- 密度 [g/cm3]: 1.13
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0410 lb/in³ | Yield Density |
| Thickness | 25.4 microns | 1.00 mil | |
| Mechanical Properties | Metric | English | Comments |
| Film Elongation at Break, MD | 60 - 80 % | 60 - 80 % | ASTM D882 |
| Film Elongation at Break, TD | 400 - 475 % | 400 - 475 % | ASTM D882 |
| Secant Modulus, MD | 1.896 - 2.758 GPa | 275.0 - 400.0 ksi | ASTM D882 |
| Secant Modulus, TD | 1.896 - 2.758 GPa | 275.0 - 400.0 ksi | ASTM D882 |
| Coefficient of Friction | 0.40 - 0.70 | 0.40 - 0.70 | film to stainless steel; ASTM D1894 |
| 0.70 - 1.2 | 0.70 - 1.2 | film to film; ASTM D1894 | |
| Tear Strength Test | 1200 - 1500 | 1200 - 1500 | graves tear MD, grams/mil; ASTM D1004 |
| 1200 - 1600 | 1200 - 1600 | graves tear TD, grams/mil; ASTM D1004 | |
| Elmendorf Tear Strength, MD | 1.18 - 3.15 g/micron | 30.0 - 80.0 g/mil | |
| Elmendorf Tear Strength, TD | 5.91 - 7.87 g/micron | 150 - 200 g/mil | ASTM D1922 |
| Film Tensile Strength at Break, MD | 290 - 359 MPa | 42000 - 52000 psi | ASTM D882 |
| Film Tensile Strength at Break, TD | 96.5 - 117 MPa | 14000 - 17000 psi | ASTM D882 |
| Thermal Properties | Metric | English | Comments |
| Shrinkage, MD | 8.0 - 15 % | 8.0 - 15 % | 400°F / 201°C - 5 min.; ASTM D1204 |
| Shrinkage, TD | 1.0 - 2.5 % | 1.0 - 2.5 % | 400°F / 201°C - 5 min.; ASTM D1204 |
| Optical Properties | Metric | English | Comments |
| Haze | <= 5.0 % | <= 5.0 % | ASTM D1003 |
| Gloss | 80 - 100 % | 80 - 100 % | at 45° |