- 吸水率 [%]: 1.0
- 缺口冲击强度: 2.24
- 弯曲模量 [MPa]: 7.58
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Specific Gravity | 1.37 g/cc | 1.37 g/cc | ASTM D792 |
| Water Absorption | 1.0 % | 1.0 % | Saturation; ASTM D570 |
| Linear Mold Shrinkage | 0.0020 - 0.0040 cm/cm | 0.0020 - 0.0040 in/in | ASTM D955 |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength at Break | 157 MPa | 22800 psi | ASTM D638 |
| Elongation at Break | 4.0 - 5.0 % | 4.0 - 5.0 % | ASTM D638 |
| Flexural Strength | 193 MPa | 28000 psi | ASTM D790 |
| Flexural Modulus | 7.58 GPa | 1100 ksi | ASTM D790 |
| Izod Impact, Notched | 2.24 J/cm | 4.20 ft-lb/in | 1/8 in specimen; ASTM D256 |
| Thermal Properties | Metric | English | Comments |
| Melting Point | 216 °C | 420 °F | ASTM D789 |
| Deflection Temperature at 1.8 MPa (264 psi) | 198 °C | 388 °F | 0.125 in bar; ASTM D648 |