- 密度 [g/cm3]: 1.09
- 缺口冲击强度: 8.0
- 断裂伸长率 [%]: 37.0
- 弯曲强度 [MPa]: 41.0
- 弯曲模量 [MPa]: 0.760
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.09 g/cc | 0.0394 lb/in³ | ASTM D792 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 41.0 MPa | 5950 psi | ASTM D638 |
| Elongation at Break | 200 % | 200 % | ASTM D638 |
| Flexural Yield Strength | 37.0 MPa | 5370 psi | ASTM D790 |
| Flexural Modulus | 0.760 GPa | 110 ksi | ASTM D790 |
| Izod Impact, Notched | 8.00 J/cm | 15.0 ft-lb/in | ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 213 °C | 415 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 46.0 °C | 115 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 238 °C | 460 °F | |