- 缺口冲击强度: 0.747
- 拉伸强度 [MPa]: 81.4
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.18 g/cc | 1.18 g/cc | |
| Linear Mold Shrinkage | 0.0040 - 0.0070 cm/cm | 0.0040 - 0.0070 in/in | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 37.98 MPa | 5509 psi | ASTM D638 |
| Tensile Strength, Yield | 81.4 MPa | 11800 psi | ASTM D638 |
| Elongation at Break | 19 % | 19 % | ASTM D638 |
| Elongation at Yield | 7.5 % | 7.5 % | ASTM D638 |
| Tensile Modulus | 1.50 GPa | 217 ksi | ASTM D790 |
| Izod Impact, Notched | 0.747 J/cm @Temperature 22.8 °C | 1.40 ft-lb/in @Temperature 73.0 °F | ASTM D256 |
| Coefficient of Friction | 0.10 | 0.10 | ASTM D3702 |
| 0.17 | 0.17 | ASTM D3702 | |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 210 - 240 °C | 410 - 464 °F | |
| Mold Temperature | 40.0 - 80.0 °C | 104 - 176 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | predrying |