BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned)

BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned) 物性表: BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned)物性表及特性介绍,BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned)注塑参数详情,如需BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned)下载, 可到相关下载区下载
  • 熔体流动速率 [g/10min]: 72.6
  • 密度 [g/cm3]: 1.32
  • 吸水率 [%]: 6.8
  • 缺口冲击强度: 17.0
  • 拉伸强度 [MPa]: 105.0
  • 弯曲模量 [MPa]: 4.20
 
Physical PropertiesMetricEnglishComments
Bulk Density 0.500 - 0.800 g/cc0.0181 - 0.0289 lb/in³
Density 1.32 g/cc0.0477 lb/in³ISO 1183
Water Absorption 6.8 - 7.4 %6.8 - 7.4 %Saturation; ISO 62
Moisture Absorption at Equilibrium 2.1 - 2.5 %2.1 - 2.5 %23°C; 50% RH; ISO 62
Viscosity Measurement 140140ISO 307
Linear Mold Shrinkage 0.0035 cm/cm0.0035 in/inrestricted
Melt Flow 72.6 g/10 min
@Load 5.00 kg,
Temperature 275 °C
72.6 g/10 min
@Load 11.0 lb,
Temperature 527 °F
ISO 1133
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength, Yield 105 MPa15200 psi50 mm/min; ISO 527-1/-2
Elongation at Yield 8.5 %8.5 %50 mm/min; ISO 527-1/-2
Modulus of Elasticity 5.50 GPa798 ksiISO 527-1/-2
Flexural Strength 150 MPa21800 psiat max force; ISO 178
Flexural Modulus 4.20 GPa609 ksiISO 178
Izod Impact, Notched (ISO) 17.0 kJ/m²
@Temperature 23.0 °C
8.09 ft-lb/in²
@Temperature 73.4 °F
ISO 180/A
Charpy Impact Unnotched 10.5 J/cm²
@Temperature 23.0 °C
50.0 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eU
Charpy Impact, Notched 2.50 J/cm²
@Temperature 23.0 °C
11.9 ft-lb/in²
@Temperature 73.4 °F
ISO 179/1eA
Tensile Creep Modulus, 1000 hours 3000 MPa
@Strain <=0.500 %
435000 psi
@Strain <=0.500 %
ISO 899-1
 
Electrical PropertiesMetricEnglishComments
Volume Resistivity 1.00e+10 ohm-cm1.00e+10 ohm-cmIEC 60093
Surface Resistance 1.00e+10 ohm1.00e+10 ohmIEC 60093
Dielectric Constant 7.0
@Frequency 1.00 Hz
7.0
@Frequency 1.00 Hz
IEC 60250
Dissipation Factor 0.24
@Frequency 1.00e+6 Hz
0.24
@Frequency 1.00e+6 Hz
IEC 60250
Comparative Tracking Index 575 V575 VTest solution A; IEC 60112
 
Thermal PropertiesMetricEnglishComments
Specific Heat Capacity 1.50 J/g-°C0.359 BTU/lb-°F
Thermal Conductivity 0.350 W/m-K2.43 BTU-in/hr-ft²-°FDIN 52612
Melting Point 220 °C428 °FDIN 53765
Maximum Service Temperature, Air 135 °C275 °Ffor 50% loss of tensile strength after 20000hr
 165 °C329 °Ffor 50% loss of tensile strength after 5000hr
 200 °C392 °F
Decomposition Temperature >= 310 °C>= 590 °F
 
Processing PropertiesMetricEnglishComments
Processing Temperature 80.0 °C176 °FHopper Throat
Zone 1 260 °C500 °FFeed Zone
Zone 2 270 °C518 °FCompression
Zone 3 280 °C536 °FMetering-zone
Zone 4 280 °C536 °FNozzle
Melt Temperature 270 - 290 °C518 - 554 °FInjection-molding/Extrusion
 280 °C536 °FOptimal
Mold Temperature 80.0 °C176 °FOptimal
 80.0 - 90.0 °C176 - 194 °FInjection-molding
Drying Temperature 80.0 °C176 °F
Dry Time 4 hour4 hour
Moisture Content 0.030 - 0.060 %0.030 - 0.060 %Optimal
 <= 0.15 %<= 0.15 %
 
Descriptive Properties
Commercial StatusEurope
Ignition Temperature>400°CASTM D129
Peripheral Screw Speed< 0.3 m/s

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46205.html

免责声明: 本文 BASF Ultramid® B3EG5 25% Glass Filled PA6 (Conditioned) 仅代表作者个人观点,中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容,其版权均由原作者和资料提供方所拥有!如因作品版权问题需要处理,请与我们联络

塑胶原料之家,专业塑料网站、原料报价网站,免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4