- 密度 [g/cm3]: 1.1
- 吸水率 [%]: 9.0
- 拉伸强度 [MPa]: 60.0
- 热变形温度 [℃]: 170.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | ISO 1183 | ||
| Water Absorption | 9.0 % | 9.0 % | Sim. to ISO 62 | ||
| Moisture Absorption at Equilibrium | 3.0 % | 3.0 % | Humidity Absorption; Sim. to ISO 62 | ||
| High Load Melt Index | 44 g/10 min @Load 21.6 kg, Temperature 275 °C | 44 g/10 min @Load 47.6 lb, Temperature 527 °F | Calculated from Volume Flow Rate of 40 cm3/10min.; ISO 1133 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Yield | 60.0 MPa | 8700 psi | ISO 527-1/-2 | ||
| Elongation at Break | >= 50 % | >= 50 % | ISO 527-1/-2 | ||
| Elongation at Yield | 4.0 % | 4.0 % | ISO 527-1/-2 | ||
| Tensile Modulus | 2.70 GPa | 392 ksi | ISO 527-1/-2 | ||
| Charpy Impact Unnotched | NB @Temperature -30.0 °C | NB @Temperature -22.0 °F | ISO 179/1eU | ||
| NB @Temperature 23.0 °C | NB @Temperature 73.4 °F | ISO 179/1eU | |||
| Charpy Impact, Notched | 2.00 J/cm² @Temperature -30.0 °C | 9.52 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA | ||
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| CTE, linear, Transverse to Flow | 140 µm/m-°C @Temperature 20.0 °C | 77.8 µin/in-°F @Temperature 68.0 °F | ISO 11359-1/-2 | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 170 °C | 338 °F | ISO 75-1/-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 60.0 °C | 140 °F | ISO 75-1/-2 | ||
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695-11-10 | ||
| Descriptive Properties | |||||
| Blow Molding | Yes | ||||
| Heat Stabilized or Stable to Heat | Yes | ||||
| High Impact or Impact Modified | Yes | ||||
| Without Fillers | Yes | ||||