- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 1.1
- 缺口冲击强度: 25.0
- 弯曲强度 [MPa]: 170.0
- 弯曲模量 [MPa]: 8.925
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 1.1 % | 1.1 % | 24 hour; ISO Test | ||
| Linear Mold Shrinkage, Flow | 0.023 cm/cm | 0.023 in/in | ISO Data | ||
| Linear Mold Shrinkage, Transverse | 0.059 cm/cm | 0.059 in/in | ISO Data | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 170 MPa | 24700 psi | 5mm/min; ISO 527 | ||
| Elongation at Break | 3.5 % | 3.5 % | 5mm/min; ISO 527 | ||
| Tensile Modulus | 10.0 GPa | 1450 ksi | 1mm/min; ISO 527 | ||
| Flexural Modulus | 8.925 GPa | 1294 ksi | ISO Data | ||
| Izod Impact, Notched (ISO) | 25.0 kJ/m² | 11.9 ft-lb/in² | ISO Test | ||
| 17.0 kJ/m² @Temperature -40.0 °C | 8.09 ft-lb/in² @Temperature -40.0 °F | ISO Test | |||
| Charpy Impact Unnotched | 10.2 J/cm² | 48.5 ft-lb/in² | ISO 179 | ||
| 11.3 J/cm² @Temperature -30.0 °C | 53.8 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Charpy Impact, Notched | 2.60 J/cm² | 12.4 ft-lb/in² | ISO 179 | ||
| 1.80 J/cm² @Temperature -30.0 °C | 8.57 ft-lb/in² @Temperature -22.0 °F | ISO 179 | |||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10 K/min | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 206 °C | 403 °F | ISO 75 | ||
| Descriptive Properties | |||||
| Color | BK23273 | ||||
| Commercial Status | Preliminary | ||||
| Impact Modified | Yes | ||||
| Primary Processing Technique | Injection Molding | ||||