- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 1.4
- 缺口冲击强度: 0.45
- 弯曲强度 [MPa]: 110.0
- 弯曲模量 [MPa]: 4.80
- 硬度: 121.0
- 热变形温度 [℃]: 210.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.4 % | 1.4 % | 24 hour; ISO Test | ||
| 8.2 % | 8.2 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.3 % | 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Measurement | 61 | 61 | Formic Acid | ||
| Linear Mold Shrinkage | 0.0050 cm/cm | 0.0050 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Hardness, Rockwell R | 121 | 121 | ASTM Test | ||
| Tensile Strength at Break | 120 MPa | 17400 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 110 MPa | 16000 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.0 % | 2.0 % | 5mm/min; ISO 527 | ||
| 3.0 % | 3.0 % | 0.2 in/min; ASTM Test | |||
| Tensile Modulus | 5.70 GPa | 827 ksi | 1mm/min; ISO 527 | ||
| Flexural Strength | 165 MPa | 23900 psi | ISO Data | ||
| Flexural Modulus | 4.80 GPa | 696 ksi | ISO Data | ||
| 5.38 GPa | 780 ksi | ASTM Test | |||
| Izod Impact, Notched | 0.450 J/cm @Thickness 3.17 mm | 0.843 ft-lb/in @Thickness 0.125 in | ASTM Test | ||
| Izod Impact, Notched (ISO) | 4.50 kJ/m² | 2.14 ft-lb/in² | ISO Test | ||
| 4.00 kJ/m² @Temperature -40.0 °C | 1.90 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 3.00 J/cm² | 14.3 ft-lb/in² | ISO 179 | ||
| Charpy Impact, Notched | 0.400 J/cm² | 1.90 ft-lb/in² | ISO 179 | ||
| 0.300 J/cm² @Temperature -30.0 °C | 1.43 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear | 50.0 µm/m-°C @Temperature -30.0 - 30.0 °C | 27.8 µin/in-°F @Temperature -22.0 - 86.0 °F | ASTM Test | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 210 °C | 410 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 190 °C | 374 °F | ISO 75 | ||
| 200 °C | 392 °F | ASTM Test | |||
| Flammability, UL94 | HB @Thickness 0.750 mm | HB @Thickness 0.0295 in | |||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | ||||
| Descriptive Properties | |||||
| Color | BK | ||||
| Commercial Status | Active America | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| UL.UL-C | Yes | ||||