Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH

Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH 物性表: Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH物性表及特性介绍,Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH注塑参数详情,如需Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH下载, 可到相关下载区下载

熔体流动速率 [g/10min]: 48.3
密度 [g/cm3]: 1.15
缺口冲击强度: 0.38
拉伸强度 [MPa]: 96.0
断裂伸长率 [%]: 143
弯曲强度 [MPa]: 96.0
弯曲模量 [MPa]: 3.70

Physical Properties	Metric	English	Comments

Density	1.15 g/cc	0.0415 lb/in³	ASTM D792
Viscosity Measurement	2.7	2.7	Relative Viscosity
Melt Flow	48.3 g/10 min @Load 5.00 kg, Temperature 235 °C	48.3 g/10 min @Load 11.0 lb, Temperature 455 °F	ASTM D1238

Mechanical Properties	Metric	English	Comments
Tensile Strength, Ultimate	96.0 MPa	13900 psi	ASTM D638
Tensile Strength, Yield	96.0 MPa	13900 psi	ASTM D638
Elongation at Break	2.3 %	2.3 %	ASTM D638
Elongation at Yield	2.4 %	2.4 %	ASTM D638
Flexural Yield Strength	143 MPa	20700 psi	ASTM D790
Flexural Modulus	3.70 GPa	537 ksi	ASTM D790
Izod Impact, Notched	0.380 J/cm	0.712 ft-lb/in	ASTM D256

Thermal Properties	Metric	English	Comments
Melting Point	221 °C	430 °F	ASTM DSC

关键词:
供应
PA6
50% RH
Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded
2.7 r.v. Compounding Grade Nylon 6

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46480.html

免责声明: 本文 Cresset Powers Cress-Alon™ NE2740 4% Nano Clay Loaded, 2.7 r.v. Compounding Grade Nylon 6, 50% RH 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息