- 密度 [g/cm3]: 1.12
- 拉伸强度 [MPa]: 25.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.12 g/cc | 0.0405 lb/in³ | ISO 1183 | ||
| Linear Mold Shrinkage, Flow | 0.0185 cm/cm | 0.0185 in/in | Parallel; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0185 cm/cm | 0.0185 in/in | Normal; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 25.0 MPa | 3630 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 6.0 % | 6.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 1.20 GPa | 174 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 1.20 J/cm² @Temperature -30.0 °C | 5.71 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 1.00e+15 ohm-cm | 1.00e+15 ohm-cm | IEC 60093 | ||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 120 µm/m-°C @Temperature 20.0 °C | 66.7 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 120 µm/m-°C @Temperature 20.0 °C | 66.7 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | IEC 60695-11-10 | ||
| V-2 @Thickness 0.800 mm | V-2 @Thickness 0.0315 in | IEC 60695-11-10 | |||
| Descriptive Properties | |||||
| Flame Retardant | Yes | ||||
| Flame Retarding Agent | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| High Impact or Impact Modified | Yes | ||||
| Injection Molding | Yes | ||||
| Without Fillers | Yes | ||||