- 密度 [g/cm3]: 1.37
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | DAM; ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 155 MPa @Temperature 23.0 °C | 22500 psi @Temperature 73.4 °F | DAM; 5mm/min; ISO 527 | ||
| Elongation at Break | 3.0 % @Temperature 23.0 °C | 3.0 % @Temperature 73.4 °F | DAM; ISO 527 | ||
| Tensile Modulus | 9.00 GPa @Temperature 23.0 °C | 1310 ksi @Temperature 73.4 °F | DAM; ISO 527 | ||
| Charpy Impact Unnotched | 5.50 J/cm² @Temperature 23.0 °C | 26.2 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | ||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature 23.0 °C | 3.81 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 261 °C | 502 °F | DAM; 10°C/min; ISO 11357-1/-3 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | DAM; Injection Molding | ||
| 295 °C | 563 °F | DAM; optimum; Injection Molding | |||
| Mold Temperature | 50.0 - 100 °C | 122 - 212 °F | DAM; Injection Molding | ||
| 80.0 °C | 176 °F | DAM; Optimum; Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM; Injection Molding | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM; Dehumidified Dryer; Injection Molding | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM; Injection Molding | ||
| Descriptive Properties | |||||
| Generic | PA66 | ||||
| Part Marking Code | >PA66-(GF+MD)30< | ISO 11469 | |||
| Product Category | Glass Reinforced Resins | ||||
| Region Available - Europe | Yes | ||||
| Resin Identification | PA66-(GF+MD)30 | ISO 1043 | |||