- 熔体流动速率 [g/10min]: 68.0
- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.3
- 缺口冲击强度: 15.0
- 拉伸强度 [MPa]: 185.0
- 弯曲模量 [MPa]: 8.60
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number; ISO 307 | ||
| Linear Mold Shrinkage | 0.0035 cm/cm | 0.0035 in/in | |||
| Melt Flow | 68 g/10 min @Load 5.00 kg, Temperature 275 °C | 68 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 185 MPa | 26800 psi | 50mm/min; ISO 527 | ||
| Elongation at Yield | 3.5 % | 3.5 % | 50mm/min; ISO 527 | ||
| Modulus of Elasticity | 9.50 GPa | 1380 ksi | ISO 527 | ||
| Flexural Strength | 270 MPa | 39200 psi | ISO 178 | ||
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 15.0 kJ/m² | 7.14 ft-lb/in² | ISO 180/A | ||
| Charpy Impact Unnotched | 9.50 J/cm² | 45.2 ft-lb/in² | ISO 179/1eU | ||
| 8.00 J/cm² @Temperature -30.0 °C | 38.1 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | ISO 179/1eA | ||
| 1.10 J/cm² @Temperature -30.0 °C | 5.24 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.8 @Frequency 1.00e+6 Hz | 3.8 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Dissipation Factor | 0.023 @Frequency 1.00e+6 Hz | 0.023 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 450 V | 450 V | Test Solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 0.200 - 0.250 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.111 - 0.139 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 0.600 - 0.700 µm/m-°C @Temperature 23.0 - 80.0 °C | 0.333 - 0.389 µin/in-°F @Temperature 73.4 - 176 °F | ISO 11359-1/-2 | ||
| Specific Heat Capacity | 1.50 J/g-°C | 0.359 BTU/lb-°F | |||
| Thermal Conductivity | 0.360 W/m-K | 2.50 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Melting Point | 220 °C | 428 °F | DIN 53765 | ||
| Maximum Service Temperature, Air | 145 °C | 293 °F | for 50% loss of tensile strength after 20,000 hr | ||
| 175 °C | 347 °F | for 50% loss of tensile strength after 5,000 hr | |||
| 200 °C | 392 °F | ||||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 210 °C | 410 °F | ISO 75 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | Natural | ||||
| Commercial Status | North America and Europe | ||||
| Form | Pellets | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||
| Processing | Injection Molding | ||||
| Special characteristic | Heat stabilized or stable to heat | ||||