- 吸水率 [%]: 1.35
- 缺口冲击强度: 1.33
- 拉伸强度 [MPa]: 47.6
- 断裂伸长率 [%]: 77.9
- 弯曲模量 [MPa]: 2.00
- 热变形温度 [℃]: 150.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.07 g/cc | 1.07 g/cc | ASTM D792 |
| Water Absorption | 1.35 % @Time 86400 sec | 1.35 % @Time 24.0 hour | ASTM D570 |
| Linear Mold Shrinkage, Flow | 0.020 cm/cm | 0.020 in/in | ASTM D955 |
| Linear Mold Shrinkage, Transverse | 0.017 cm/cm | 0.017 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 47.6 MPa | 6900 psi | ASTM D638 |
| Elongation at Break | >= 100 % | >= 100 % | ASTM D638 |
| Elongation at Yield | 5.0 % | 5.0 % | ASTM D638 |
| Tensile Modulus | 2.17 GPa | 315 ksi | ASTM D638 |
| Flexural Yield Strength | 77.9 MPa | 11300 psi | ASTM D790 |
| Flexural Modulus | 2.00 GPa | 290 ksi | ASTM D790 |
| Izod Impact, Notched | 1.33 J/cm @Temperature -40.0 °C | 2.50 ft-lb/in @Temperature -40.0 °F | ASTM D256 |
| 8.54 J/cm @Temperature 22.8 °C | 16.0 ft-lb/in @Temperature 73.0 °F | ASTM D256 | |
| Multi-axial Impact @ -30°C Total Energy | 62.0 J @Thickness 12.7 mm | 45.7 ft-lb @Thickness 0.500 in | ASTM D3763 |
| 169 J @Thickness 25.4 mm | 125 ft-lb @Thickness 1.00 in | ASTM D3763 | |
| Thermal Properties | Metric | English | Comments |
| Deflection Temperature at 0.46 MPa (66 psi) | 150 °C | 302 °F | ASTM D648 |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | ASTM D648 |
| Processing Properties | Metric | English | Comments |
| Melt Temperature | 249 - 277 °C | 480 - 530 °F | |
| Mold Temperature | 65.6 - 79.4 °C | 150 - 175 °F | |
| Dry Time | 2 - 4 hour | 2 - 4 hour | dehumidified dryer |
| Moisture Content | <= 0.20 % | <= 0.20 % | Processing |