- 熔体流动速率 [g/10min]: 5.0
- 密度 [g/cm3]: 1.31
- 吸水率 [%]: 2.3
- 弯曲强度 [MPa]: 120.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.31 g/cc | 0.0473 lb/in³ | |
| Water Absorption | 2.3 % | 2.3 % | |
| Moisture Absorption at Equilibrium | 0.90 % | 0.90 % | Humidity Absorption |
| Melt Flow | 5.0 g/10 min @Load 2.16 kg, Temperature 235 °C | 5.0 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 120 MPa | 17400 psi | 5 mm/min |
| Elongation at Break | 3.5 % | 3.5 % | 5 mm/min |
| Tensile Modulus | 7.50 GPa | 1090 ksi | 1 mm/min |
| Charpy Impact, Notched | 0.550 J/cm² | 2.62 ft-lb/in² | |
| Tensile Creep Modulus, 1 hour | 5740 MPa | 833000 psi | |
| Tensile Creep Modulus, 1000 hours | 4050 MPa | 587000 psi | |
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 430000 ohm-cm | 430000 ohm-cm | |
| Surface Resistance | 55000 ohm | 55000 ohm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 19.0 µm/m-°C @Temperature 20.0 °C | 10.6 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | 126 µm/m-°C @Temperature 20.0 °C | 70.0 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 220 °C | 428 °F | 10°C/min |
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | |
| Vicat Softening Point | 183 °C | 361 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||