- 密度 [g/cm3]: 1.14
- 吸水率 [%]: 1.2
- 缺口冲击强度: 0.6
- 拉伸强度 [MPa]: 80.0
- 断裂伸长率 [%]: 110
- 弯曲模量 [MPa]: 2.80
- 热变形温度 [℃]: 235.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.14 g/cc | 0.0412 lb/in³ | ASTM D792 |
| Water Absorption | 1.2 % | 1.2 % | 23°C/24 hr; ASTM D570 |
| Linear Mold Shrinkage | 0.015 cm/cm | 0.015 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 80.0 MPa | 11600 psi | ASTM D638 |
| Elongation at Break | 65 % | 65 % | ASTM D638 |
| Flexural Yield Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 2.80 GPa | 406 ksi | ASTM D790 |
| Izod Impact, Notched | 0.600 J/cm | 1.12 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 260 °C | 500 °F | ASTM D2133 |
| Deflection Temperature at 0.46 MPa (66 psi) | 235 °C | 455 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 90.0 °C | 194 °F | ASTM D648 |
| Flammability, UL94 | V-2 | V-2 | |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 270 - 290 °C | 518 - 554 °F | |
| Mold Temperature | 40.0 - 60.0 °C | 104 - 140 °F | |