- 密度 [g/cm3]: 1.35
- 吸水率 [%]: 6.3
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.35 g/cc | 0.0488 lb/in³ | (DAM); ISO 1183 | ||
| Water Absorption | 6.3 % | 6.3 % | DAM; Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 1.9 % | 1.9 % | Humidity Absorption (DAM); Sim. to ISO 62 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 100 MPa | 14500 psi | ISO 527-1/-2 | ||
| Elongation at Break | 4.5 % | 4.5 % | ISO 527-1/-2 | ||
| Tensile Modulus | 4.90 GPa | 711 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | 6.50 J/cm² @Temperature -30.0 °C | 30.9 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU | ||
| 9.00 J/cm² @Temperature 23.0 °C | 42.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 0.800 J/cm² @Temperature -30.0 °C | 3.81 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 2.00 J/cm² @Temperature 23.0 °C | 9.52 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+13 ohm-cm | 1.00e+13 ohm-cm | IEC 60093 | ||
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | IEC 60093 | ||
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz | 5.0 @Frequency 1e+6 Hz | IEC 60250 | ||
| 20 @Frequency 100 Hz | 20 @Frequency 100 Hz | IEC 60250 | |||
| Dielectric Strength | 20.0 kV/mm | 508 kV/in | IEC 60243-1 | ||
| Dissipation Factor | 0.12 @Frequency 1e+6 Hz | 0.12 @Frequency 1e+6 Hz | IEC 60250 | ||
| 0.30 @Frequency 100 Hz | 0.30 @Frequency 100 Hz | IEC 60250 | |||
| Comparative Tracking Index | 600 V | 600 V | IEC 60112 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 220 °C | 428 °F | 10°C/min (DAM); ISO 11357-1/-3 | ||
| Descriptive Properties | |||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| Injection Molding | Yes | ||||
| Light Stabilized or Stable to Light | Yes | ||||
| Release Agent | Yes | ||||
| U.V. Stabilized or Stable to Weather | Yes | ||||
| With Fillers | Yes | ||||