- 密度 [g/cm3]: 1.13
- 吸水率 [%]: 1.6
- 缺口冲击强度: 0.427
- 弯曲模量 [MPa]: 3.17
- 硬度: 120.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.13 g/cc | 0.0408 lb/in³ | ASTM D792 |
| Water Absorption | 1.6 % | 1.6 % | At 24 hrs; ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.0090 - 0.013 cm/cm | 0.0090 - 0.013 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Rockwell R | 120 | 120 | ASTM D785 |
| Tensile Strength at Break | 82.7 MPa | 12000 psi | ASTM D638 |
| Elongation at Break | 10 % | 10 % | ASTM D638 |
| Flexural Strength | 110 MPa | 16000 psi | ASTM D790 |
| Flexural Modulus | 3.17 GPa | 460 ksi | ASTM D790 |
| Izod Impact, Notched | 0.427 J/cm | 0.800 ft-lb/in | 0.125 in; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 420 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 70.0 °C | 158 °F | Unannealed; ASTM D648 |