- 密度 [g/cm3]: 1.56
- 吸水率 [%]: 4.5
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.56 g/cc | 0.0564 lb/in³ | ISO 1183 | ||
| Water Absorption | 4.5 % | 4.5 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.4 % | 1.4 % | Humidity Absorption; Sim. to ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 230 MPa | 33400 psi | ISO 527-1/-2 | ||
| Elongation at Break | 3.0 % | 3.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 16.0 GPa | 2320 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 8.50 J/cm² @Temperature -30.0 °C | 40.5 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 10.0 J/cm² @Temperature 23.0 °C | 47.6 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.50 J/cm² @Temperature -30.0 °C | 7.14 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.20 J/cm² @Temperature 23.0 °C | 10.5 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Dielectric Constant | 3.5 @Frequency 100 Hz | 3.5 @Frequency 100 Hz | IEC 60250 | ||
| 5.2 @Frequency 1e+6 Hz | 5.2 @Frequency 1e+6 Hz | IEC 60250 | |||
| Dielectric Strength | 35.0 kV/mm | 889 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.0050 @Frequency 100 Hz | 0.0050 @Frequency 100 Hz | IEC 60250 | ||
| 0.015 @Frequency 1e+6 Hz | 0.015 @Frequency 1e+6 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| >= 600 V | >= 600 V | PLC 0; UL 746A | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 10.0 µm/m-°C @Temperature 20.0 °C | 5.56 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 50.0 µm/m-°C @Temperature 20.0 °C | 27.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Melting Point | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 215 °C | 419 °F | ISO 75-1/-2 | ||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | UL746B | |||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | UL746B | ||
| 65.0 °C @Thickness 3.00 mm | 149 °F @Thickness 0.118 in | UL746B | |||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| HB @Thickness 3.00 mm | HB @Thickness 0.118 in | IEC 60695-11-10 | |||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 220 °C | 428 °F | 10°C/min; ISO 11357-1/-3 | ||
| Descriptive Properties | |||||
| Injection Molding | Yes | ||||
| Release Agent | Yes | ||||
| With Fillers | Yes | ||||