- 熔体流动速率 [g/10min]: 92.25
- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 7.7
- 拉伸强度 [MPa]: 70.0
- 弯曲模量 [MPa]: 2.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | ISO 1183 | ||
| Water Absorption | 7.7 - 8.3 % | 7.7 - 8.3 % | Saturation; ISO 62 | ||
| Moisture Absorption at Equilibrium | 2.3 - 2.9 % | 2.3 - 2.9 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 140 | 140 | ISO 307 | ||
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | restricted | ||
| Melt Flow | 92.25 g/10 min @Load 5.00 kg, Temperature 275 °C | 92.25 g/10 min @Load 11.0 lb, Temperature 527 °F | ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 70.0 MPa | 10200 psi | 50 mm/min; ISO 527-1/-2 | ||
| Elongation at Yield | 15 % | 15 % | 50 mm/min; ISO 527-1/-2 | ||
| Modulus of Elasticity | 3.50 GPa | 508 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 100 MPa | 14500 psi | at max force; ISO 178 | ||
| Flexural Modulus | 2.50 GPa | 363 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 10.5 J/cm² @Temperature 23.0 °C | 50.0 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Charpy Impact, Notched | 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | ||
| Tensile Creep Modulus, 1000 hours | 2100 MPa @Strain <=0.500 % | 305000 psi @Strain <=0.500 % | ISO 899-1 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+10 ohm-cm | 1.00e+10 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+10 ohm | 1.00e+10 ohm | IEC 60093 | ||
| Dielectric Constant | 7.0 @Frequency 1.00 Hz | 7.0 @Frequency 1.00 Hz | IEC 60250 | ||
| Dissipation Factor | 0.24 @Frequency 1.00e+6 Hz | 0.24 @Frequency 1.00e+6 Hz | IEC 60250 | ||
| Comparative Tracking Index | 550 V | 550 V | Test solution A; IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | 0.340 W/m-K | 2.36 BTU-in/hr-ft²-°F | DIN 52612 | ||
| Maximum Service Temperature, Air | 135 °C | 275 °F | for 50% loss of tensile strength after 20000hr | ||
| 165 °C | 329 °F | for 50% loss of tensile strength after 5000hr | |||
| 200 °C | 392 °F | ||||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection-molding/Extrusion | ||
| Mold Temperature | 80.0 - 90.0 °C | 176 - 194 °F | Injection-molding | ||
| Descriptive Properties | |||||
| Color | BK 00564 | ||||
| Commercial Status | Europe | ||||