- 密度 [g/cm3]: 1.46
- 吸水率 [%]: 5.0
- 缺口冲击强度: 12.0
- 弯曲模量 [MPa]: 11.0
- 热变形温度 [℃]: 260.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.46 g/cc | 0.0527 lb/in?? | ISO 1183 |
| Filler Content | 40 % | 40 % | ISO 3451 |
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | Humidity Absorption, 50% RH, 23??C; ISO 62 |
| Water Absorption at Saturation | 5.0 % | 5.0 % | 23??C; ISO 62 |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | |
| Linear Mold Shrinkage, Transverse | 0.010 cm/cm | 0.010 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 215 MPa | 31200 psi | ISO 527 |
| Elongation at Break | 3.0 % | 3.0 % | ISO 527 |
| Tensile Modulus | 13.0 GPa | 1890 ksi | ISO 527 |
| Flexural Strength | 300 MPa | 43500 psi | 23??C, at break; ISO 178 |
| Flexural Modulus | 11.0 GPa | 1600 ksi | ISO 178 |
| Izod Impact, Notched (ISO) | 12.0 kJ/m?? @Temperature -30.0 ??C | 5.71 ft-lb/in?? @Temperature -22.0 ??F | ISO 180/1A |
| 15.0 kJ/m?? @Temperature 23.0 ??C | 7.14 ft-lb/in?? @Temperature 73.4 ??F | ISO 180/1A | |
| Charpy Impact Unnotched | 8.00 J/cm?? @Temperature -30.0 ??C | 38.1 ft-lb/in?? @Temperature -22.0 ??F | ISO 179/eU |
| 9.00 J/cm?? @Temperature 23.0 ??C | 42.8 ft-lb/in?? @Temperature 73.4 ??F | ISO 179/eU | |
| Charpy Impact, Notched | 1.30 J/cm?? @Temperature -30.0 ??C | 6.19 ft-lb/in?? @Temperature -22.0 ??F | ISO 179/eA |
| 1.60 J/cm?? @Temperature 23.0 ??C | 7.61 ft-lb/in?? @Temperature 73.4 ??F | ISO 179/eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Comparative Tracking Index | 500 V | 500 V | IEC 60112 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 262 ??C | 504 ??F | 10 K/min; ISO 3146 |
| Deflection Temperature at 0.46 MPa (66 psi) | 260 ??C | 500 ??F | ISO 75-1/2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 255 ??C | 491 ??F | ISO 75-1/2 |
| Vicat Softening Point | 255 ??C | 491 ??F | 50N; ISO 306 |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||
| Glow Wire Test | 650 ??C @Thickness 2.00 mm | 1200 ??F @Thickness 0.0787 in | plaque; IEC 60695 |