- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 拉伸强度 [MPa]: 36.0
- 弯曲强度 [MPa]: 80.0
- 弯曲模量 [MPa]: 0.740
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | (DAM); ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hr. (DAM); ISO 62 | ||
| 9.5 % | 9.5 % | (Beginning DAM); ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H. (Beginning DAM); ISO 62 | ||
| Viscosity Measurement | 48 | 48 | Formic Acid; ASTM D789 | ||
| Linear Mold Shrinkage | 0.012 cm/cm | 0.012 in/in | MD; ASTM Test | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 60.0 MPa | 8700 psi | 0.2 in/min; ASTM D638 | ||
| Tensile Strength, Ultimate | 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ASTM D638 | ||
| 80.0 MPa @Temperature -40.0 °C | 11600 psi @Temperature -40.0 °F | ISO 527 | |||
| Tensile Strength, Yield | 36.0 MPa | 5220 psi | 50 mm/min; ISO 527 | ||
| 36.0 MPa | 5220 psi | 2 in/min; ASTM D638 | |||
| 21.0 MPa @Temperature 120 °C | 3050 psi @Temperature 248 °F | ASTM D638 | |||
| 21.0 MPa @Temperature 120 °C | 3050 psi @Temperature 248 °F | ISO 527 | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ASTM D638 | |||
| 30.0 MPa @Temperature 80.0 °C | 4350 psi @Temperature 176 °F | ISO 527 | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ASTM D638 | |||
| 110 MPa @Temperature -40.0 °C | 16000 psi @Temperature -40.0 °F | ISO 527 | |||
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; Nominal; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM D638 | |||
| 2.5 % @Temperature -40.0 °C | 2.5 % @Temperature -40.0 °F | ASTM D638 | |||
| Elongation at Yield | 16 % | 16 % | 50 mm/min; ISO 527 | ||
| 16 % | 16 % | 2 in/min; ASTM D638 | |||
| 35 % @Temperature 80.0 °C | 35 % @Temperature 176 °F | ASTM D638 | |||
| 40 % @Temperature 120 °C | 40 % @Temperature 248 °F | ASTM D638 | |||
| Tensile Modulus | 0.970 GPa | 141 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 35.0 MPa | 5080 psi | ASTM D790 | ||
| 155 MPa @Temperature -40.0 °C | 22500 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.740 GPa | 107 ksi | ASTM D790 | ||
| 3.66 GPa @Temperature -40.0 °C | 531 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched | NB | NB | ASTM D256 | ||
| 0.450 J/cm @Temperature -40.0 °C | 0.843 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min (DAM) | ||
| 220 °C | 428 °F | (DAM); ASTM D3418 | |||
| Descriptive Properties | |||||
| Additive | Unfilled | ||||
| Color | Natural | ||||
| Commercial Status (March 2007) | Active America | ||||
| FDA | 21 CFR 177.1500 | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Injection molding | Processable | ||||
| Primary Processing Technique | Film Extrusion | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.