- 吸水率 [%]: 1.1
- 缺口冲击强度: 9.0
- 拉伸强度 [MPa]: 103.0
- 弯曲模量 [MPa]: 6.10
- 热变形温度 [℃]: 222.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.48 g/cc | 1.48 g/cc | ISO 1183 |
| Water Absorption | 1.1 % @Time 86400 sec | 1.1 % @Time 24.0 hour | ISO 62 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 50% RH; ISO 62 |
| Linear Mold Shrinkage | 0.010 cm/cm @Thickness 2.00 mm | 0.010 in/in @Thickness 0.0787 in | ISO 294-4 |
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm @Thickness 2.00 mm | 0.011 in/in @Thickness 0.0787 in | ISO 294-4 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 103 MPa | 14900 psi | ISO 527 |
| Elongation at Break | 15 % | 15 % | ISO 527 |
| Elongation at Yield | 9.0 % | 9.0 % | ISO 527 |
| Tensile Modulus | 6.90 GPa | 1000 ksi | ISO 527 |
| Flexural Strength | 124 MPa | 18000 psi | ISO 178 |
| Flexural Modulus | 6.10 GPa | 885 ksi | ISO 178 |
| Poissons Ratio | 0.35 | 0.35 | ISO 527 |
| Shear Modulus | 2.56 GPa | 371 ksi | Calculated |
| Izod Impact, Notched (ISO) | 9.00 kJ/m² | 4.28 ft-lb/in² | ISO 180 |
| Charpy Impact Unnotched | 10.9 J/cm² @Temperature -30.0 °C | 51.9 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 14.3 J/cm² @Temperature 23.0 °C | 68.1 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Charpy Impact, Notched | 0.620 J/cm² @Temperature -30.0 °C | 2.95 ft-lb/in² @Temperature -22.0 °F | ISO 179 |
| 0.740 J/cm² @Temperature 23.0 °C | 3.52 ft-lb/in² @Temperature 73.4 °F | ISO 179 | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 5.50e+16 ohm-cm @Thickness 3.00 mm | 5.50e+16 ohm-cm @Thickness 0.118 in | IEC 60093 |
| Dielectric Strength | 15.0 kV/mm @Thickness 3.00 mm | 381 kV/in @Thickness 0.118 in | IEC 60243 |
| Arc Resistance | 60 - 120 sec @Thickness 3.00 mm | 60 - 120 sec @Thickness 0.118 in | UL 746A |
| Comparative Tracking Index | >= 600 V @Thickness 3.00 mm | >= 600 V @Thickness 0.118 in | IEC 60112 |
| Hot Wire Ignition, HWI | 7.0 - 15 sec @Thickness 0.750 mm | 7.0 - 15 sec @Thickness 0.0295 in | UL 746A |
| 7.0 - 15 sec @Thickness 1.50 mm | 7.0 - 15 sec @Thickness 0.0591 in | UL 746A | |
| 15 - 30 sec @Thickness 3.00 mm | 15 - 30 sec @Thickness 0.118 in | UL 746A | |
| High Amp Arc Ignition, HAI | >= 120 arcs @Thickness 3.00 mm | >= 120 arcs @Thickness 0.118 in | UL 746A |
| >= 120 arcs @Thickness 0.750 mm | >= 120 arcs @Thickness 0.0295 in | UL 746A | |
| >= 120 arcs @Thickness 1.50 mm | >= 120 arcs @Thickness 0.0591 in | UL 746A | |
| High Voltage Arc-Tracking Rate, HVTR | 10.0 - 25.4 mm/min @Thickness 3.00 mm | 0.394 - 1.00 in/min @Thickness 0.118 in | UL 746A |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 6.00 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 3.33 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| CTE, linear, Transverse to Flow | 6.30 µm/m-°C @Thickness 2.00 mm, Temperature 23.0 - 55.0 °C | 3.50 µin/in-°F @Thickness 0.0787 in, Temperature 73.4 - 131 °F | ISO 11359 |
| Melting Point | 258 °C | 496 °F | ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 222 °C | 432 °F | ISO 75 |
| Deflection Temperature at 1.8 MPa (264 psi) | 118 °C | 244 °F | ISO 75 |
| Vicat Softening Point | 238 °C @Load 5.10 kg | 460 °F @Load 11.2 lb | ISO 306 |
| UL RTI, Electrical | 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | UL 746B |
| 105 °C @Thickness 0.750 mm | 221 °F @Thickness 0.0295 in | UL 746B | |
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | UL 746B | |
| UL RTI, Mechanical with Impact | 90.0 °C @Thickness 3.00 mm | 194 °F @Thickness 0.118 in | UL 746B |
| 90.0 °C @Thickness 0.750 mm | 194 °F @Thickness 0.0295 in | UL 746B | |
| 90.0 °C @Thickness 1.50 mm | 194 °F @Thickness 0.0591 in | UL 746B | |
| UL RTI, Mechanical without Impact | 105 °C @Thickness 3.00 mm | 221 °F @Thickness 0.118 in | UL 746B |
| 105 °C @Thickness 0.750 mm | 221 °F @Thickness 0.0295 in | UL 746B | |
| 105 °C @Thickness 1.50 mm | 221 °F @Thickness 0.0591 in | UL 746B | |
| Flammability, UL94 | HB @Thickness 3.00 mm | HB @Thickness 0.118 in | |
| HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | ||
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 280 - 310 °C | 536 - 590 °F | |
| Melt Temperature | 285 - 305 °C | 545 - 581 °F | |
| Mold Temperature | 65.0 - 95.0 °C | 149 - 203 °F | |
| Injection Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Hold Pressure | 55.0 - 140 MPa | 7980 - 20300 psi | |
| Back Pressure | 0.200 - 1.00 MPa | 29.0 - 145 psi | |
| Clamp Pressure | 29.43 - 68.67 MPa | 4268 - 9960 psi | |
| Cushion | 0.300 - 0.640 cm | 0.118 - 0.252 in | |
| Screw Speed | 40 - 120 rpm | 40 - 120 rpm | |