- 密度 [g/cm3]: 1.05
- 吸水率 [%]: 6.0
- 缺口冲击强度: 20.0
- 拉伸强度 [MPa]: 50.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.05 g/cc | 0.0379 lb/in³ | ISO 1183 |
| Filler Content | 0.00 % | 0.00 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 2.0 % | 2.0 % | Humidity Absorption, 50% RH, 23°C; ISO 62 |
| Water Absorption at Saturation | 6.0 % | 6.0 % | 23°C; ISO 62 |
| Linear Mold Shrinkage | 0.017 cm/cm | 0.017 in/in | |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 50.0 MPa | 7250 psi | ISO 527 |
| Elongation at Yield | 5.0 % | 5.0 % | ISO 527 |
| Tensile Modulus | 1.50 GPa | 218 ksi | ISO 527 |
| Izod Impact, Notched (ISO) | 20.0 kJ/m² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 180/1A |
| 85.0 kJ/m² @Temperature 23.0 °C | 40.4 ft-lb/in² @Temperature 73.4 °F | ISO 180/1A | |
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/eU |
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/eU | |
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 179/eA |
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 °C | 504 °F | 10 K/min; ISO 3146 |
| Deflection Temperature at 1.8 MPa (264 psi) | 65.0 °C | 149 °F | ISO 75-1/2 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||