- 密度 [g/cm3]: 1.37
- 缺口冲击强度: 10.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.37 g/cc | 0.0495 lb/in³ | ISO 1183 | ||
| Moisture Absorption | 1.80 % @Temperature 23.0 °C | 1.80 % @Temperature 73.4 °F | 50% RH; ISO 62 | ||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm | 0.0030 in/in | Eurotec | ||
| Linear Mold Shrinkage, Transverse | 0.011 cm/cm | 0.011 in/in | Eurotec | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 185 MPa | 26800 psi | ISO 527 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | ISO 527 | ||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A | ||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 65.0 kJ/m² @Temperature -30.0 °C | 30.9 ft-lb/in² @Temperature -22.0 °F | ISO 180/1U | ||
| 75.0 kJ/m² @Temperature 23.0 °C | 35.7 ft-lb/in² @Temperature 73.4 °F | ISO 180/1U | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 262 °C | 504 °F | [10 K/min], ISO 11357 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 260 °C | 500 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 255 °C | 491 °F | ISO 75 | ||
| Vicat Softening Point | 255 °C @Load 5.10 kg | 491 °F @Load 11.2 lb | ISO 306 | ||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | ||||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 270 - 300 °C | 518 - 572 °F | |||
| Feed Temperature | 60.0 - 80.0 °C | 140 - 176 °F | Throat | ||
| Mold Temperature | 70.0 - 110 °C | 158 - 230 °F | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | |||
| Moisture Content | <= 0.20 % | <= 0.20 % | ISO 960 | ||
| Hold Pressure | 50.0 - 100 MPa | 7250 - 14500 psi | |||
| Descriptive Properties | |||||
| Back Pressure | Low | ||||
| Injection Speed | Fast | ||||