- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.3
- 缺口冲击强度: 0.5
- 拉伸强度 [MPa]: 83.0
- 断裂伸长率 [%]: 90.0
- 弯曲模量 [MPa]: 3.00
- 硬度: 120.0
- 热变形温度 [℃]: 232.0
- 脆化温度 [℃]: -79.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.3 % | 1.3 % | 24 hours; ASTM D570 |
| Water Absorption at Saturation | 8.0 % | 8.0 % | ASTM D570 |
| Linear Mold Shrinkage | 0.015 - 0.020 cm/cm | 0.015 - 0.020 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell M | 85 | 85 | ASTM D785 |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength, Yield | 83.0 MPa | 12000 psi | ASTM D638 |
| 62.0 MPa @Temperature 77.0 °C | 8990 psi @Temperature 171 °F | ASTM D638 | |
| 107 MPa @Temperature -40.0 °C | 15500 psi @Temperature -40.0 °F | ASTM D638 | |
| Elongation at Break | 70 % | 70 % | ASTM D638 |
| 20 % @Temperature -40.0 °C | 20 % @Temperature -40.0 °F | ASTM D638 | |
| 300 % @Temperature 77.0 °C | 300 % @Temperature 171 °F | ASTM D638 | |
| Elongation at Yield | 10 % | 10 % | ASTM D638 |
| 5.0 % @Temperature -40.0 °C | 5.0 % @Temperature -40.0 °F | ASTM D638 | |
| 30 % @Temperature 77.0 °C | 30 % @Temperature 171 °F | ASTM D638 | |
| Tensile Modulus | 3.00 GPa | 435 ksi | D638 |
| Flexural Yield Strength | 90.0 MPa | 13100 psi | ASTM D790 |
| Flexural Modulus | 3.00 GPa | 435 ksi | ASTM D790 |
| Compressive Yield Strength | 34.0 MPa | 4930 psi | at 1% deformation; ASTM D695 |
| Shear Strength | 69.0 MPa | 10000 psi | ASTM D732 |
| Izod Impact, Notched | 0.500 J/cm @Thickness 3.17 mm | 0.937 ft-lb/in @Thickness 0.125 in | ASTM D256 |
| 0.300 J/cm @Thickness 3.17 mm, Temperature -40.0 °C | 0.562 ft-lb/in @Thickness 0.125 in, Temperature -40.0 °F | ASTM D256 | |
| Tensile Impact Strength | 170 kJ/m² | 80.9 ft-lb/in² | Type S specimen; ASTM D1822 |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+15 ohm-cm | 6.00e+15 ohm-cm | ASTM D257 |
| Dielectric Constant | 3.1 @Frequency 1e+6 Hz | 3.1 @Frequency 1e+6 Hz | ASTM D150 |
| 3.6 @Frequency 1000 Hz | 3.6 @Frequency 1000 Hz | ASTM D150 | |
| 3.7 @Frequency 100 Hz | 3.7 @Frequency 100 Hz | ASTM D150 | |
| Dielectric Strength | 21.3 kV/mm | 541 kV/in | Step by step; ASTM D149 |
| 22.4 kV/mm | 569 kV/in | Short Time; ASTM D149 | |
| Dissipation Factor | 0.020 @Frequency 100 Hz | 0.020 @Frequency 100 Hz | ASTM D150 |
| 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150 | |
| 0.030 @Frequency 1e+6 Hz | 0.030 @Frequency 1e+6 Hz | ASTM D150 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 81.0 µm/m-°C @Temperature -40.0 - 82.0 °C | 45.0 µin/in-°F @Temperature -40.0 - 180 °F | |
| Specific Heat Capacity | 1.70 J/g-°C | 0.406 BTU/lb-°F | Mfr. internal test |
| Thermal Conductivity | 0.240 W/m-K | 1.67 BTU-in/hr-ft²-°F | Mfr. internal test |
| Melting Point | 260 °C | 500 °F | ASTM D789 |
| Deflection Temperature at 0.46 MPa (66 psi) | 232 °C @Thickness 3.17 mm | 450 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 82.0 °C @Thickness 3.17 mm | 180 °F @Thickness 0.125 in | Unannealed; ASTM D648 |
| Brittleness Temperature | -79.0 °C | -110 °F | |
| Flammability, UL94 | V-2 | V-2 | |
| Oxygen Index | 30 % | 30 % | ASTM D2863 |