- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 8.0
- 缺口冲击强度: 0.4
- 拉伸强度 [MPa]: 75.0
- 弯曲模量 [MPa]: 2.55
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 8.0 % @Temperature 23.0 °C | 8.0 % @Temperature 73.4 °F | 24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.013 cm/cm | 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 100 | 100 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 75.0 MPa | 10900 psi | ASTM D638, ISO R527 |
| Elongation at Break | 40 % | 40 % | ASTM D638, ISO R527 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 2.55 GPa | 370 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.400 - 0.600 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 0.749 - 1.12 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256, ISO 180/4a |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.5 @Frequency 1000 Hz | 3.5 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Dielectric Strength | 110 kV/mm | 2790 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Comparative Tracking Index | 600 V | 600 V | VDE 0303-P1, IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 70.0 °C | 158 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 85.0 °C | 185 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 225 °C @Load 5.00 kg | 437 °F @Load 11.0 lb | 120°C/min; ASTM D1525/B, ISO 306/B |
| 240 °C @Load 0.999 kg | 464 °F @Load 2.20 lb | 120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||