- 密度 [g/cm3]: 1.36
- 吸水率 [%]: 6.3
- 弯曲模量 [MPa]: 5.50
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Bulk Density | 0.500 - 0.800 g/cc | 0.0181 - 0.0289 lb/in³ | |||
| Density | 1.36 g/cc | 0.0491 lb/in³ | ISO 1183 | ||
| Water Absorption | 6.3 - 6.9 % | 6.3 - 6.9 % | ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 - 2.3 % | 1.9 - 2.3 % | 23°C; 50% RH; ISO 62 | ||
| Viscosity Measurement | 145 | 145 | ISO 307 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 7.5 % | 7.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 5.60 GPa | 812 ksi | ISO 527-1/-2 | ||
| Flexural Strength | 160 MPa | 23200 psi | ISO 178 | ||
| Flexural Modulus | 5.50 GPa | 798 ksi | ISO 178 | ||
| Charpy Impact Unnotched | 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Maximum Service Temperature, Air | 200 °C | 392 °F | |||
| Decomposition Temperature | >= 300 °C | >= 572 °F | |||
| Processing Properties | Metric | English | Comments | ||
| Processing Temperature | 80.0 °C | 176 °F | Hopper Throat | ||
| Zone 1 | 260 °C | 500 °F | Feed Zone | ||
| Zone 2 | 270 °C | 518 °F | Compression | ||
| Zone 3 | 280 °C | 536 °F | Metering-zone | ||
| Zone 4 | 280 °C | 536 °F | Nozzle | ||
| Melt Temperature | 270 - 290 °C | 518 - 554 °F | Injection Molding/Extrusion | ||
| 280 °C | 536 °F | Optimal | |||
| Mold Temperature | 80.0 °C | 176 °F | Optimal | ||
| 80.0 - 90.0 °C | 176 - 194 °F | Injection Molding | |||
| Drying Temperature | 80.0 °C | 176 °F | |||
| Dry Time | 4 hour | 4 hour | |||
| Moisture Content | 0.030 - 0.060 % | 0.030 - 0.060 % | Optimal | ||
| <= 0.15 % | <= 0.15 % | ||||
| Descriptive Properties | |||||
| Color | BK 23210 | ||||
| Commercial Status | Europe | ||||
| Ignition Temperature | >400°C | ASTM D1929 | |||
| Peripheral Screw Speed | < 0.3 m/s | ||||