- 密度 [g/cm3]: 1.19
- 缺口冲击强度: 1.4
- 弯曲模量 [MPa]: 3.60
- 硬度: 110.0
- 热变形温度 [℃]: 246.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.19 g/cc | 1.19 g/cc | DAM; ASTM D792 | ||
| Density | 1.19 g/cc | 0.0430 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 14 % | 14 % | DAM | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell M | 70 | 70 | DAM; ISO 2039/2 | ||
| Hardness, Rockwell R | 110 | 110 | DAM; ISO 2039/2 | ||
| Tensile Strength at Break | 85.0 MPa @Temperature 23.0 °C | 12300 psi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Strength | 90.0 MPa @Temperature 23.0 °C | 13100 psi @Temperature 73.4 °F | DAM; ASTM D638 | ||
| Elongation at Break | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 9.0 % @Temperature 23.0 °C | 9.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Modulus | 4.20 GPa @Temperature 23.0 °C | 609 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Flexural Modulus | 3.60 GPa @Temperature 23.0 °C | 522 ksi @Temperature 73.4 °F | DAM; ISO 178 | ||
| 3.66 GPa @Temperature 23.0 °C | 531 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Izod Impact, Notched | 1.40 J/cm @Temperature 23.0 °C | 2.62 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| Izod Impact, Unnotched | 9.60 J/cm @Temperature 23.0 °C | 18.0 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| Izod Impact, Notched (ISO) | 7.00 kJ/m² @Temperature -40.0 °C | 3.33 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 13.0 kJ/m² @Temperature 23.0 °C | 6.19 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | ||
| 1.20 J/cm² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Comparative Tracking Index | 580 V @Temperature 23.0 °C | 580 V @Temperature 73.4 °F | DAM; UL 746A | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 96.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 53.3 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 96.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 53.3 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 118 µm/m-°C @Temperature 23.0 - 55.0 °C | 65.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 118 µm/m-°C @Temperature 23.0 - 55.0 °C | 65.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 123 µm/m-°C @Temperature 55.0 - 160 °C | 68.3 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 123 µm/m-°C @Temperature 55.0 - 160 °C | 68.3 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| Melting Point | 263 °C | 505 °F | DAM; ASTM D3418 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 246 °C | 475 °F | DAM; ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 195 °C | 383 °F | DAM; ISO 75-1/-2 | ||
| 205 °C | 401 °F | DAM; ASTM D648 | |||
| UL RTI, Electrical | 120 °C @Thickness 3.00 mm | 248 °F @Thickness 0.118 in | DAM; UL 746B | ||
| 120 °C @Thickness 1.50 mm | 248 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 120 °C @Thickness 0.750 mm | 248 °F @Thickness 0.0295 in | DAM; UL 746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 0.750 mm | 149 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 95.0 °C @Thickness 1.50 mm | 203 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| UL RTI, Mechanical without Impact | 85.0 °C @Thickness 0.750 mm | 185 °F @Thickness 0.0295 in | DAM; UL 746B | ||
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | DAM; UL 746B | |||
| 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | DAM; UL 746B | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; IEC 60695-11-10 | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | DAM; UL94 | |||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | DAM; UL94 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 263 °C | 505 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 295 °C | 563 °F | DAM; Optimum | |||
| 285 - 305 °C | 545 - 581 °F | DAM | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM | ||
| 80.0 °C | 176 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Heat Stabilizer | DAM | |||
| Appearance | Black Color | DAM | |||
| Colors Available | DAM | ||||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | Impact Resistance, High | DAM | |||
| Toughness, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 66 | DAM | |||
| Heat Stabilized | Yes | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA66-IGF14< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA66 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Toughened Resins | DAM | ||||
| Resin Identification | PA66-IGF14 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| Automotive Applications | DAM | ||||
| Fasteners | DAM | ||||
| Industrial Applications | DAM | ||||
| Sporting Goods | DAM | ||||