- 密度 [g/cm3]: 1.44
- 弯曲强度 [MPa]: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.44 g/cc | 0.0520 lb/in³ | (Dry) |
| Linear Mold Shrinkage | 0.0020 cm/cm | 0.0020 in/in | ASTM Data MD (Dry) |
| Linear Mold Shrinkage, Transverse | 0.0060 cm/cm | 0.0060 in/in | ISO Data (Dry) |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | ASTM data at 5 mm/min. |
| 121 MPa | 17500 psi | ISO value at 5mm/min. | |
| Tensile Modulus | 6.91 GPa | 1000 ksi | same value from ASTM and ISO test. |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 220 °C | 428 °F | (Dry) |
| Processing Properties | Metric | English | Comments |
| Processing Temperature | 275 °C | 527 °F | See Materials Notes |
| Mold Temperature | 95.0 °C | 203 °F | See Materials Notes |
| Drying Temperature | 85.0 °C | 185 °F | See Materials Notes |