- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 2.1
- 缺口冲击强度: 1.07
- 弯曲强度 [MPa]: 177.0
- 弯曲模量 [MPa]: 8.60
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 2.1 % | 2.1 % | 24 hour; ISO Test | ||
| 6.6 % | 6.6 % | ISO 62 | |||
| Moisture Absorption at Equilibrium | 2.1 % | 2.1 % | 23°C/50% R.H.; ISO 62 | ||
| Viscosity Test | 140 cm³/g | 140 cm³/g | Viscosity number | ||
| Linear Mold Shrinkage | 0.0030 cm/cm | 0.0030 in/in | ASTM Data; MD | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 180 MPa | 26100 psi | 0.2 in/min; ASTM Test | ||
| Tensile Strength, Ultimate | 177 MPa | 25700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 2.5 % | 2.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 8.83 GPa | 1280 ksi | ASTM Test | ||
| 10.5 GPa | 1520 ksi | 1mm/min; ISO 527 | |||
| Flexural Modulus | 8.60 GPa | 1250 ksi | ISO Data | ||
| Izod Impact, Notched | 1.07 J/cm @Temperature -40.0 °C | 2.00 ft-lb/in @Temperature -40.0 °F | ASTM Test | ||
| 1.50 J/cm @Thickness 3.17 mm | 2.81 ft-lb/in @Thickness 0.125 in | ASTM Test | |||
| Izod Impact, Notched (ISO) | 10.0 kJ/m² | 4.76 ft-lb/in² | ISO Test | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | >= 1.00e+13 ohm-cm | >= 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+12 ohm | 1.00e+12 ohm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| 220 °C | 428 °F | ASTM Test | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ASTM Test | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | ISO 75 | ||
| 210 °C | 410 °F | ASTM Test | |||
| Descriptive Properties | |||||
| Color | BK00564 BGVW | ||||
| Commercial Status | North America and Europe | ||||
| Impact Modified | No | ||||
| Primary Processing Technique | Injection Molding | ||||