- 密度 [g/cm3]: 1.23
- 缺口冲击强度: 8.0
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
Moisture Absorption | 2.00 % @Temperature 23.0 °C | 2.00 % @Temperature 73.4 °F | 50% RH; ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.014 cm/cm | 0.014 in/in | Eurotec | ||
Linear Mold Shrinkage, Transverse | 0.014 cm/cm | 0.014 in/in | Eurotec | ||
Mechanical Properties | Metric | English | Comments | ||
Tensile Strength at Break | 70.0 MPa | 10200 psi | ISO 527 | ||
Tensile Modulus | 3.25 GPa | 471 ksi | ISO 527 | ||
Izod Impact, Notched (ISO) | 8.00 kJ/m² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | ||
9.00 kJ/m² @Temperature 23.0 °C | 4.28 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
Comparative Tracking Index | 550 V | 550 V | Solution A; IEC 60112 | ||
Thermal Properties | Metric | English | Comments | ||
Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 | ||
Deflection Temperature at 1.8 MPa (264 psi) | 80.0 °C | 176 °F | ISO 75 | ||
Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
Processing Properties | Metric | English | Comments | ||
Processing Temperature | 270 - 300 °C | 518 - 572 °F | |||
Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat | ||
Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |||
Drying Temperature | 80.0 °C | 176 °F | |||
Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 | ||
Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | |||
Descriptive Properties | |||||
Back Pressure | Low | ||||
Injection Speed | Fast |