BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)

BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry) 物性表: BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)物性表及特性介绍,BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)注塑参数详情,如需BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry)下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.34
  • 吸水率 [%]: 0.9
  • 断裂伸长率 [%]: 235
  • 弯曲强度 [MPa]: 150.0
  • 弯曲模量 [MPa]: 8.00
  • 热变形温度 [℃]: 219.0
 
Physical PropertiesMetricEnglishComments
Density 1.34 g/cc0.0484 lb/in³ISO data
Water Absorption 0.90 %0.90 %24 hrs; ISO data
Moisture Absorption at Equilibrium 1.5 %1.5 %50% RH; 23°C; ISO data
Water Absorption at Saturation 5.4 %5.4 %in water; 23°C; ISO data
Linear Mold Shrinkage 0.0020 cm/cm0.0020 in/inISO data
 0.0030 cm/cm0.0030 in/inASTM data MD
Linear Mold Shrinkage, Transverse 0.0090 cm/cm0.0090 in/inISO Data
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Ultimate 150 MPa21800 psiASTM data at 5 mm/min.
 152 MPa22000 psiISO value at 5mm/min.
Elongation at Break 3.5 %3.5 %Strain at break, ISO, 5 mm/min
 3.5 %3.5 %Strain at break, ASTM, 5 mm/min
Tensile Modulus 9.41 GPa1360 ksisame value from ASTM and ISO test.
Flexural Yield Strength 235 MPa34100 psiASTM Data
Flexural Modulus 8.00 GPa1160 ksiASTM Data
Poissons Ratio 0.350.35ISO data
Shear Modulus 3.50 GPa508 ksicalculated
Charpy Impact, Notched 1.90 J/cm²9.04 ft-lb/in²ISO Data
 1.40 J/cm²
@Temperature -30.0 °C
6.66 ft-lb/in²
@Temperature -22.0 °F
ISO data
 
Electrical PropertiesMetricEnglishComments
Electrical Resistivity >= 1.00e+15 ohm-cm>= 1.00e+15 ohm-cmISO data
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow 24.0 µm/m-°C
@Temperature 20.0 °C
13.3 µin/in-°F
@Temperature 68.0 °F
ISO data
CTE, linear, Transverse to Flow 84.0 µm/m-°C
@Temperature 20.0 °C
46.7 µin/in-°F
@Temperature 68.0 °F
ISO data
Melting Point 220 °C428 °FASTM and ISO test
Deflection Temperature at 0.46 MPa (66 psi) 219 °C426 °FISO data
Deflection Temperature at 1.8 MPa (264 psi) 205 °C401 °FISO data
 210 °C410 °FASTM Data
Flammability, UL94  HB
@Thickness 0.800 mm
HB
@Thickness 0.0315 in
 HB
@Thickness 3.00 mm
HB
@Thickness 0.118 in
 
Processing PropertiesMetricEnglishComments
Processing Temperature 275 °C527 °FSee Materials Notes
Mold Temperature 95.0 °C203 °FSee Materials Notes
Drying Temperature 85.0 °C185 °FSee Materials Notes

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-45987.html

免责声明: 本文 BASF Capron® HPN 9333G HS Impact Modified, 33% Glass-Filled Nylon 6 (Dry) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络