- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.45
- 拉伸强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 2.20
- 硬度: 119.0
- 热变形温度 [℃]: 167.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.6 % | 1.6 % | 24 hr.; ISO 62 | ||
| 9.5 % | 9.5 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.7 % | 2.7 % | 23°C/50% R.H.; ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 119 | 119 | ASTM D785 | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 2 in/min; ASTM D638 | ||
| 79.0 MPa | 11500 psi | 50 mm/min; ISO 527 | |||
| Elongation at Break | >= 50 % | >= 50 % | 50 mm/min; Nominal; ISO 527 | ||
| >= 100 % | >= 100 % | 2 in/min; ASTM D638 | |||
| Elongation at Yield | 10 % | 10 % | 50 mm/min; ISO 527 | ||
| 10 % | 10 % | 2 in/min; ASTM D638 | |||
| Tensile Modulus | 3.00 GPa | 435 ksi | 1 mm/min; ISO 527 | ||
| Flexural Strength | 70.0 MPa | 10200 psi | ISO 178 | ||
| 100 MPa | 14500 psi | ASTM D790 | |||
| 8.00 MPa @Temperature 120 °C | 1160 psi @Temperature 248 °F | ASTM D790 | |||
| 179 MPa @Temperature -40.0 °C | 26000 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 2.20 GPa | 319 ksi | ISO 178 | ||
| 2.45 GPa | 355 ksi | ASTM D790 | |||
| 0.305 GPa @Temperature 120 °C | 44.2 ksi @Temperature 248 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.450 J/cm | 0.843 ft-lb/in | ASTM D256 | ||
| 0.370 J/cm @Temperature -40.0 °C | 0.693 ft-lb/in @Temperature -40.0 °F | ASTM D256 | |||
| Charpy Impact Unnotched | 8.50 J/cm² | 40.5 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.410 J/cm² | 1.95 ft-lb/in² | ISO 179 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 86.0 µm/m-°C @Temperature 20.0 °C | 47.8 µin/in-°F @Temperature 68.0 °F | ASTM E831 | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM D3418 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 167 °C | 333 °F | ASTM D648 | ||
| 178 °C | 352 °F | ISO 75 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 | ||
| 60.0 °C | 140 °F | ISO 75 | |||
| Oxygen Index | 23 % | 23 % | ISO 4589-1/-2 | ||
| Descriptive Properties | |||||
| Additive | Unfilled | ||||
| Attribute | Heat stabilized or stable to heat | ||||
| Color | Natural | ||||
| Commercial Status (March 2007) | Active America | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Other extrusion | Processable | ||||
| Primary Processing Technique | Wire and Cable | ||||
| Profile extrusion | Processable | ||||
| UL.UL-C | Yes | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.