12216 psi @Strain 3.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
84.372 MPa @Strain 2.70 %, Temperature 80.0 °C | 12237 psi @Strain 2.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
84.5 MPa @Strain 5.00 %, Temperature 150 °C | 12300 psi @Strain 5.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
84.586 MPa @Strain 6.00 %, Temperature 120 °C | 12268 psi @Strain 6.00 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
84.62 MPa @Strain 3.90 %, Temperature 100 °C | 12270 psi @Strain 3.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
84.938 MPa @Strain 2.40 %, Temperature 100 °C | 12319 psi @Strain 2.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
84.983 MPa @Strain 1.40 %, Temperature 60.0 °C | 12326 psi @Strain 1.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
85.064 MPa @Strain 4.00 %, Temperature 100 °C | 12338 psi @Strain 4.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
85.279 MPa @Strain 4.10 %, Temperature 100 °C | 12369 psi @Strain 4.10 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
85.506 MPa @Strain 2.90 %, Temperature 120 °C | 12402 psi @Strain 2.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
85.567 MPa @Strain 2.80 %, Temperature 80.0 °C | 12410 psi @Strain 2.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
85.637 MPa @Strain 4.20 %, Temperature 100 °C | 12421 psi @Strain 4.20 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
85.763 MPa @Strain 2.30 %, Temperature 60.0 °C | 12439 psi @Strain 2.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
85.8 MPa @Strain 6.00 %, Temperature 150 °C | 12400 psi @Strain 6.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
85.983 MPa @Strain 4.30 %, Temperature 100 °C | 12471 psi @Strain 4.30 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
86.131 MPa @Strain 4.40 %, Temperature 100 °C | 12492 psi @Strain 4.40 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
86.157 MPa @Strain 2.10 %, Temperature 80.0 °C | 12496 psi @Strain 2.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
86.428 MPa @Strain 4.50 %, Temperature 100 °C | 12535 psi @Strain 4.50 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
86.585 MPa @Strain 0.900 %, Temperature -40.0 °C | 12558 psi @Strain 0.900 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
86.72 MPa @Strain 4.60 %, Temperature 100 °C | 12580 psi @Strain 4.60 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
86.727 MPa @Strain 2.90 %, Temperature 80.0 °C | 12579 psi @Strain 2.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
86.838 MPa @Strain 3.00 %, Temperature 120 °C | 12595 psi @Strain 3.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
86.885 MPa @Strain 4.70 %, Temperature 100 °C | 12602 psi @Strain 4.70 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
86.951 MPa @Strain 2.50 %, Temperature 100 °C | 12611 psi @Strain 2.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
87.012 MPa @Strain 4.80 %, Temperature 100 °C | 12620 psi @Strain 4.80 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
87.266 MPa @Strain 4.90 %, Temperature 100 °C | 12657 psi @Strain 4.90 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
87.354 MPa @Strain 0.900 %, Temperature 0.000 °C | 12670 psi @Strain 0.900 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
87.433 MPa @Strain 5.00 %, Temperature 100 °C | 12681 psi @Strain 5.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
87.5 MPa @Strain 7.00 %, Temperature 150 °C | 12700 psi @Strain 7.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
87.674 MPa @Strain 2.40 %, Temperature 60.0 °C | 12716 psi @Strain 2.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
87.7 MPa @Strain 8.00 %, Temperature 150 °C | 12700 psi @Strain 8.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
87.7 MPa @Strain 3.00 %, Temperature 80.0 °C | 12700 psi @Strain 3.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
88.041 MPa @Strain 1.60 %, Temperature 23.0 °C | 12769 psi @Strain 1.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
88.114 MPa @Strain 3.10 %, Temperature 120 °C | 12780 psi @Strain 3.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
88.143 MPa @Strain 1.00 %, Temperature 23.0 °C | 12784 psi @Strain 1.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
88.206 MPa @Strain 6.00 %, Temperature 100 °C | 12793 psi @Strain 6.00 %, Temperature 212 °F | 50%RH; ISO 11403-1/-2 | |||
88.653 MPa @Strain 3.10 %, Temperature 80.0 °C | 12858 psi @Strain 3.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
88.672 MPa @Strain 2.20 %, Temperature 80.0 °C | 12861 psi @Strain 2.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
88.949 MPa @Strain 2.60 %, Temperature 100 °C | 12901 psi @Strain 2.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
89.177 MPa @Strain 1.50 %, Temperature 60.0 °C | 12934 psi @Strain 1.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
89.246 MPa @Strain 3.20 %, Temperature 120 °C | 12944 psi @Strain 3.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
89.417 MPa @Strain 3.20 %, Temperature 80.0 °C | 12969 psi @Strain 3.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
89.44 MPa @Strain 2.50 %, Temperature 60.0 °C | 12970 psi @Strain 2.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
89.52 MPa @Strain 1.10 %, Temperature 0.000 °C | 12980 psi @Strain 1.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
89.834 MPa @Strain 1.00 %, Temperature -40.0 °C | 13029 psi @Strain 1.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
90.201 MPa @Strain 3.30 %, Temperature 80.0 °C | 13083 psi @Strain 3.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
90.419 MPa @Strain 3.30 %, Temperature 120 °C | 13114 psi @Strain 3.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
90.76 MPa @Strain 2.70 %, Temperature 100 °C | 13160 psi @Strain 2.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
90.862 MPa @Strain 3.40 %, Temperature 80.0 °C | 13178 psi @Strain 3.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
91.126 MPa @Strain 2.30 %, Temperature 80.0 °C | 13217 psi @Strain 2.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
91.135 MPa @Strain 2.60 %, Temperature 60.0 °C | 13218 psi @Strain 2.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
91.429 MPa @Strain 3.40 %, Temperature 120 °C | 13261 psi @Strain 3.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
91.464 MPa @Strain 3.50 %, Temperature 80.0 °C | 13266 psi @Strain 3.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
91.792 MPa @Strain 1.70 %, Temperature 23.0 °C | 13313 psi @Strain 1.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
92.07 MPa @Strain 3.60 %, Temperature 80.0 °C | 13350 psi @Strain 3.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
92.417 MPa @Strain 3.50 %, Temperature 120 °C | 13404 psi @Strain 3.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
92.502 MPa @Strain 2.80 %, Temperature 100 °C | 13416 psi @Strain 2.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
92.533 MPa @Strain 3.70 %, Temperature 80.0 °C | 13421 psi @Strain 3.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
92.681 MPa @Strain 2.70 %, Temperature 60.0 °C | 13442 psi @Strain 2.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
93.032 MPa @Strain 3.80 %, Temperature 80.0 °C | 13493 psi @Strain 3.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
93.209 MPa @Strain 1.60 %, Temperature 60.0 °C | 13519 psi @Strain 1.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
93.249 MPa @Strain 3.60 %, Temperature 120 °C | 13525 psi @Strain 3.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
93.409 MPa @Strain 3.90 %, Temperature 80.0 °C | 13548 psi @Strain 3.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
93.433 MPa @Strain 2.40 %, Temperature 80.0 °C | 13551 psi @Strain 2.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
93.8 MPa @Strain 4.00 %, Temperature 80.0 °C | 13600 psi @Strain 4.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
94.101 MPa @Strain 2.80 %, Temperature 60.0 °C | 13648 psi @Strain 2.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
94.104 MPa @Strain 3.70 %, Temperature 120 °C | 13649 psi @Strain 3.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
94.148 MPa @Strain 2.90 %, Temperature 100 °C | 13655 psi @Strain 2.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
94.176 MPa @Strain 4.10 %, Temperature 80.0 °C | 13659 psi @Strain 4.10 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
94.433 MPa @Strain 4.20 %, Temperature 80.0 °C | 13696 psi @Strain 4.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
94.78 MPa @Strain 4.30 %, Temperature 80.0 °C | 13750 psi @Strain 4.30 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
94.873 MPa @Strain 3.80 %, Temperature 120 °C | 13760 psi @Strain 3.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
95.041 MPa @Strain 4.40 %, Temperature 80.0 °C | 13785 psi @Strain 4.40 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
95.236 MPa @Strain 4.50 %, Temperature 80.0 °C | 13813 psi @Strain 4.50 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
95.374 MPa @Strain 2.90 %, Temperature 60.0 °C | 13833 psi @Strain 2.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
95.498 MPa @Strain 1.80 %, Temperature 23.0 °C | 13851 psi @Strain 1.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
95.511 MPa @Strain 4.60 %, Temperature 80.0 °C | 13853 psi @Strain 4.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
95.526 MPa @Strain 1.00 %, Temperature -40.0 °C | 13855 psi @Strain 1.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
95.584 MPa @Strain 3.90 %, Temperature 120 °C | 13863 psi @Strain 3.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
95.638 MPa @Strain 3.00 %, Temperature 100 °C | 13871 psi @Strain 3.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
95.672 MPa @Strain 4.70 %, Temperature 80.0 °C | 13876 psi @Strain 4.70 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
95.724 MPa @Strain 2.50 %, Temperature 80.0 °C | 13884 psi @Strain 2.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
95.832 MPa @Strain 4.80 %, Temperature 80.0 °C | 13899 psi @Strain 4.80 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
95.872 MPa @Strain 1.10 %, Temperature 23.0 °C | 13905 psi @Strain 1.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
96.055 MPa @Strain 4.90 %, Temperature 80.0 °C | 13932 psi @Strain 4.90 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
96.14 MPa @Strain 5.00 %, Temperature 80.0 °C | 13940 psi @Strain 5.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
96.219 MPa @Strain 1.00 %, Temperature 0.000 °C | 13955 psi @Strain 1.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
96.269 MPa @Strain 4.00 %, Temperature 120 °C | 13963 psi @Strain 4.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
96.534 MPa @Strain 3.00 %, Temperature 60.0 °C | 14001 psi @Strain 3.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
96.622 MPa @Strain 1.20 %, Temperature 0.000 °C | 14014 psi @Strain 1.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
96.764 MPa @Strain 6.00 %, Temperature 80.0 °C | 14034 psi @Strain 6.00 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
96.82 MPa @Strain 4.10 %, Temperature 120 °C | 14040 psi @Strain 4.10 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
96.982 MPa @Strain 1.70 %, Temperature 60.0 °C | 14066 psi @Strain 1.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
97.051 MPa @Strain 3.10 %, Temperature 100 °C | 14076 psi @Strain 3.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
97.445 MPa @Strain 4.20 %, Temperature 120 °C | 14133 psi @Strain 4.20 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
97.551 MPa @Strain 3.10 %, Temperature 60.0 °C | 14149 psi @Strain 3.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
97.875 MPa @Strain 2.60 %, Temperature 80.0 °C | 14196 psi @Strain 2.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
97.91 MPa @Strain 4.30 %, Temperature 120 °C | 14200 psi @Strain 4.30 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
98.361 MPa @Strain 4.40 %, Temperature 120 °C | 14266 psi @Strain 4.40 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
98.41 MPa @Strain 3.20 %, Temperature 100 °C | 14270 psi @Strain 3.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
98.411 MPa @Strain 1.10 %, Temperature -40.0 °C | 14273 psi @Strain 1.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
98.481 MPa @Strain 3.20 %, Temperature 60.0 °C | 14283 psi @Strain 3.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
98.892 MPa @Strain 4.50 %, Temperature 120 °C | 14343 psi @Strain 4.50 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
99.023 MPa @Strain 1.90 %, Temperature 23.0 °C | 14362 psi @Strain 1.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
99.241 MPa @Strain 4.60 %, Temperature 120 °C | 14394 psi @Strain 4.60 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
99.312 MPa @Strain 3.30 %, Temperature 60.0 °C | 14404 psi @Strain 3.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
99.585 MPa @Strain 3.30 %, Temperature 100 °C | 14444 psi @Strain 3.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
99.663 MPa @Strain 4.70 %, Temperature 120 °C | 14455 psi @Strain 4.70 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
99.974 MPa @Strain 2.70 %, Temperature 80.0 °C | 14500 psi @Strain 2.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
100.057 MPa @Strain 4.80 %, Temperature 120 °C | 14512.1 psi @Strain 4.80 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
100.094 MPa @Strain 3.40 %, Temperature 60.0 °C | 14517.4 psi @Strain 3.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
100.348 MPa @Strain 4.90 %, Temperature 120 °C | 14554.3 psi @Strain 4.90 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
100.563 MPa @Strain 1.80 %, Temperature 60.0 °C | 14585.5 psi @Strain 1.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
100.702 MPa @Strain 3.40 %, Temperature 100 °C | 14605.6 psi @Strain 3.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
100.729 MPa @Strain 5.00 %, Temperature 120 °C | 14609.5 psi @Strain 5.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
100.777 MPa @Strain 3.50 %, Temperature 60.0 °C | 14616.5 psi @Strain 3.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
101.335 MPa @Strain 3.60 %, Temperature 60.0 °C | 14697.4 psi @Strain 3.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
101.543 MPa @Strain 6.00 %, Temperature 120 °C | 14727.6 psi @Strain 6.00 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
101.744 MPa @Strain 3.50 %, Temperature 100 °C | 14756.7 psi @Strain 3.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
101.871 MPa @Strain 3.70 %, Temperature 60.0 °C | 14775.2 psi @Strain 3.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
101.946 MPa @Strain 2.80 %, Temperature 80.0 °C | 14786.0 psi @Strain 2.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
102.328 MPa @Strain 3.80 %, Temperature 60.0 °C | 14841.4 psi @Strain 3.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
102.393 MPa @Strain 2.00 %, Temperature 23.0 °C | 14850.9 psi @Strain 2.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
102.708 MPa @Strain 3.60 %, Temperature 100 °C | 14896.6 psi @Strain 3.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
102.75 MPa @Strain 3.90 %, Temperature 60.0 °C | 14903 psi @Strain 3.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
103.115 MPa @Strain 4.00 %, Temperature 60.0 °C | 14955.6 psi @Strain 4.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
103.264 MPa @Strain 1.20 %, Temperature 23.0 °C | 14977.2 psi @Strain 1.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
103.407 MPa @Strain 1.30 %, Temperature 0.000 °C | 14997.9 psi @Strain 1.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
103.443 MPa @Strain 4.10 %, Temperature 60.0 °C | 15003.2 psi @Strain 4.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
103.55 MPa @Strain 3.70 %, Temperature 100 °C | 15019 psi @Strain 3.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
103.752 MPa @Strain 4.20 %, Temperature 60.0 °C | 15048.0 psi @Strain 4.20 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
103.791 MPa @Strain 2.90 %, Temperature 80.0 °C | 15053.6 psi @Strain 2.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
104.003 MPa @Strain 4.30 %, Temperature 60.0 °C | 15084.4 psi @Strain 4.30 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
104.057 MPa @Strain 1.90 %, Temperature 60.0 °C | 15092.2 psi @Strain 1.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
104.245 MPa @Strain 4.40 %, Temperature 60.0 °C | 15119.5 psi @Strain 4.40 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
104.289 MPa @Strain 3.80 %, Temperature 100 °C | 15125.9 psi @Strain 3.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
104.397 MPa @Strain 1.10 %, Temperature -40.0 °C | 15141.5 psi @Strain 1.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
104.468 MPa @Strain 4.50 %, Temperature 60.0 °C | 15151.8 psi @Strain 4.50 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
104.642 MPa @Strain 4.60 %, Temperature 60.0 °C | 15177.1 psi @Strain 4.60 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
104.796 MPa @Strain 1.10 %, Temperature 0.000 °C | 15199.4 psi @Strain 1.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
104.806 MPa @Strain 4.70 %, Temperature 60.0 °C | 15200.9 psi @Strain 4.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
104.948 MPa @Strain 4.80 %, Temperature 60.0 °C | 15221.4 psi @Strain 4.80 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
105.028 MPa @Strain 3.90 %, Temperature 100 °C | 15233.1 psi @Strain 3.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
105.076 MPa @Strain 4.90 %, Temperature 60.0 °C | 15240.0 psi @Strain 4.90 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
105.188 MPa @Strain 5.00 %, Temperature 60.0 °C | 15256.3 psi @Strain 5.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
105.473 MPa @Strain 6.00 %, Temperature 60.0 °C | 15297.6 psi @Strain 6.00 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
105.6 MPa @Strain 3.00 %, Temperature 80.0 °C | 15320 psi @Strain 3.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
105.672 MPa @Strain 4.00 %, Temperature 100 °C | 15326.5 psi @Strain 4.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
105.718 MPa @Strain 2.10 %, Temperature 23.0 °C | 15333.1 psi @Strain 2.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
106.251 MPa @Strain 4.10 %, Temperature 100 °C | 15410.4 psi @Strain 4.10 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
106.741 MPa @Strain 4.20 %, Temperature 100 °C | 15481.5 psi @Strain 4.20 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
106.856 MPa @Strain 1.20 %, Temperature -40.0 °C | 15498.2 psi @Strain 1.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
107.188 MPa @Strain 4.30 %, Temperature 100 °C | 15546.3 psi @Strain 4.30 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
107.275 MPa @Strain 3.10 %, Temperature 80.0 °C | 15559.0 psi @Strain 3.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
107.427 MPa @Strain 2.00 %, Temperature 60.0 °C | 15581.0 psi @Strain 2.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
107.66 MPa @Strain 4.40 %, Temperature 100 °C | 15615 psi @Strain 4.40 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
108.048 MPa @Strain 4.50 %, Temperature 100 °C | 15671.1 psi @Strain 4.50 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
108.403 MPa @Strain 4.60 %, Temperature 100 °C | 15722.6 psi @Strain 4.60 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
108.743 MPa @Strain 4.70 %, Temperature 100 °C | 15771.9 psi @Strain 4.70 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
108.822 MPa @Strain 2.20 %, Temperature 23.0 °C | 15783.3 psi @Strain 2.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
108.896 MPa @Strain 3.20 %, Temperature 80.0 °C | 15794.1 psi @Strain 3.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
108.998 MPa @Strain 4.80 %, Temperature 100 °C | 15808.9 psi @Strain 4.80 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
109.296 MPa @Strain 4.90 %, Temperature 100 °C | 15852.1 psi @Strain 4.90 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
109.533 MPa @Strain 5.00 %, Temperature 100 °C | 15886.4 psi @Strain 5.00 %, Temperature 212 °F | DAM; ISO 11403-1/-2 | |||
109.777 MPa @Strain 1.40 %, Temperature 0.000 °C | 15921.8 psi @Strain 1.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
110.335 MPa @Strain 3.30 %, Temperature 80.0 °C | 16002.8 psi @Strain 3.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
110.439 MPa @Strain 1.30 %, Temperature 23.0 °C | 16017.9 psi @Strain 1.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
110.482 MPa @Strain 2.10 %, Temperature 60.0 °C | 16024.1 psi @Strain 2.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
111.715 MPa @Strain 3.40 %, Temperature 80.0 °C | 16202.9 psi @Strain 3.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
111.83 MPa @Strain 2.30 %, Temperature 23.0 °C | 16220 psi @Strain 2.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
112.949 MPa @Strain 3.50 %, Temperature 80.0 °C | 16381.9 psi @Strain 3.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
113.095 MPa @Strain 1.20 %, Temperature 0.000 °C | 16403.1 psi @Strain 1.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
113.213 MPa @Strain 1.20 %, Temperature -40.0 °C | 16420.2 psi @Strain 1.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
113.523 MPa @Strain 2.20 %, Temperature 60.0 °C | 16465.1 psi @Strain 2.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
114.13 MPa @Strain 3.60 %, Temperature 80.0 °C | 16553 psi @Strain 3.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
114.655 MPa @Strain 2.40 %, Temperature 23.0 °C | 16629.3 psi @Strain 2.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
115.114 MPa @Strain 3.70 %, Temperature 80.0 °C | 16695.9 psi @Strain 3.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
115.186 MPa @Strain 1.30 %, Temperature -40.0 °C | 16706.3 psi @Strain 1.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
115.766 MPa @Strain 1.50 %, Temperature 0.000 °C | 16790.5 psi @Strain 1.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
116.082 MPa @Strain 3.80 %, Temperature 80.0 °C | 16836.3 psi @Strain 3.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
116.4 MPa @Strain 2.30 %, Temperature 60.0 °C | 16880 psi @Strain 2.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
116.902 MPa @Strain 3.90 %, Temperature 80.0 °C | 16955.2 psi @Strain 3.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
117.376 MPa @Strain 1.40 %, Temperature 23.0 °C | 17024.0 psi @Strain 1.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
117.395 MPa @Strain 2.50 %, Temperature 23.0 °C | 17026.7 psi @Strain 2.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
117.672 MPa @Strain 4.00 %, Temperature 80.0 °C | 17066.9 psi @Strain 4.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
118.318 MPa @Strain 4.10 %, Temperature 80.0 °C | 17160.6 psi @Strain 4.10 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
118.884 MPa @Strain 4.20 %, Temperature 80.0 °C | 17242.7 psi @Strain 4.20 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
119.117 MPa @Strain 2.40 %, Temperature 60.0 °C | 17276.5 psi @Strain 2.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
119.454 MPa @Strain 4.30 %, Temperature 80.0 °C | 17325.4 psi @Strain 4.30 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
119.896 MPa @Strain 4.40 %, Temperature 80.0 °C | 17389.5 psi @Strain 4.40 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
119.958 MPa @Strain 2.60 %, Temperature 23.0 °C | 17398.5 psi @Strain 2.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
120.346 MPa @Strain 4.50 %, Temperature 80.0 °C | 17454.7 psi @Strain 4.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
120.689 MPa @Strain 4.60 %, Temperature 80.0 °C | 17504.5 psi @Strain 4.60 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
121.023 MPa @Strain 4.70 %, Temperature 80.0 °C | 17552.9 psi @Strain 4.70 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
121.281 MPa @Strain 1.30 %, Temperature 0.000 °C | 17590.4 psi @Strain 1.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
121.338 MPa @Strain 4.80 %, Temperature 80.0 °C | 17598.6 psi @Strain 4.80 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
121.537 MPa @Strain 4.90 %, Temperature 80.0 °C | 17627.5 psi @Strain 4.90 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
121.583 MPa @Strain 1.60 %, Temperature 0.000 °C | 17634.2 psi @Strain 1.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
121.718 MPa @Strain 2.50 %, Temperature 60.0 °C | 17653.7 psi @Strain 2.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
121.786 MPa @Strain 1.30 %, Temperature -40.0 °C | 17663.6 psi @Strain 1.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
121.79 MPa @Strain 5.00 %, Temperature 80.0 °C | 17664 psi @Strain 5.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
122.375 MPa @Strain 2.70 %, Temperature 23.0 °C | 17749.0 psi @Strain 2.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
122.378 MPa @Strain 6.00 %, Temperature 80.0 °C | 17749.5 psi @Strain 6.00 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
123.35 MPa @Strain 1.40 %, Temperature -40.0 °C | 17890 psi @Strain 1.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
124.027 MPa @Strain 1.50 %, Temperature 23.0 °C | 17988.6 psi @Strain 1.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
124.14 MPa @Strain 2.60 %, Temperature 60.0 °C | 18005 psi @Strain 2.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
124.623 MPa @Strain 2.80 %, Temperature 23.0 °C | 18075.1 psi @Strain 2.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
126.495 MPa @Strain 2.70 %, Temperature 60.0 °C | 18346.6 psi @Strain 2.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
126.698 MPa @Strain 2.90 %, Temperature 23.0 °C | 18376.0 psi @Strain 2.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
127.162 MPa @Strain 1.70 %, Temperature 0.000 °C | 18443.3 psi @Strain 1.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
128.622 MPa @Strain 2.80 %, Temperature 60.0 °C | 18655.1 psi @Strain 2.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
128.639 MPa @Strain 3.00 %, Temperature 23.0 °C | 18657.5 psi @Strain 3.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
129.016 MPa @Strain 1.40 %, Temperature 0.000 °C | 18712.2 psi @Strain 1.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
130.058 MPa @Strain 1.40 %, Temperature -40.0 °C | 18863.4 psi @Strain 1.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
130.201 MPa @Strain 1.60 %, Temperature 23.0 °C | 18884.1 psi @Strain 1.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
130.391 MPa @Strain 3.10 %, Temperature 23.0 °C | 18911.7 psi @Strain 3.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
130.73 MPa @Strain 2.90 %, Temperature 60.0 °C | 18961 psi @Strain 2.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
131.364 MPa @Strain 1.50 %, Temperature -40.0 °C | 19052.8 psi @Strain 1.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
131.935 MPa @Strain 3.20 %, Temperature 23.0 °C | 19135.6 psi @Strain 3.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
132.458 MPa @Strain 1.80 %, Temperature 0.000 °C | 19211.4 psi @Strain 1.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
132.599 MPa @Strain 3.00 %, Temperature 60.0 °C | 19231.9 psi @Strain 3.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
133.313 MPa @Strain 3.30 %, Temperature 23.0 °C | 19335.5 psi @Strain 3.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
134.344 MPa @Strain 3.10 %, Temperature 60.0 °C | 19485.0 psi @Strain 3.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
134.438 MPa @Strain 3.40 %, Temperature 23.0 °C | 19498.6 psi @Strain 3.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
135.416 MPa @Strain 3.50 %, Temperature 23.0 °C | 19640.5 psi @Strain 3.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
135.866 MPa @Strain 3.20 %, Temperature 60.0 °C | 19705.7 psi @Strain 3.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
136.181 MPa @Strain 1.70 %, Temperature 23.0 °C | 19751.4 psi @Strain 1.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
136.236 MPa @Strain 3.60 %, Temperature 23.0 °C | 19759.4 psi @Strain 3.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
136.485 MPa @Strain 1.50 %, Temperature 0.000 °C | 19795.5 psi @Strain 1.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
136.919 MPa @Strain 3.70 %, Temperature 23.0 °C | 19858.5 psi @Strain 3.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
137.268 MPa @Strain 6.00 %, Temperature 23.0 °C | 19909.1 psi @Strain 6.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
137.271 MPa @Strain 3.30 %, Temperature 60.0 °C | 19909.5 psi @Strain 3.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
137.411 MPa @Strain 1.90 %, Temperature 0.000 °C | 19929.8 psi @Strain 1.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
137.472 MPa @Strain 3.80 %, Temperature 23.0 °C | 19938.7 psi @Strain 3.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
137.875 MPa @Strain 3.90 %, Temperature 23.0 °C | 19997.1 psi @Strain 3.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.045 MPa @Strain 1.50 %, Temperature -40.0 °C | 20021.8 psi @Strain 1.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
138.221 MPa @Strain 4.00 %, Temperature 23.0 °C | 20047.3 psi @Strain 4.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.44 MPa @Strain 5.00 %, Temperature 23.0 °C | 20079 psi @Strain 5.00 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.462 MPa @Strain 3.40 %, Temperature 60.0 °C | 20082.3 psi @Strain 3.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
138.474 MPa @Strain 4.10 %, Temperature 23.0 °C | 20084.0 psi @Strain 4.10 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.546 MPa @Strain 4.90 %, Temperature 23.0 °C | 20094.4 psi @Strain 4.90 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.619 MPa @Strain 4.20 %, Temperature 23.0 °C | 20105.0 psi @Strain 4.20 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.66 MPa @Strain 4.80 %, Temperature 23.0 °C | 20111 psi @Strain 4.80 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.744 MPa @Strain 4.70 %, Temperature 23.0 °C | 20123.2 psi @Strain 4.70 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.747 MPa @Strain 4.30 %, Temperature 23.0 °C | 20123.6 psi @Strain 4.30 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.786 MPa @Strain 4.60 %, Temperature 23.0 °C | 20129.2 psi @Strain 4.60 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.804 MPa @Strain 4.50 %, Temperature 23.0 °C | 20131.9 psi @Strain 4.50 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.806 MPa @Strain 4.40 %, Temperature 23.0 °C | 20132.1 psi @Strain 4.40 %, Temperature 73.4 °F | 50%RH; ISO 11403-1/-2 | |||
138.921 MPa @Strain 1.60 %, Temperature -40.0 °C | 20148.8 psi @Strain 1.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
139.509 MPa @Strain 3.50 %, Temperature 60.0 °C | 20234.1 psi @Strain 3.50 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
140.351 MPa @Strain 3.60 %, Temperature 60.0 °C | 20356.2 psi @Strain 3.60 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
141.085 MPa @Strain 3.70 %, Temperature 60.0 °C | 20462.7 psi @Strain 3.70 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
141.658 MPa @Strain 3.80 %, Temperature 60.0 °C | 20545.8 psi @Strain 3.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.057 MPa @Strain 1.80 %, Temperature 23.0 °C | 20603.7 psi @Strain 1.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
142.164 MPa @Strain 3.90 %, Temperature 60.0 °C | 20619.2 psi @Strain 3.90 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.233 MPa @Strain 2.00 %, Temperature 0.000 °C | 20629.2 psi @Strain 2.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
142.476 MPa @Strain 4.00 %, Temperature 60.0 °C | 20664.4 psi @Strain 4.00 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.704 MPa @Strain 4.10 %, Temperature 60.0 °C | 20697.5 psi @Strain 4.10 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.855 MPa @Strain 4.20 %, Temperature 60.0 °C | 20719.4 psi @Strain 4.20 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.915 MPa @Strain 4.30 %, Temperature 60.0 °C | 20728.1 psi @Strain 4.30 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
142.979 MPa @Strain 4.40 %, Temperature 60.0 °C | 20737.4 psi @Strain 4.40 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
143.77 MPa @Strain 1.60 %, Temperature 0.000 °C | 20852 psi @Strain 1.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
145.853 MPa @Strain 1.60 %, Temperature -40.0 °C | 21154.2 psi @Strain 1.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
146.3 MPa @Strain 1.70 %, Temperature -40.0 °C | 21220 psi @Strain 1.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
146.856 MPa @Strain 2.10 %, Temperature 0.000 °C | 21299.7 psi @Strain 2.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
147.592 MPa @Strain 1.90 %, Temperature 23.0 °C | 21406.4 psi @Strain 1.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
150.87 MPa @Strain 1.70 %, Temperature 0.000 °C | 21882 psi @Strain 1.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
151.123 MPa @Strain 2.20 %, Temperature 0.000 °C | 21918.6 psi @Strain 2.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
152.756 MPa @Strain 2.00 %, Temperature 23.0 °C | 22155.4 psi @Strain 2.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
153.502 MPa @Strain 1.70 %, Temperature -40.0 °C | 22263.6 psi @Strain 1.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
153.619 MPa @Strain 1.80 %, Temperature -40.0 °C | 22280.6 psi @Strain 1.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
155.138 MPa @Strain 2.30 %, Temperature 0.000 °C | 22500.9 psi @Strain 2.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
157.561 MPa @Strain 1.80 %, Temperature 0.000 °C | 22852.3 psi @Strain 1.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
157.695 MPa @Strain 2.10 %, Temperature 23.0 °C | 22871.8 psi @Strain 2.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
158.895 MPa @Strain 2.40 %, Temperature 0.000 °C | 23045.8 psi @Strain 2.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
160.662 MPa @Strain 1.90 %, Temperature -40.0 °C | 23302.1 psi @Strain 1.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
160.801 MPa @Strain 1.80 %, Temperature -40.0 °C | 23322.3 psi @Strain 1.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
162.283 MPa @Strain 2.20 %, Temperature 23.0 °C | 23537.2 psi @Strain 2.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
162.565 MPa @Strain 2.50 %, Temperature 0.000 °C | 23578.1 psi @Strain 2.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
164.066 MPa @Strain 1.90 %, Temperature 0.000 °C | 23795.8 psi @Strain 1.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
166.068 MPa @Strain 2.60 %, Temperature 0.000 °C | 24086.2 psi @Strain 2.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
166.588 MPa @Strain 2.30 %, Temperature 23.0 °C | 24161.6 psi @Strain 2.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
167.341 MPa @Strain 2.00 %, Temperature -40.0 °C | 24270.8 psi @Strain 2.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
167.909 MPa @Strain 1.90 %, Temperature -40.0 °C | 24353.2 psi @Strain 1.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
169.368 MPa @Strain 2.70 %, Temperature 0.000 °C | 24564.8 psi @Strain 2.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
170.46 MPa @Strain 2.00 %, Temperature 0.000 °C | 24723 psi @Strain 2.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
170.8 MPa @Strain 2.40 %, Temperature 23.0 °C | 24770 psi @Strain 2.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
172.261 MPa @Strain 2.80 %, Temperature 0.000 °C | 24984.4 psi @Strain 2.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
173.846 MPa @Strain 2.10 %, Temperature -40.0 °C | 25214.3 psi @Strain 2.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
174.621 MPa @Strain 2.50 %, Temperature 23.0 °C | 25326.7 psi @Strain 2.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
174.78 MPa @Strain 2.00 %, Temperature -40.0 °C | 25350 psi @Strain 2.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
175.018 MPa @Strain 2.90 %, Temperature 0.000 °C | 25384.3 psi @Strain 2.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
176.393 MPa @Strain 2.10 %, Temperature 0.000 °C | 25583.7 psi @Strain 2.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
177.494 MPa @Strain 3.00 %, Temperature 0.000 °C | 25743.4 psi @Strain 3.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
178.211 MPa @Strain 2.60 %, Temperature 23.0 °C | 25847.4 psi @Strain 2.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
179.847 MPa @Strain 3.10 %, Temperature 0.000 °C | 26084.6 psi @Strain 3.10 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
180.125 MPa @Strain 2.20 %, Temperature -40.0 °C | 26125.0 psi @Strain 2.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
181.564 MPa @Strain 2.10 %, Temperature -40.0 °C | 26333.7 psi @Strain 2.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
181.638 MPa @Strain 2.70 %, Temperature 23.0 °C | 26344.4 psi @Strain 2.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
181.946 MPa @Strain 2.20 %, Temperature 0.000 °C | 26389.1 psi @Strain 2.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
181.984 MPa @Strain 3.20 %, Temperature 0.000 °C | 26394.6 psi @Strain 3.20 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
183.82 MPa @Strain 3.30 %, Temperature 0.000 °C | 26661 psi @Strain 3.30 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
184.738 MPa @Strain 2.80 %, Temperature 23.0 °C | 26794.0 psi @Strain 2.80 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
185.249 MPa @Strain 3.40 %, Temperature 0.000 °C | 26868.1 psi @Strain 3.40 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
186.247 MPa @Strain 2.30 %, Temperature -40.0 °C | 27012.9 psi @Strain 2.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
186.304 MPa @Strain 3.50 %, Temperature 0.000 °C | 27021.2 psi @Strain 3.50 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187 MPa @Strain 3.60 %, Temperature 0.000 °C | 27100 psi @Strain 3.60 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187.085 MPa @Strain 4.00 %, Temperature 0.000 °C | 27134.4 psi @Strain 4.00 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187.288 MPa @Strain 2.30 %, Temperature 0.000 °C | 27163.9 psi @Strain 2.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
187.323 MPa @Strain 3.70 %, Temperature 0.000 °C | 27169.0 psi @Strain 3.70 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187.396 MPa @Strain 3.90 %, Temperature 0.000 °C | 27179.5 psi @Strain 3.90 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187.455 MPa @Strain 3.80 %, Temperature 0.000 °C | 27188.1 psi @Strain 3.80 %, Temperature 32.0 °F | 50%RH; ISO 11403-1/-2 | |||
187.574 MPa @Strain 2.90 %, Temperature 23.0 °C | 27205.4 psi @Strain 2.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
188.031 MPa @Strain 2.20 %, Temperature -40.0 °C | 27271.6 psi @Strain 2.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
190.185 MPa @Strain 3.00 %, Temperature 23.0 °C | 27584.1 psi @Strain 3.00 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
192.227 MPa @Strain 2.40 %, Temperature -40.0 °C | 27880.2 psi @Strain 2.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
192.475 MPa @Strain 2.40 %, Temperature 0.000 °C | 27916.2 psi @Strain 2.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
192.527 MPa @Strain 3.10 %, Temperature 23.0 °C | 27923.7 psi @Strain 3.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
194.221 MPa @Strain 2.30 %, Temperature -40.0 °C | 28169.4 psi @Strain 2.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
194.715 MPa @Strain 3.20 %, Temperature 23.0 °C | 28241.1 psi @Strain 3.20 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
196.58 MPa @Strain 3.30 %, Temperature 23.0 °C | 28512 psi @Strain 3.30 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
197.416 MPa @Strain 2.50 %, Temperature 0.000 °C | 28632.8 psi @Strain 2.50 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
197.917 MPa @Strain 2.50 %, Temperature -40.0 °C | 28705.5 psi @Strain 2.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
198.124 MPa @Strain 3.40 %, Temperature 23.0 °C | 28735.5 psi @Strain 3.40 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
199.31 MPa @Strain 3.50 %, Temperature 23.0 °C | 28908 psi @Strain 3.50 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
200.141 MPa @Strain 3.60 %, Temperature 23.0 °C | 29028.1 psi @Strain 3.60 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
200.343 MPa @Strain 2.40 %, Temperature -40.0 °C | 29057.3 psi @Strain 2.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
200.578 MPa @Strain 3.70 %, Temperature 23.0 °C | 29091.4 psi @Strain 3.70 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
201.89 MPa @Strain 2.60 %, Temperature 0.000 °C | 29282 psi @Strain 2.60 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
203.298 MPa @Strain 2.60 %, Temperature -40.0 °C | 29485.9 psi @Strain 2.60 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
206.127 MPa @Strain 2.50 %, Temperature -40.0 °C | 29896.2 psi @Strain 2.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
206.232 MPa @Strain 2.70 %, Temperature 0.000 °C | 29911.5 psi @Strain 2.70 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
208.571 MPa @Strain 2.70 %, Temperature -40.0 °C | 30250.7 psi @Strain 2.70 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
210.283 MPa @Strain 2.80 %, Temperature 0.000 °C | 30499.0 psi @Strain 2.80 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
211.674 MPa @Strain 2.60 %, Temperature -40.0 °C | 30700.8 psi @Strain 2.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
213.637 MPa @Strain 2.80 %, Temperature -40.0 °C | 30985.5 psi @Strain 2.80 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
214.104 MPa @Strain 2.90 %, Temperature 0.000 °C | 31053.2 psi @Strain 2.90 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
217.056 MPa @Strain 2.70 %, Temperature -40.0 °C | 31481.4 psi @Strain 2.70 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
217.669 MPa @Strain 3.00 %, Temperature 0.000 °C | 31570.3 psi @Strain 3.00 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
218.408 MPa @Strain 2.90 %, Temperature -40.0 °C | 31677.5 psi @Strain 2.90 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
220.92 MPa @Strain 3.10 %, Temperature 0.000 °C | 32042 psi @Strain 3.10 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
222.22 MPa @Strain 2.80 %, Temperature -40.0 °C | 32230 psi @Strain 2.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
222.921 MPa @Strain 3.00 %, Temperature -40.0 °C | 32332.0 psi @Strain 3.00 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
223.865 MPa @Strain 3.20 %, Temperature 0.000 °C | 32468.9 psi @Strain 3.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
226.485 MPa @Strain 3.30 %, Temperature 0.000 °C | 32848.9 psi @Strain 3.30 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
227.22 MPa @Strain 3.10 %, Temperature -40.0 °C | 32956 psi @Strain 3.10 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
227.396 MPa @Strain 2.90 %, Temperature -40.0 °C | 32981.1 psi @Strain 2.90 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
228.005 MPa @Strain 3.40 %, Temperature 0.000 °C | 33069.4 psi @Strain 3.40 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
231.512 MPa @Strain 3.20 %, Temperature -40.0 °C | 33578.0 psi @Strain 3.20 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
232.215 MPa @Strain 3.00 %, Temperature -40.0 °C | 33680.0 psi @Strain 3.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
235.584 MPa @Strain 3.30 %, Temperature -40.0 °C | 34168.6 psi @Strain 3.30 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
236.76 MPa @Strain 3.10 %, Temperature -40.0 °C | 34339 psi @Strain 3.10 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
239.346 MPa @Strain 3.40 %, Temperature -40.0 °C | 34714.3 psi @Strain 3.40 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
241.194 MPa @Strain 3.20 %, Temperature -40.0 °C | 34982.3 psi @Strain 3.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
242.453 MPa @Strain 3.50 %, Temperature -40.0 °C | 35164.9 psi @Strain 3.50 %, Temperature -40.0 °F | 50%RH; ISO 11403-1/-2 | |||
245.374 MPa @Strain 3.30 %, Temperature -40.0 °C | 35588.6 psi @Strain 3.30 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
249.617 MPa @Strain 3.40 %, Temperature -40.0 °C | 36203.9 psi @Strain 3.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
252.178 MPa @Strain 3.50 %, Temperature -40.0 °C | 36575.4 psi @Strain 3.50 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
5.0 % @Temperature 23.0 °C | 5.0 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
Tensile Modulus | 7.20 GPa @Temperature 23.0 °C | 1040 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
10.0 GPa @Temperature 23.0 °C | 1450 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
Flexural Modulus | 5.52 GPa @Temperature 23.0 °C | 801 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
8.275 GPa @Temperature 23.0 °C | 1200 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
Izod Impact, Notched | 1.10 J/cm @Temperature 23.0 °C | 2.06 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
1.33 J/cm @Temperature 23.0 °C | 2.49 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
Izod Impact, Notched (ISO) | 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | ||
14.0 kJ/m² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
Charpy Impact Unnotched | 7.50 J/cm² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
Charpy Impact, Notched | 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
1.40 J/cm² @Temperature 23.0 °C | 6.66 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
Electrical Properties | Metric | English | Comments | ||
Comparative Tracking Index | 400 V @Temperature 23.0 °C | 400 V @Temperature 73.4 °F | DAM; UL 746A | ||
400 - 600 V @Temperature 23.0 °C | 400 - 600 V @Temperature 73.4 °F | DAM; UL 746A | |||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | DAM; ASTM D648 | ||
253 °C | 487 °F | DAM; ISO 75-1/-2 | |||
UL RTI, Electrical | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | DAM; UL 746B | ||
140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
UL RTI, Mechanical with Impact | 125 °C @Thickness 1.50 mm | 257 °F @Thickness 0.0591 in | DAM; UL 746B | ||
125 °C @Thickness 3.00 mm | 257 °F @Thickness 0.118 in | DAM; UL 746B | |||
125 °C @Thickness 0.750 mm | 257 °F @Thickness 0.0295 in | DAM; UL 746B | |||
UL RTI, Mechanical without Impact | 140 °C @Thickness 0.750 mm | 284 °F @Thickness 0.0295 in | DAM; UL 746B | ||
140 °C @Thickness 3.00 mm | 284 °F @Thickness 0.118 in | DAM; UL 746B | |||
140 °C @Thickness 1.50 mm | 284 °F @Thickness 0.0591 in | DAM; UL 746B | |||
Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | |||
HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
Processing Properties | Metric | English | Comments | ||
Melt Temperature | 262 °C | 504 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
295 °C | 563 °F | DAM; Optimum | |||
285 - 305 °C | 545 - 581 °F | DAM | |||
Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
100 °C | 212 °F | DAM; optimum | |||
Drying Temperature | 80.0 °C | 176 °F | DAM | ||
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
Descriptive Properties | |||||
Additive | Heat Stabilizer | DAM | |||
Hydrolysis Resistant | DAM | ||||
Appearance | Black Color | DAM | |||
Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
Features | Antifreeze Resistant | DAM | |||
Chemical Resistance, Good | DAM | ||||
Creep Resistance, Good | DAM | ||||
Fatigue Resistant | DAM | ||||
Fuel Resistant | DAM | ||||
Grease Resistant | DAM | ||||
Heat Aging Resistance, Good | DAM | ||||
Hydrolysis Resistant | DAM | ||||
Oil Resistant | DAM | ||||
Stiffness, High | DAM | ||||
Strength, High | DAM | ||||
Thermal Aging Resistance, Good | DAM | ||||
Filler | Glass fiber reinforcement | DAM | |||
Forms | Pellets | DAM | |||
Generic | Nylon 66 | DAM | |||
Material Status | Current | DAM | |||
Part Marking Code | >PA66-GF30< | ISO 11469; DAM | |||
Polymer Family | Polyamide | DAM | |||
Polymer Type | PA66 | DAM | |||
Processing Method | Blow Molding | DAM | |||
Injection Molding | DAM | ||||
Product Category | Glass Reinforced Resins | DAM | |||
Hydrolysis Resistant Resins | DAM | ||||
Region Available - Global | Yes | DAM | |||
Resin Identification | PA66-GF30 | ISO 1043; DAM | |||
RoHS Compliance | Contact Manufacturer | DAM | |||
Uses | Appliance Components | DAM | |||
Automotive Applications | DAM | ||||
Electrical/Electronic Applications | DAM | ||||
Industrial Applications | DAM |