- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.0
- 缺口冲击强度: 0.7
- 拉伸强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 8.90
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ASTM D792, ISO 1183 |
| Water Absorption | 6.0 % @Temperature 23.0 °C | 6.0 % @Temperature 73.4 °F | 24h; ASTM D570, ISO 62 |
| Linear Mold Shrinkage | 0.0020 - 0.011 cm/cm | 0.0020 - 0.011 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell L | 110 | 110 | ASTM D785, ISO 2039/2 |
| Tensile Strength, Yield | 170 MPa | 24700 psi | ASTM D638, ISO R527 |
| Elongation at Break | 3.0 % | 3.0 % | ASTM D638, ISO R527 |
| Flexural Strength | 235 MPa | 34100 psi | ASTM D790, ISO 178 |
| Flexural Modulus | 8.90 GPa | 1290 ksi | ASTM D790, ISO 178 |
| Izod Impact, Notched | 0.700 J/cm @Thickness 3.20 mm, Temperature 23.0 °C | 1.31 ft-lb/in @Thickness 0.126 in, Temperature 73.4 °F | ASTM D256, ISO 180/4a |
| Electrical Properties | Metric | English | Comments |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | ASTM D257, IEC 93 |
| Dielectric Constant | 3.5 @Frequency 1000 Hz | 3.5 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Dielectric Strength | 90.0 kV/mm | 2290 kV/in | ASTM D149, IEC 243 |
| Dissipation Factor | 0.020 @Frequency 1000 Hz | 0.020 @Frequency 1000 Hz | ASTM D150, IEC 250 |
| Comparative Tracking Index | 475 V | 475 V | VDE 0303-P1, IEC 112 |
| Thermal Properties | Metric | English | Comments |
| Maximum Service Temperature, Air | 100 °C | 212 °F | 20000 h; VDE 0304/P2-1, IEC 216 |
| 110 °C | 230 °F | 5000 h; VDE 0304/P2-1, IEC 216 | |
| 200 °C | 392 °F | few hours; VDE 0304/P2-1, IEC 216 | |
| Deflection Temperature at 1.8 MPa (264 psi) | 248 °C | 478 °F | ASTM D648, ISO 75 |
| Vicat Softening Point | 250 °C @Load 5.00 kg | 482 °F @Load 11.0 lb | 120°C/min; ASTM D1525/B, ISO 306/B |
| 254 °C @Load 0.999 kg | 489 °F @Load 2.20 lb | 120°C/min; ASTM D1525/A, ISO 306/A | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||