- 密度 [g/cm3]: 1.04
- 缺口冲击强度: 101.0
- 弯曲模量 [MPa]: 0.480
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.04 g/cc | 0.0376 lb/in³ | ISO 1183 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 38.0 MPa | 5510 psi | ISO 527 | ||
| Elongation at Break | 160 % | 160 % | Nominal; ISO 527 | ||
| Tensile Modulus | 0.494 GPa | 71.6 ksi | ISO 527 | ||
| Flexural Modulus | 0.480 GPa | 69.6 ksi | ISO 178 | ||
| Izod Impact, Notched (ISO) | 101 kJ/m² | 48.1 ft-lb/in² | ISO 180 | ||
| Charpy Impact, Notched | 11.7 J/cm² | 55.7 ft-lb/in² | ISO 179 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | ISO 3146 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 40.0 °C | 104 °F | ISO 75 | ||
| Processing Properties | Metric | English | Comments | ||
| Zone 1 | 225 - 245 °C | 437 - 473 °F | Rear | ||
| Zone 2 | 225 - 250 °C | 437 - 482 °F | Middle | ||
| Zone 3 | 225 - 245 °C | 437 - 473 °F | Front | ||
| Zone 4 | 230 - 245 °C | 446 - 473 °F | Head | ||
| Zone 5 | 230 - 245 °C | 446 - 473 °F | Flange | ||
| Die Temperature | 230 - 245 °C | 446 - 473 °F | |||
| Melt Temperature | 225 - 245 °C | 437 - 473 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.10 % | <= 0.10 % | |||
| Descriptive Properties | |||||
| Commercial Status | North America | ||||