Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C

Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C 物性表: Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C物性表及特性介绍,Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C注塑参数详情,如需Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.16
  • 透光率 [%]: 90.0
 
Physical PropertiesMetricEnglishComments
Density 1.16 g/cc0.0420 lb/in³Yield Density
Water Vapor Transmission 140 g/m²/day9.02 g/100 in²/day100°F (37.8°C) / 100%RH; ASTM F1249
Oxygen Transmission Rate 0.230 cc/m²/day0.0148 cc/100 in²/day50°F (10°C) / 0%RH; ASTM D3985
 0.620 cc/m²/day0.0399 cc/100 in²/day73°F (23°F) / 65%RH; ASTM D3985
 0.930 cc/m²/day0.0599 cc/100 in²/day73°F (23°C) / 0%RH; ASTM D3985
Thickness 15.2 microns0.600 mil
Surface Tension >= 56 dynes/cm>= 56 dynes/cmtreated side; ASTM D2578
 
Mechanical PropertiesMetricEnglishComments
Film Tensile Strength at Yield, TD 68.9 - 82.7 MPa10000 - 12000 psiASTM D882
Film Elongation at Break, MD 55 - 80 %55 - 80 %ASTM D882
Film Elongation at Break, TD 180 - 425 %180 - 425 %ASTM D882
Secant Modulus, MD 3.275 - 4.689 GPa475.0 - 680.1 ksiASTM D882
Secant Modulus, TD 2.586 - 3.448 GPa375.1 - 500.1 ksiASTM D882
Coefficient of Friction 0.25 - 0.570.25 - 0.57film to stainless steel; ASTM D1894
 0.66 - 2.00.66 - 2.0film to film; ASTM D1894
Tear Strength Test 925 - 1450925 - 1450graves tear TD, grams/mil; ASTM D1004
 1000 - 14001000 - 1400graves tear MD, grams/mil; ASTM D1004
Film Tensile Strength at Break, MD 200 - 290 MPa29000 - 42000 psiASTM D882
Film Tensile Strength at Break, TD 48.3 - 96.5 MPa7000 - 14000 psiASTM D882
 
Thermal PropertiesMetricEnglishComments
Shrinkage, MD <= 11 %<= 11 %350°F / 177°C - 10 min.; ASTM D1204
Shrinkage, TD <= 2.5 %<= 2.5 %350°F / 177°C - 10 min.; ASTM D1204
 
Optical PropertiesMetricEnglishComments
Haze <= 5.0 %<= 5.0 %ASTM D1003
Transmission, Visible 90.0 %90.0 %clear; thickness not quantified

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45899.html

免责声明: 本文 Honeywell Capran® Oxyshield™ OEB (0.60 mil) Monoaxially Oriented, Co-Extruded Nylon 6/EVOH/Nylon 6 C 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4