- 密度 [g/cm3]: 1.23
- 吸水率 [%]: 2.5
- 成型收缩率 [%]: 0.003
- 缺口冲击强度: 0.53
- 弯曲模量 [MPa]: 2.41
- 热变形温度 [℃]: 220.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.23 g/cc | 0.0444 lb/in³ | DAM; ISO 1183 | ||
| Filler Content | 15 % | 15 % | DAM | ||
| Water Absorption | 2.5 % @Temperature 23.0 °C | 2.5 % @Temperature 73.4 °F | Equilibrium 50%RH; DAM; ISO 62, Similar to | ||
| 7.6 % @Temperature 23.0 °C | 7.6 % @Temperature 73.4 °F | Saturation, immersed; DAM; ISO 62, Similar to | |||
| Linear Mold Shrinkage | 0.0030 cm/cm @Thickness 3.20 mm | 0.0030 in/in @Thickness 0.126 in | Flow; DAM | ||
| 0.0030 cm/cm @Thickness 1.60 mm | 0.0030 in/in @Thickness 0.0630 in | Flow; DAM | |||
| 0.0050 cm/cm @Thickness 6.40 mm | 0.0050 in/in @Thickness 0.252 in | Flow; DAM | |||
| 0.0090 cm/cm @Thickness 1.60 mm | 0.0090 in/in @Thickness 0.0630 in | Transverse; DAM | |||
| 0.010 cm/cm @Thickness 3.20 mm | 0.010 in/in @Thickness 0.126 in | Transverse; DAM | |||
| 0.013 cm/cm @Thickness 6.40 mm | 0.013 in/in @Thickness 0.252 in | Transverse; DAM | |||
| Linear Mold Shrinkage, Flow | 0.0030 cm/cm @Thickness 2.00 mm | 0.0030 in/in @Thickness 0.0787 in | Parallel; DAM; ISO 294-4 | ||
| Linear Mold Shrinkage, Transverse | 0.0080 cm/cm @Thickness 2.00 mm | 0.0080 in/in @Thickness 0.0787 in | Normal; DAM; ISO 294-4 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 72.0 MPa @Temperature 23.0 °C | 10400 psi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 135 MPa @Temperature 23.0 °C | 19600 psi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Tensile Strength | 75.0 MPa @Temperature 23.0 °C | 10900 psi @Temperature 73.4 °F | 50%RH; ASTM D638 | ||
| 128 MPa @Temperature 23.0 °C | 18600 psi @Temperature 73.4 °F | DAM; ASTM D638 | |||
| Tensile Stress | 4.30 MPa @Strain 0.240 %, Temperature 150 °C | 624 psi @Strain 0.240 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | ||
| 4.91 MPa @Strain 0.210 %, Temperature 80.0 °C | 712 psi @Strain 0.210 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 5.49 MPa @Strain 0.240 %, Temperature 120 °C | 796 psi @Strain 0.240 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 7.19 MPa @Strain 0.270 %, Temperature 40.0 °C | 1040 psi @Strain 0.270 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 7.60 MPa @Strain 0.250 %, Temperature -20.0 °C | 1100 psi @Strain 0.250 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.21 MPa @Strain 0.480 %, Temperature 150 °C | 1190 psi @Strain 0.480 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 8.31 MPa @Strain 0.420 %, Temperature 120 °C | 1210 psi @Strain 0.420 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 10.25 MPa @Strain 0.470 %, Temperature 80.0 °C | 1487 psi @Strain 0.470 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.01 MPa @Strain 0.520 %, Temperature 80.0 °C | 1742 psi @Strain 0.520 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 12.19 MPa @Strain 0.780 %, Temperature 150 °C | 1768 psi @Strain 0.780 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 12.69 MPa @Strain 0.620 %, Temperature 150 °C | 1841 psi @Strain 0.620 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 13.09 MPa @Strain 0.620 %, Temperature 120 °C | 1899 psi @Strain 0.620 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 13.59 MPa @Strain 0.560 %, Temperature 60.0 °C | 1971 psi @Strain 0.560 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 14.21 MPa @Strain 0.780 %, Temperature 120 °C | 2061 psi @Strain 0.780 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 15.57 MPa @Strain 0.480 %, Temperature 60.0 °C | 2258 psi @Strain 0.480 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 15.61 MPa @Strain 1.08 %, Temperature 150 °C | 2264 psi @Strain 1.08 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 16.63 MPa @Strain 0.830 %, Temperature 80.0 °C | 2412 psi @Strain 0.830 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 17.3 MPa @Strain 0.670 %, Temperature 40.0 °C | 2510 psi @Strain 0.670 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 18.45 MPa @Strain 1.40 %, Temperature 150 °C | 2676 psi @Strain 1.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.01 MPa @Strain 1.13 %, Temperature 120 °C | 2757 psi @Strain 1.13 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 19.23 MPa @Strain 1.02 %, Temperature 150 °C | 2789 psi @Strain 1.02 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 19.54 MPa @Strain 0.650 %, Temperature -20.0 °C | 2834 psi @Strain 0.650 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 20.23 MPa @Strain 1.02 %, Temperature 120 °C | 2934 psi @Strain 1.02 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 20.91 MPa @Strain 1.72 %, Temperature 150 °C | 3033 psi @Strain 1.72 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.63 MPa @Strain 0.950 %, Temperature 60.0 °C | 3137 psi @Strain 0.950 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 21.88 MPa @Strain 1.01 %, Temperature 80.0 °C | 3173 psi @Strain 1.01 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 22.41 MPa @Strain 1.20 %, Temperature 80.0 °C | 3250 psi @Strain 1.20 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.05 MPa @Strain 2.05 %, Temperature 150 °C | 3343 psi @Strain 2.05 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 23.18 MPa @Strain 1.49 %, Temperature 120 °C | 3362 psi @Strain 1.49 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 24.66 MPa @Strain 1.43 %, Temperature 150 °C | 3577 psi @Strain 1.43 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 24.97 MPa @Strain 2.38 %, Temperature 150 °C | 3622 psi @Strain 2.38 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 25.87 MPa @Strain 1.08 %, Temperature 40.0 °C | 3752 psi @Strain 1.08 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.29 MPa @Strain 1.43 %, Temperature 120 °C | 3813 psi @Strain 1.43 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 26.64 MPa @Strain 2.70 %, Temperature 150 °C | 3864 psi @Strain 2.70 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 26.81 MPa @Strain 1.86 %, Temperature 120 °C | 3888 psi @Strain 1.86 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 27.58 MPa @Strain 1.60 %, Temperature 80.0 °C | 4000 psi @Strain 1.60 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.13 MPa @Strain 3.05 %, Temperature 150 °C | 4080 psi @Strain 3.05 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.32 MPa @Strain 1.33 %, Temperature 60.0 °C | 4107 psi @Strain 1.33 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 28.78 MPa @Strain 0.950 %, Temperature 60.0 °C | 4174 psi @Strain 0.950 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 28.97 MPa @Strain 0.400 %, Temperature -40.0 °C | 4202 psi @Strain 0.400 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 29.16 MPa @Strain 1.85 %, Temperature 150 °C | 4229 psi @Strain 1.85 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 29.45 MPa @Strain 3.40 %, Temperature 150 °C | 4271 psi @Strain 3.40 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.54 MPa @Strain 1.06 %, Temperature -20.0 °C | 4284 psi @Strain 1.06 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 29.99 MPa @Strain 2.23 %, Temperature 120 °C | 4350 psi @Strain 2.23 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 30.42 MPa @Strain 1.50 %, Temperature 80.0 °C | 4412 psi @Strain 1.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 30.6 MPa @Strain 3.75 %, Temperature 150 °C | 4440 psi @Strain 3.75 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.52 MPa @Strain 1.84 %, Temperature 120 °C | 4572 psi @Strain 1.84 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 31.57 MPa @Strain 4.12 %, Temperature 150 °C | 4579 psi @Strain 4.12 %, Temperature 302 °F | 50%RH; ISO 11403-1/-2 | |||
| 31.88 MPa @Strain 1.97 %, Temperature 80.0 °C | 4624 psi @Strain 1.97 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 32.68 MPa @Strain 2.61 %, Temperature 120 °C | 4740 psi @Strain 2.61 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.03 MPa @Strain 2.28 %, Temperature 150 °C | 4791 psi @Strain 2.28 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 33.36 MPa @Strain 1.49 %, Temperature 40.0 °C | 4838 psi @Strain 1.49 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 33.89 MPa @Strain 1.70 %, Temperature 60.0 °C | 4915 psi @Strain 1.70 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 34.94 MPa @Strain 2.99 %, Temperature 120 °C | 5068 psi @Strain 2.99 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 35.6 MPa @Strain 2.36 %, Temperature 80.0 °C | 5160 psi @Strain 2.36 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 36.13 MPa @Strain 2.26 %, Temperature 120 °C | 5240 psi @Strain 2.26 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 36.36 MPa @Strain 2.69 %, Temperature 150 °C | 5274 psi @Strain 2.69 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 36.82 MPa @Strain 3.39 %, Temperature 120 °C | 5340 psi @Strain 3.39 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.35 MPa @Strain 1.43 %, Temperature -20.0 °C | 5417 psi @Strain 1.43 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 37.43 MPa @Strain 1.98 %, Temperature 80.0 °C | 5429 psi @Strain 1.98 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 38.29 MPa @Strain 3.79 %, Temperature 120 °C | 5554 psi @Strain 3.79 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 38.3 MPa @Strain 1.36 %, Temperature 60.0 °C | 5550 psi @Strain 1.36 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 38.64 MPa @Strain 2.73 %, Temperature 80.0 °C | 5604 psi @Strain 2.73 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.15 MPa @Strain 2.09 %, Temperature 60.0 °C | 5678 psi @Strain 2.09 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.21 MPa @Strain 3.13 %, Temperature 150 °C | 5687 psi @Strain 3.13 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 39.24 MPa @Strain 1.86 %, Temperature 40.0 °C | 5691 psi @Strain 1.86 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 39.48 MPa @Strain 4.23 %, Temperature 120 °C | 5726 psi @Strain 4.23 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 40.0 MPa @Strain 2.67 %, Temperature 120 °C | 5800 psi @Strain 2.67 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 40.43 MPa @Strain 4.67 %, Temperature 120 °C | 5864 psi @Strain 4.67 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.19 MPa @Strain 5.12 %, Temperature 120 °C | 5974 psi @Strain 5.12 %, Temperature 248 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.26 MPa @Strain 3.12 %, Temperature 80.0 °C | 5984 psi @Strain 3.12 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 41.64 MPa @Strain 3.58 %, Temperature 150 °C | 6039 psi @Strain 3.58 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 42.59 MPa @Strain 0.810 %, Temperature 40.0 °C | 6177 psi @Strain 0.810 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 43.25 MPa @Strain 3.53 %, Temperature 80.0 °C | 6273 psi @Strain 3.53 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.4 MPa @Strain 2.46 %, Temperature 60.0 °C | 6290 psi @Strain 2.46 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 43.49 MPa @Strain 3.11 %, Temperature 120 °C | 6308 psi @Strain 3.11 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 43.5 MPa @Strain 2.47 %, Temperature 80.0 °C | 6310 psi @Strain 2.47 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 43.56 MPa @Strain 4.00 %, Temperature 150 °C | 6318 psi @Strain 4.00 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 44.57 MPa @Strain 1.81 %, Temperature -20.0 °C | 6464 psi @Strain 1.81 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.69 MPa @Strain 2.24 %, Temperature 40.0 °C | 6482 psi @Strain 2.24 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 44.84 MPa @Strain 3.97 %, Temperature 80.0 °C | 6504 psi @Strain 3.97 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 45.14 MPa @Strain 4.46 %, Temperature 150 °C | 6547 psi @Strain 4.46 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 45.98 MPa @Strain 4.42 %, Temperature 80.0 °C | 6669 psi @Strain 4.42 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 46.32 MPa @Strain 3.54 %, Temperature 120 °C | 6718 psi @Strain 3.54 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 46.45 MPa @Strain 4.95 %, Temperature 150 °C | 6737 psi @Strain 4.95 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 46.84 MPa @Strain 1.80 %, Temperature 60.0 °C | 6794 psi @Strain 1.80 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 46.92 MPa @Strain 4.91 %, Temperature 80.0 °C | 6805 psi @Strain 4.91 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.13 MPa @Strain 2.84 %, Temperature 60.0 °C | 6836 psi @Strain 2.84 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 47.53 MPa @Strain 5.46 %, Temperature 150 °C | 6894 psi @Strain 5.46 %, Temperature 302 °F | DAM; ISO 11403-1/-2 | |||
| 47.64 MPa @Strain 5.42 %, Temperature 80.0 °C | 6910 psi @Strain 5.42 %, Temperature 176 °F | 50%RH; ISO 11403-1/-2 | |||
| 48.64 MPa @Strain 3.98 %, Temperature 120 °C | 7055 psi @Strain 3.98 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 48.67 MPa @Strain 2.95 %, Temperature 80.0 °C | 7059 psi @Strain 2.95 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 49.68 MPa @Strain 2.64 %, Temperature 40.0 °C | 7205 psi @Strain 2.64 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.12 MPa @Strain 3.22 %, Temperature 60.0 °C | 7269 psi @Strain 3.22 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 50.5 MPa @Strain 4.48 %, Temperature 120 °C | 7320 psi @Strain 4.48 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 50.81 MPa @Strain 2.19 %, Temperature -20.0 °C | 7369 psi @Strain 2.19 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 51.93 MPa @Strain 4.98 %, Temperature 120 °C | 7532 psi @Strain 4.98 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 52.46 MPa @Strain 3.64 %, Temperature 60.0 °C | 7609 psi @Strain 3.64 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 52.69 MPa @Strain 1.02 %, Temperature 40.0 °C | 7642 psi @Strain 1.02 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 52.87 MPa @Strain 3.44 %, Temperature 80.0 °C | 7668 psi @Strain 3.44 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 53.13 MPa @Strain 5.45 %, Temperature 120 °C | 7706 psi @Strain 5.45 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 53.93 MPa @Strain 3.05 %, Temperature 40.0 °C | 7822 psi @Strain 3.05 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.1 MPa @Strain 5.97 %, Temperature 120 °C | 7850 psi @Strain 5.97 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 54.24 MPa @Strain 4.10 %, Temperature 60.0 °C | 7867 psi @Strain 4.10 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 54.54 MPa @Strain 2.24 %, Temperature 60.0 °C | 7910 psi @Strain 2.24 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 54.85 MPa @Strain 6.47 %, Temperature 120 °C | 7955 psi @Strain 6.47 %, Temperature 248 °F | DAM; ISO 11403-1/-2 | |||
| 55.51 MPa @Strain 4.62 %, Temperature 60.0 °C | 8051 psi @Strain 4.62 %, Temperature 140 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.21 MPa @Strain 3.95 %, Temperature 80.0 °C | 8153 psi @Strain 3.95 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 56.39 MPa @Strain 2.57 %, Temperature -20.0 °C | 8179 psi @Strain 2.57 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 56.72 MPa @Strain 0.800 %, Temperature -40.0 °C | 8227 psi @Strain 0.800 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 57.19 MPa @Strain 3.47 %, Temperature 40.0 °C | 8295 psi @Strain 3.47 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 58.62 MPa @Strain 4.50 %, Temperature 80.0 °C | 8502 psi @Strain 4.50 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 59.7 MPa @Strain 3.93 %, Temperature 40.0 °C | 8660 psi @Strain 3.93 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 60.49 MPa @Strain 5.09 %, Temperature 80.0 °C | 8773 psi @Strain 5.09 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 60.93 MPa @Strain 2.67 %, Temperature 60.0 °C | 8837 psi @Strain 2.67 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 61.39 MPa @Strain 2.95 %, Temperature -20.0 °C | 8904 psi @Strain 2.95 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.46 MPa @Strain 4.44 %, Temperature 40.0 °C | 8914 psi @Strain 4.44 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 61.84 MPa @Strain 5.67 %, Temperature 80.0 °C | 8969 psi @Strain 5.67 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 62.15 MPa @Strain 1.24 %, Temperature 40.0 °C | 9014 psi @Strain 1.24 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 62.69 MPa @Strain 5.03 %, Temperature 40.0 °C | 9092 psi @Strain 5.03 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 62.8 MPa @Strain 6.27 %, Temperature 80.0 °C | 9110 psi @Strain 6.27 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 63.4 MPa @Strain 1.10 %, Temperature 23.0 °C | 9200 psi @Strain 1.10 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 63.51 MPa @Strain 5.58 %, Temperature 40.0 °C | 9211 psi @Strain 5.58 %, Temperature 104 °F | 50%RH; ISO 11403-1/-2 | |||
| 63.53 MPa @Strain 6.93 %, Temperature 80.0 °C | 9214 psi @Strain 6.93 %, Temperature 176 °F | DAM; ISO 11403-1/-2 | |||
| 65.61 MPa @Strain 3.37 %, Temperature -20.0 °C | 9516 psi @Strain 3.37 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 66.76 MPa @Strain 3.14 %, Temperature 60.0 °C | 9683 psi @Strain 3.14 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 68.83 MPa @Strain 3.84 %, Temperature -20.0 °C | 9983 psi @Strain 3.84 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 70.36 MPa @Strain 1.44 %, Temperature 40.0 °C | 10200 psi @Strain 1.44 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 70.95 MPa @Strain 4.37 %, Temperature -20.0 °C | 10290 psi @Strain 4.37 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 71.51 MPa @Strain 3.65 %, Temperature 60.0 °C | 10370 psi @Strain 3.65 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 71.52 MPa @Strain 1.26 %, Temperature 23.0 °C | 10370 psi @Strain 1.26 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 72.22 MPa @Strain 4.95 %, Temperature -20.0 °C | 10470 psi @Strain 4.95 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 72.97 MPa @Strain 5.54 %, Temperature -20.0 °C | 10580 psi @Strain 5.54 %, Temperature -4.00 °F | 50%RH; ISO 11403-1/-2 | |||
| 74.67 MPa @Strain 4.24 %, Temperature 60.0 °C | 10830 psi @Strain 4.24 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 76.58 MPa @Strain 4.92 %, Temperature 60.0 °C | 11110 psi @Strain 4.92 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 77.51 MPa @Strain 5.57 %, Temperature 60.0 °C | 11240 psi @Strain 5.57 %, Temperature 140 °F | DAM; ISO 11403-1/-2 | |||
| 78.09 MPa @Strain 1.65 %, Temperature 40.0 °C | 11330 psi @Strain 1.65 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 79.3 MPa @Strain 1.41 %, Temperature 23.0 °C | 11500 psi @Strain 1.41 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 82.07 MPa @Strain 1.20 %, Temperature -40.0 °C | 11900 psi @Strain 1.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 84.36 MPa @Strain 1.46 %, Temperature 0.000 °C | 12240 psi @Strain 1.46 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 84.86 MPa @Strain 1.85 %, Temperature 40.0 °C | 12310 psi @Strain 1.85 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 86.89 MPa @Strain 1.57 %, Temperature 23.0 °C | 12600 psi @Strain 1.57 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 90.95 MPa @Strain 2.07 %, Temperature 40.0 °C | 13190 psi @Strain 2.07 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 92.6 MPa @Strain 1.63 %, Temperature 0.000 °C | 13400 psi @Strain 1.63 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 94.32 MPa @Strain 1.74 %, Temperature 23.0 °C | 13680 psi @Strain 1.74 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 96.25 MPa @Strain 2.30 %, Temperature 40.0 °C | 13960 psi @Strain 2.30 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 98.54 MPa @Strain 1.69 %, Temperature -20.0 °C | 14290 psi @Strain 1.69 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 100.26 MPa @Strain 1.79 %, Temperature 0.000 °C | 14542 psi @Strain 1.79 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 101.07 MPa @Strain 2.55 %, Temperature 40.0 °C | 14659 psi @Strain 2.55 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 101.31 MPa @Strain 1.90 %, Temperature 23.0 °C | 14694 psi @Strain 1.90 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 105.22 MPa @Strain 2.84 %, Temperature 40.0 °C | 15261 psi @Strain 2.84 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 106.21 MPa @Strain 1.60 %, Temperature -40.0 °C | 15404 psi @Strain 1.60 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 107.08 MPa @Strain 1.94 %, Temperature 0.000 °C | 15531 psi @Strain 1.94 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 107.42 MPa @Strain 1.87 %, Temperature -20.0 °C | 15580 psi @Strain 1.87 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 107.9 MPa @Strain 2.07 %, Temperature 23.0 °C | 15650 psi @Strain 2.07 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 108.43 MPa @Strain 3.16 %, Temperature 40.0 °C | 15726 psi @Strain 3.16 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 110.46 MPa @Strain 3.53 %, Temperature 40.0 °C | 16021 psi @Strain 3.53 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 110.72 MPa @Strain 4.01 %, Temperature 40.0 °C | 16059 psi @Strain 4.01 %, Temperature 104 °F | DAM; ISO 11403-1/-2 | |||
| 113.39 MPa @Strain 2.09 %, Temperature 0.000 °C | 16446 psi @Strain 2.09 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 114.51 MPa @Strain 2.25 %, Temperature 23.0 °C | 16608 psi @Strain 2.25 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 115.67 MPa @Strain 2.05 %, Temperature -20.0 °C | 16777 psi @Strain 2.05 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 119.64 MPa @Strain 2.24 %, Temperature 0.000 °C | 17352 psi @Strain 2.24 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 120.67 MPa @Strain 2.45 %, Temperature 23.0 °C | 17502 psi @Strain 2.45 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 122.31 MPa @Strain 2.20 %, Temperature -20.0 °C | 17740 psi @Strain 2.20 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 125.45 MPa @Strain 2.39 %, Temperature 0.000 °C | 18195 psi @Strain 2.39 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 126.22 MPa @Strain 2.66 %, Temperature 23.0 °C | 18307 psi @Strain 2.66 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 126.72 MPa @Strain 2.00 %, Temperature -40.0 °C | 18379 psi @Strain 2.00 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 128.57 MPa @Strain 2.35 %, Temperature -20.0 °C | 18648 psi @Strain 2.35 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 130.84 MPa @Strain 2.55 %, Temperature 0.000 °C | 18977 psi @Strain 2.55 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 130.93 MPa @Strain 2.89 %, Temperature 23.0 °C | 18990 psi @Strain 2.89 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 134.82 MPa @Strain 3.15 %, Temperature 23.0 °C | 19554 psi @Strain 3.15 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 135.2 MPa @Strain 2.52 %, Temperature -20.0 °C | 19610 psi @Strain 2.52 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 135.95 MPa @Strain 2.71 %, Temperature 0.000 °C | 19718 psi @Strain 2.71 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 137.78 MPa @Strain 3.44 %, Temperature 23.0 °C | 19983 psi @Strain 3.44 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 139.16 MPa @Strain 3.81 %, Temperature 23.0 °C | 20183 psi @Strain 3.81 %, Temperature 73.4 °F | DAM; ISO 11403-1/-2 | |||
| 140.72 MPa @Strain 2.87 %, Temperature 0.000 °C | 20410 psi @Strain 2.87 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 141.08 MPa @Strain 2.68 %, Temperature -20.0 °C | 20462 psi @Strain 2.68 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 144.77 MPa @Strain 3.03 %, Temperature 0.000 °C | 20997 psi @Strain 3.03 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 146.03 MPa @Strain 2.40 %, Temperature -40.0 °C | 21180 psi @Strain 2.40 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 146.62 MPa @Strain 2.85 %, Temperature -20.0 °C | 21265 psi @Strain 2.85 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 148.76 MPa @Strain 3.20 %, Temperature 0.000 °C | 21576 psi @Strain 3.20 %, Temperature 32.0 °F | DAM; ISO 11403-1/-2 | |||
| 151.5 MPa @Strain 3.00 %, Temperature -20.0 °C | 21970 psi @Strain 3.00 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 156.08 MPa @Strain 3.17 %, Temperature -20.0 °C | 22638 psi @Strain 3.17 %, Temperature -4.00 °F | DAM; ISO 11403-1/-2 | |||
| 161.72 MPa @Strain 2.80 %, Temperature -40.0 °C | 23456 psi @Strain 2.80 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| 175 MPa @Strain 3.20 %, Temperature -40.0 °C | 25400 psi @Strain 3.20 %, Temperature -40.0 °F | DAM; ISO 11403-1/-2 | |||
| Elongation at Break | 3.5 % @Temperature 23.0 °C | 3.5 % @Temperature 73.4 °F | DAM; ASTM D638 | ||
| 4.0 % @Temperature 23.0 °C | 4.0 % @Temperature 73.4 °F | DAM; ISO 527 | |||
| 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | 50%RH; ASTM D638 | |||
| 10 % @Temperature 23.0 °C | 10 % @Temperature 73.4 °F | 50%RH; ISO 527 | |||
| Tensile Modulus | 3.50 GPa @Temperature 23.0 °C | 508 ksi @Temperature 73.4 °F | 50%RH; ISO 527 | ||
| 6.00 GPa @Temperature 23.0 °C | 870 ksi @Temperature 73.4 °F | DAM; ISO 527 | |||
| Flexural Modulus | 2.41 GPa @Temperature 23.0 °C | 350 ksi @Temperature 73.4 °F | 50%RH; ASTM D790 | ||
| 5.00 GPa @Temperature 23.0 °C | 725 ksi @Temperature 73.4 °F | DAM; ISO 178 | |||
| 5.38 GPa @Temperature 23.0 °C | 780 ksi @Temperature 73.4 °F | DAM; ASTM D790 | |||
| Shear Modulus | 0.0170 GPa @Temperature 226 °C | 2.47 ksi @Temperature 439 °F | DAM; ISO 6721 | ||
| 0.114 GPa @Temperature 220 °C | 16.5 ksi @Temperature 428 °F | DAM; ISO 6721 | |||
| 0.203 GPa @Temperature 214 °C | 29.4 ksi @Temperature 417 °F | DAM; ISO 6721 | |||
| 0.244 GPa @Temperature 210 °C | 35.4 ksi @Temperature 410 °F | DAM; ISO 6721 | |||
| 0.285 GPa @Temperature 204 °C | 41.3 ksi @Temperature 399 °F | DAM; ISO 6721 | |||
| 0.309 GPa @Temperature 200 °C | 44.8 ksi @Temperature 392 °F | DAM; ISO 6721 | |||
| 0.355 GPa @Temperature 190 °C | 51.5 ksi @Temperature 374 °F | DAM; ISO 6721 | |||
| 0.380 GPa @Temperature 180 °C | 55.1 ksi @Temperature 356 °F | DAM; ISO 6721 | |||
| 0.396 GPa @Temperature 170 °C | 57.4 ksi @Temperature 338 °F | DAM; ISO 6721 | |||
| 0.407 GPa @Temperature 160 °C | 59.0 ksi @Temperature 320 °F | DAM; ISO 6721 | |||
| 0.415 GPa @Temperature 150 °C | 60.2 ksi @Temperature 302 °F | DAM; ISO 6721 | |||
| 0.421 GPa @Temperature 140 °C | 61.1 ksi @Temperature 284 °F | DAM; ISO 6721 | |||
| 0.425 GPa @Temperature 130 °C | 61.6 ksi @Temperature 266 °F | DAM; ISO 6721 | |||
| 0.429 GPa @Temperature 120 °C | 62.2 ksi @Temperature 248 °F | DAM; ISO 6721 | |||
| 0.433 GPa @Temperature 110 °C | 62.8 ksi @Temperature 230 °F | DAM; ISO 6721 | |||
| 0.440 GPa @Temperature 100 °C | 63.8 ksi @Temperature 212 °F | DAM; ISO 6721 | |||
| 0.454 GPa @Temperature 90.0 °C | 65.8 ksi @Temperature 194 °F | DAM; ISO 6721 | |||
| 0.481 GPa @Temperature 80.0 °C | 69.8 ksi @Temperature 176 °F | DAM; ISO 6721 | |||
| 0.537 GPa @Temperature 70.0 °C | 77.9 ksi @Temperature 158 °F | DAM; ISO 6721 | |||
| 0.663 GPa @Temperature 60.0 °C | 96.2 ksi @Temperature 140 °F | DAM; ISO 6721 | |||
| 0.967 GPa @Temperature 50.0 °C | 140 ksi @Temperature 122 °F | DAM; ISO 6721 | |||
| 1.215 GPa @Temperature 40.0 °C | 176.2 ksi @Temperature 104 °F | DAM; ISO 6721 | |||
| 1.313 GPa @Temperature 30.0 °C | 190.4 ksi @Temperature 86.0 °F | DAM; ISO 6721 | |||
| 1.374 GPa @Temperature 20.0 °C | 199.3 ksi @Temperature 68.0 °F | DAM; ISO 6721 | |||
| 1.419 GPa @Temperature 10.0 °C | 205.8 ksi @Temperature 50.0 °F | DAM; ISO 6721 | |||
| 1.451 GPa @Temperature 0.000 °C | 210.5 ksi @Temperature 32.0 °F | DAM; ISO 6721 | |||
| 1.465 GPa @Temperature -10.0 °C | 212.5 ksi @Temperature 14.0 °F | DAM; ISO 6721 | |||
| 1.475 GPa @Temperature -20.0 °C | 213.9 ksi @Temperature -4.00 °F | DAM; ISO 6721 | |||
| 1.489 GPa @Temperature -30.0 °C | 216.0 ksi @Temperature -22.0 °F | DAM; ISO 6721 | |||
| 1.514 GPa @Temperature -40.0 °C | 219.6 ksi @Temperature -40.0 °F | DAM; ISO 6721 | |||
| 1.557 GPa @Temperature -50.0 °C | 225.8 ksi @Temperature -58.0 °F | DAM; ISO 6721 | |||
| Izod Impact, Notched | 0.530 J/cm @Temperature 23.0 °C | 0.993 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D256 | ||
| 1.17 J/cm @Temperature 23.0 °C | 2.19 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D256 | |||
| Izod Impact, Unnotched | 5.33 J/cm @Temperature 23.0 °C | 9.99 ft-lb/in @Temperature 73.4 °F | DAM; ASTM D4812 | ||
| 12.25 J/cm @Temperature 23.0 °C | 22.95 ft-lb/in @Temperature 73.4 °F | 50%RH; ASTM D4812 | |||
| Izod Impact, Notched (ISO) | 5.00 kJ/m² @Temperature -40.0 °C | 2.38 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1A | ||
| 5.00 kJ/m² @Temperature -30.0 °C | 2.38 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 180/1A | |||
| 6.00 kJ/m² @Temperature 23.0 °C | 2.86 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1A | |||
| 12.0 kJ/m² @Temperature 23.0 °C | 5.71 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 180/1A | |||
| Izod Impact, Unnotched (ISO) | 40.0 kJ/m² @Temperature -40.0 °C | 19.0 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 180/1U | ||
| 45.0 kJ/m² @Temperature 23.0 °C | 21.4 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 180/1U | |||
| Charpy Impact Unnotched | 4.50 J/cm² @Temperature -30.0 °C | 21.4 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eU | ||
| 5.00 J/cm² @Temperature 23.0 °C | 23.8 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eU | |||
| 5.40 J/cm² @Temperature -30.0 °C | 25.7 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eU | |||
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eU | |||
| Charpy Impact, Notched | 0.600 J/cm² @Temperature -30.0 °C | 2.86 ft-lb/in² @Temperature -22.0 °F | DAM; ISO 179/1eA | ||
| 0.600 J/cm² @Temperature -40.0 °C | 2.86 ft-lb/in² @Temperature -40.0 °F | DAM; ISO 179/1eA | |||
| 0.700 J/cm² @Temperature 23.0 °C | 3.33 ft-lb/in² @Temperature 73.4 °F | DAM; ISO 179/1eA | |||
| 1.40 J/cm² @Temperature -30.0 °C | 6.66 ft-lb/in² @Temperature -22.0 °F | 50%RH; ISO 179/1eA | |||
| 1.50 J/cm² @Temperature 23.0 °C | 7.14 ft-lb/in² @Temperature 73.4 °F | 50%RH; ISO 179/1eA | |||
| Thermal Properties | Metric | English | Comments | ||
| CTE, linear, Parallel to Flow | 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | ||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| 500 µm/m-°C @Temperature -40.0 - 23.0 °C | 278 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 23.0 - 55.0 °C | 278 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 500 µm/m-°C @Temperature 55.0 - 160 °C | 278 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| CTE, linear, Transverse to Flow | 81.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 45.0 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ISO 11359-1/-2 | ||
| 81.0 µm/m-°C @Temperature -40.0 - 23.0 °C | 45.0 µin/in-°F @Temperature -40.0 - 73.4 °F | DAM; ASTM E 831 | |||
| 109 µm/m-°C @Temperature 23.0 - 55.0 °C | 60.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ISO 11359-1/-2 | |||
| 109 µm/m-°C @Temperature 23.0 - 55.0 °C | 60.6 µin/in-°F @Temperature 73.4 - 131 °F | DAM; ASTM E 831 | |||
| 134 µm/m-°C @Temperature 55.0 - 160 °C | 74.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ISO 11359-1/-2 | |||
| 134 µm/m-°C @Temperature 55.0 - 160 °C | 74.4 µin/in-°F @Temperature 131 - 320 °F | DAM; ASTM E 831 | |||
| Deflection Temperature at 0.46 MPa (66 psi) | 220 °C | 428 °F | DAM; ASTM D648 | ||
| 220 °C | 428 °F | DAM; ISO 75-1/-2 | |||
| Deflection Temperature at 1.8 MPa (264 psi) | 200 °C | 392 °F | DAM; ASTM D648 | ||
| 200 °C | 392 °F | DAM; ISO 75-1/-2 | |||
| UL RTI, Electrical | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical with Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| UL RTI, Mechanical without Impact | 65.0 °C @Thickness 1.50 mm | 149 °F @Thickness 0.0591 in | DAM; UL 746B | ||
| Flammability, UL94 | HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; IEC 60695-11-10 | ||
| HB @Thickness 1.50 mm | HB @Thickness 0.0591 in | DAM; UL94 | |||
| Oxygen Index | 21 % | 21 % | DAM; ISO 4589-1/-2 | ||
| Processing Properties | Metric | English | Comments | ||
| Melt Temperature | 221 °C | 430 °F | 10°C/min; DAM; ISO 11357-1/-3 | ||
| 270 °C | 518 °F | DAM; Optimum | |||
| 260 - 280 °C | 500 - 536 °F | DAM | |||
| Mold Temperature | 70.0 - 120 °C | 158 - 248 °F | DAM | ||
| 100 °C | 212 °F | DAM; optimum | |||
| Drying Temperature | 80.0 °C | 176 °F | DAM | ||
| Dry Time | 2.00 - 4.00 hour | 2.00 - 4.00 hour | DAM | ||
| Moisture Content | <= 0.20 % | <= 0.20 % | DAM | ||
| Descriptive Properties | |||||
| Additive | Lubricant | DAM | |||
| Appearance | Natural Color | DAM | |||
| Drying Recommended | Yes, if moisture content of resin exceeds recommended level | DAM | |||
| Features | General Purpose | DAM | |||
| Gloss, High | DAM | ||||
| Stiffness, Good | DAM | ||||
| Strength, Good | DAM | ||||
| Surface Finish, Good | DAM | ||||
| Filler | Glass fiber reinforcement | DAM | |||
| Forms | Pellets | DAM | |||
| Generic | Nylon 6 | DAM | |||
| Material Status | Current | DAM | |||
| Part Marking Code | >PA6-GF15< | ISO 11469; DAM | |||
| Polymer Family | Polyamide | DAM | |||
| Polymer Type | PA6 | DAM | |||
| Processing Method | Injection Molding | DAM | |||
| Product Category | Glass Reinforced Resins | DAM | |||
| Region Available - Global | Yes | DAM | |||
| Resin Identification | PA6-GF15 | ISO 1043; DAM | |||
| RoHS Compliance | Contact Manufacturer | DAM | |||
| Ultrasonic Weldable | Yes | DAM | |||
| Uses | Appliance Components | DAM | |||
| High Gloss Applications | DAM | ||||
| Industrial Applications | DAM | ||||
| Sporting Goods | DAM | ||||