- 密度 [g/cm3]: 1.13
- 缺口冲击强度: 0.48
- 拉伸强度 [MPa]: 46.0
- 弯曲模量 [MPa]: 0.760
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 | ||
| Moisture Absorption at Equilibrium | 1.6 % | 1.6 % | 24 Hours; ASTM D570 | ||
| 2.6 % | 2.6 % | 50% RH; ASTM D570 | |||
| 9.2 % | 9.2 % | Saturation; ASTM D570 | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 46.0 MPa @Temperature 23.0 °C | 6670 psi @Temperature 73.4 °F | ASTM D638 | ||
| 119 MPa @Temperature -40.0 °C | 17300 psi @Temperature -40.0 °F | ASTM D638 | |||
| Flexural Strength | 37.0 MPa @Temperature 23.0 °C | 5370 psi @Temperature 73.4 °F | ASTM D790 | ||
| 176 MPa @Temperature -40.0 °C | 25500 psi @Temperature -40.0 °F | ASTM D790 | |||
| Flexural Modulus | 0.760 GPa @Temperature 23.0 °C | 110 ksi @Temperature 73.4 °F | ASTM D790 | ||
| 3.90 GPa @Temperature -40.0 °C | 566 ksi @Temperature -40.0 °F | ASTM D790 | |||
| Izod Impact, Notched | 0.480 J/cm @Temperature -40.0 °C | 0.899 ft-lb/in @Temperature -40.0 °F | ASTM D256 | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ASTM D256 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 245 - 260 °C | 473 - 500 °F | |||
| Mold Temperature | 60.0 °C | 140 °F | |||
| Dry Time | 2 - 4 hour | 2 - 4 hour | |||
| Moisture Content | <= 0.15 % | <= 0.15 % | |||
| Descriptive Properties | |||||
| Color | BK 102 | ||||
| Commercial Status | North America | ||||