  3. PA6
  4. DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6

DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6

DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6 物性表: DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6物性表及特性介绍,DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6注塑参数详情,如需DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6下载, 可到相关下载区下载
  • 密度 [g/cm3]: 1.36
  • 吸水率 [%]: 1.9
  • 成型收缩率 [%]: 0.002
  • 缺口冲击强度: 1.33
  • 弯曲模量 [MPa]: 4.48
  • 热变形温度 [℃]: 220.0
 
Physical PropertiesMetricEnglishComments
Density 1.36 g/cc0.0491 lb/in³DAM; ISO 1183
Filler Content 30 %30 %DAM
Water Absorption  1.9 %
@Temperature 23.0 °C		1.9 %
@Temperature 73.4 °F		Equilibrium 50%RH; DAM; ISO 62, Similar to
 6.3 %
@Temperature 23.0 °C		6.3 %
@Temperature 73.4 °F		Saturation, immersed; DAM; ISO 62, Similar to
Linear Mold Shrinkage  0.0020 cm/cm
@Thickness 1.60 mm		0.0020 in/in
@Thickness 0.0630 in		Flow; DAM
 0.0020 cm/cm
@Thickness 3.20 mm		0.0020 in/in
@Thickness 0.126 in		Flow; DAM
 0.010 cm/cm
@Thickness 3.20 mm		0.010 in/in
@Thickness 0.126 in		Transverse; DAM
 0.010 cm/cm
@Thickness 1.60 mm		0.010 in/in
@Thickness 0.0630 in		Transverse; DAM
Linear Mold Shrinkage, Flow 0.0020 cm/cm
@Thickness 2.00 mm		0.0020 in/in
@Thickness 0.0787 in		Parallel; DAM; ISO 294-4
Linear Mold Shrinkage, Transverse 0.0060 cm/cm
@Thickness 2.00 mm		0.0060 in/in
@Thickness 0.0787 in		Normal; DAM; ISO 294-4
 
Mechanical PropertiesMetricEnglishComments
Tensile Strength at Break  115 MPa
@Temperature 23.0 °C		16700 psi
@Temperature 73.4 °F		50%RH; ISO 527
 185 MPa
@Temperature 23.0 °C		26800 psi
@Temperature 73.4 °F		DAM; ISO 527
Tensile Strength  117 MPa
@Temperature 23.0 °C		17000 psi
@Temperature 73.4 °F		50%RH; ASTM D638
 178 MPa
@Temperature 23.0 °C		25800 psi
@Temperature 73.4 °F		DAM; ASTM D638
Tensile Stress  21.8 MPa
@Strain 0.350 %,
Temperature 120 °C		3160 psi
@Strain 0.350 %,
Temperature 248 °F		DAM; ISO 527
 23.5 MPa
@Strain 0.350 %,
Temperature 90.0 °C		3410 psi
@Strain 0.350 %,
Temperature 194 °F		DAM; ISO 527
 30.5 MPa
@Strain 0.310 %,
Temperature 60.0 °C		4420 psi
@Strain 0.310 %,
Temperature 140 °F		DAM; ISO 527
 31.8 MPa
@Strain 0.220 %,
Temperature 23.0 °C		4610 psi
@Strain 0.220 %,
Temperature 73.4 °F		DAM; ISO 527
 32.3 MPa
@Strain 0.250 %,
Temperature 40.0 °C		4680 psi
@Strain 0.250 %,
Temperature 104 °F		DAM; ISO 527
 33.8 MPa
@Strain 0.210 %,
Temperature 0.000 °C		4900 psi
@Strain 0.210 %,
Temperature 32.0 °F		DAM; ISO 527
 36.0 MPa
@Strain 0.210 %,
Temperature -20.0 °C		5220 psi
@Strain 0.210 %,
Temperature -4.00 °F		DAM; ISO 527
 38.0 MPa
@Strain 0.700 %,
Temperature 120 °C		5510 psi
@Strain 0.700 %,
Temperature 248 °F		DAM; ISO 527
 41.7 MPa
@Strain 0.700 %,
Temperature 90.0 °C		6050 psi
@Strain 0.700 %,
Temperature 194 °F		DAM; ISO 527
 50.2 MPa
@Strain 1.05 %,
Temperature 120 °C		7280 psi
@Strain 1.05 %,
Temperature 248 °F		DAM; ISO 527
 53.3 MPa
@Strain 0.620 %,
Temperature 60.0 °C		7730 psi
@Strain 0.620 %,
Temperature 140 °F		DAM; ISO 527
 55.9 MPa
@Strain 1.05 %,
Temperature 90.0 °C		8110 psi
@Strain 1.05 %,
Temperature 194 °F		DAM; ISO 527
 59.5 MPa
@Strain 1.40 %,
Temperature 120 °C		8630 psi
@Strain 1.40 %,
Temperature 248 °F		DAM; ISO 527
 60.3 MPa
@Strain 0.500 %,
Temperature 40.0 °C		8750 psi
@Strain 0.500 %,
Temperature 104 °F		DAM; ISO 527
 61.9 MPa
@Strain 0.440 %,
Temperature 23.0 °C		8980 psi
@Strain 0.440 %,
Temperature 73.4 °F		DAM; ISO 527
 64.7 MPa
@Strain 0.420 %,
Temperature 0.000 °C		9380 psi
@Strain 0.420 %,
Temperature 32.0 °F		DAM; ISO 527
 66.5 MPa
@Strain 1.75 %,
Temperature 120 °C		9650 psi
@Strain 1.75 %,
Temperature 248 °F		DAM; ISO 527
 66.8 MPa
@Strain 1.40 %,
Temperature 90.0 °C		9690 psi
@Strain 1.40 %,
Temperature 194 °F		DAM; ISO 527
 67.9 MPa
@Strain 0.420 %,
Temperature -20.0 °C		9850 psi
@Strain 0.420 %,
Temperature -4.00 °F		DAM; ISO 527
 70.7 MPa
@Strain 0.930 %,
Temperature 60.0 °C		10300 psi
@Strain 0.930 %,
Temperature 140 °F		DAM; ISO 527
 71.8 MPa
@Strain 2.10 %,
Temperature 120 °C		10400 psi
@Strain 2.10 %,
Temperature 248 °F		DAM; ISO 527
 75.0 MPa
@Strain 1.75 %,
Temperature 90.0 °C		10900 psi
@Strain 1.75 %,
Temperature 194 °F		DAM; ISO 527
 75.7 MPa
@Strain 2.45 %,
Temperature 120 °C		11000 psi
@Strain 2.45 %,
Temperature 248 °F		DAM; ISO 527
 78.7 MPa
@Strain 2.80 %,
Temperature 120 °C		11400 psi
@Strain 2.80 %,
Temperature 248 °F		DAM; ISO 527
 80.8 MPa
@Strain 3.15 %,
Temperature 120 °C		11700 psi
@Strain 3.15 %,
Temperature 248 °F		DAM; ISO 527
 81.3 MPa
@Strain 2.10 %,
Temperature 90.0 °C		11800 psi
@Strain 2.10 %,
Temperature 194 °F		DAM; ISO 527
 82.3 MPa
@Strain 3.50 %,
Temperature 120 °C		11900 psi
@Strain 3.50 %,
Temperature 248 °F		DAM; Break; ISO 527
 83.7 MPa
@Strain 0.750 %,
Temperature 40.0 °C		12100 psi
@Strain 0.750 %,
Temperature 104 °F		DAM; ISO 527
 84.0 MPa
@Strain 1.24 %,
Temperature 60.0 °C		12200 psi
@Strain 1.24 %,
Temperature 140 °F		DAM; ISO 527
 85.9 MPa
@Strain 2.45 %,
Temperature 90.0 °C		12500 psi
@Strain 2.45 %,
Temperature 194 °F		DAM; ISO 527
 89.2 MPa
@Strain 2.80 %,
Temperature 90.0 °C		12900 psi
@Strain 2.80 %,
Temperature 194 °F		DAM; ISO 527
 89.2 MPa
@Strain 0.660 %,
Temperature 23.0 °C		12900 psi
@Strain 0.660 %,
Temperature 73.4 °F		DAM; ISO 527
 91.6 MPa
@Strain 3.15 %,
Temperature 90.0 °C		13300 psi
@Strain 3.15 %,
Temperature 194 °F		DAM; ISO 527
 92.4 MPa
@Strain 0.630 %,
Temperature 0.000 °C		13400 psi
@Strain 0.630 %,
Temperature 32.0 °F		DAM; ISO 527
 93.5 MPa
@Strain 3.50 %,
Temperature 90.0 °C		13600 psi
@Strain 3.50 %,
Temperature 194 °F		DAM; Break; ISO 527
 94.4 MPa
@Strain 1.55 %,
Temperature 60.0 °C		13700 psi
@Strain 1.55 %,
Temperature 140 °F		DAM; ISO 527
 96.0 MPa
@Strain 0.630 %,
Temperature -20.0 °C		13900 psi
@Strain 0.630 %,
Temperature -4.00 °F		DAM; ISO 527
 102 MPa
@Strain 1.86 %,
Temperature 60.0 °C		14800 psi
@Strain 1.86 %,
Temperature 140 °F		DAM; ISO 527
 103 MPa
@Strain 1.00 %,
Temperature 40.0 °C		14900 psi
@Strain 1.00 %,
Temperature 104 °F		DAM; ISO 527
 109 MPa
@Strain 2.17 %,
Temperature 60.0 °C		15800 psi
@Strain 2.17 %,
Temperature 140 °F		DAM; ISO 527
 113 MPa
@Strain 0.880 %,
Temperature 23.0 °C		16400 psi
@Strain 0.880 %,
Temperature 73.4 °F		DAM; ISO 527
 114 MPa
@Strain 2.48 %,
Temperature 60.0 °C		16500 psi
@Strain 2.48 %,
Temperature 140 °F		DAM; ISO 527
 117 MPa
@Strain 2.79 %,
Temperature 60.0 °C		17000 psi
@Strain 2.79 %,
Temperature 140 °F		DAM; ISO 527
 117 MPa
@Strain 0.840 %,
Temperature 0.000 °C		17000 psi
@Strain 0.840 %,
Temperature 32.0 °F		DAM; ISO 527
 118 MPa
@Strain 1.25 %,
Temperature 40.0 °C		17100 psi
@Strain 1.25 %,
Temperature 104 °F		DAM; ISO 527
 120 MPa
@Strain 3.10 %,
Temperature 60.0 °C		17400 psi
@Strain 3.10 %,
Temperature 140 °F		DAM; Break; ISO 527
 120 MPa
@Strain 0.840 %,
Temperature -20.0 °C		17400 psi
@Strain 0.840 %,
Temperature -4.00 °F		DAM; ISO 527
 129 MPa
@Strain 1.50 %,
Temperature 40.0 °C		18700 psi
@Strain 1.50 %,
Temperature 104 °F		DAM; ISO 527
 132 MPa
@Strain 1.10 %,
Temperature 23.0 °C		19100 psi
@Strain 1.10 %,
Temperature 73.4 °F		DAM; ISO 527
 137 MPa
@Strain 1.75 %,
Temperature 40.0 °C		19900 psi
@Strain 1.75 %,
Temperature 104 °F		DAM; ISO 527
 138 MPa
@Strain 1.05 %,
Temperature 0.000 °C		20000 psi
@Strain 1.05 %,
Temperature 32.0 °F		DAM; ISO 527
 142 MPa
@Strain 1.05 %,
Temperature -20.0 °C		20600 psi
@Strain 1.05 %,
Temperature -4.00 °F		DAM; ISO 527
 143 MPa
@Strain 2.00 %,
Temperature 40.0 °C		20700 psi
@Strain 2.00 %,
Temperature 104 °F		DAM; ISO 527
 147 MPa
@Strain 2.25 %,
Temperature 40.0 °C		21300 psi
@Strain 2.25 %,
Temperature 104 °F		DAM; ISO 527
 149 MPa
@Strain 2.50 %,
Temperature 40.0 °C		21600 psi
@Strain 2.50 %,
Temperature 104 °F		DAM; Break; ISO 527
 149 MPa
@Strain 1.32 %,
Temperature 23.0 °C		21600 psi
@Strain 1.32 %,
Temperature 73.4 °F		DAM; ISO 527
 156 MPa
@Strain 1.26 %,
Temperature 0.000 °C		22600 psi
@Strain 1.26 %,
Temperature 32.0 °F		DAM; ISO 527
 160 MPa
@Strain 1.26 %,
Temperature -20.0 °C		23200 psi
@Strain 1.26 %,
Temperature -4.00 °F		DAM; ISO 527
 162 MPa
@Strain 1.54 %,
Temperature 23.0 °C		23500 psi
@Strain 1.54 %,
Temperature 73.4 °F		DAM; ISO 527
 172 MPa
@Strain 1.76 %,
Temperature 23.0 °C		24900 psi
@Strain 1.76 %,
Temperature 73.4 °F		DAM; ISO 527
 172 MPa
@Strain 1.47 %,
Temperature 0.000 °C		24900 psi
@Strain 1.47 %,
Temperature 32.0 °F		DAM; ISO 527
 175 MPa
@Strain 1.47 %,
Temperature -20.0 °C		25400 psi
@Strain 1.47 %,
Temperature -4.00 °F		DAM; ISO 527
 179 MPa
@Strain 1.98 %,
Temperature 23.0 °C		26000 psi
@Strain 1.98 %,
Temperature 73.4 °F		DAM; ISO 527
 183 MPa
@Strain 2.20 %,
Temperature 23.0 °C		26500 psi
@Strain 2.20 %,
Temperature 73.4 °F		DAM; Break; ISO 527
 184 MPa
@Strain 1.68 %,
Temperature 0.000 °C		26700 psi
@Strain 1.68 %,
Temperature 32.0 °F		DAM; ISO 527
 188 MPa
@Strain 1.68 %,
Temperature -20.0 °C		27300 psi
@Strain 1.68 %,
Temperature -4.00 °F		DAM; ISO 527
 195 MPa
@Strain 1.89 %,
Temperature 0.000 °C		28300 psi
@Strain 1.89 %,
Temperature 32.0 °F		DAM; ISO 527
 199 MPa
@Strain 1.89 %,
Temperature -20.0 °C		28900 psi
@Strain 1.89 %,
Temperature -4.00 °F		DAM; ISO 527
 203 MPa
@Strain 2.10 %,
Temperature 0.000 °C		29400 psi
@Strain 2.10 %,
Temperature 32.0 °F		DAM; Break; ISO 527
 207 MPa
@Strain 2.10 %,
Temperature -20.0 °C		30000 psi
@Strain 2.10 %,
Temperature -4.00 °F		DAM; Break; ISO 527
Elongation at Break  3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		DAM; ASTM D638
 3.5 %
@Temperature 23.0 °C		3.5 %
@Temperature 73.4 °F		DAM; ISO 527
 6.0 %
@Temperature 23.0 °C		6.0 %
@Temperature 73.4 °F		50%RH; ASTM D638
 6.0 %
@Temperature 23.0 °C		6.0 %
@Temperature 73.4 °F		50%RH; ISO 527
Tensile Modulus  6.00 GPa
@Temperature 23.0 °C		870 ksi
@Temperature 73.4 °F		50%RH; ISO 527
 9.80 GPa
@Temperature 23.0 °C		1420 ksi
@Temperature 73.4 °F		DAM; ISO 527
Flexural Modulus  4.48 GPa
@Temperature 23.0 °C		650 ksi
@Temperature 73.4 °F		50%RH; ASTM D790
 8.20 GPa
@Temperature 23.0 °C		1190 ksi
@Temperature 73.4 °F		DAM; ISO 178
 8.82 GPa
@Temperature 23.0 °C		1280 ksi
@Temperature 73.4 °F		DAM; ASTM D790
Shear Modulus  0.000 GPa
@Temperature 228 °C		0.000 ksi
@Temperature 442 °F		DAM; ISO 6721
 0.0620 GPa
@Temperature 224 °C		8.99 ksi
@Temperature 435 °F		DAM; ISO 6721
 0.152 GPa
@Temperature 220 °C		22.0 ksi
@Temperature 428 °F		DAM; ISO 6721
 0.199 GPa
@Temperature 218 °C		28.9 ksi
@Temperature 424 °F		DAM; ISO 6721
 0.283 GPa
@Temperature 214 °C		41.0 ksi
@Temperature 417 °F		DAM; ISO 6721
 0.346 GPa
@Temperature 210 °C		50.2 ksi
@Temperature 410 °F		DAM; ISO 6721
 0.408 GPa
@Temperature 204 °C		59.2 ksi
@Temperature 399 °F		DAM; ISO 6721
 0.446 GPa
@Temperature 200 °C		64.7 ksi
@Temperature 392 °F		DAM; ISO 6721
 0.489 GPa
@Temperature 194 °C		70.9 ksi
@Temperature 381 °F		DAM; ISO 6721
 0.510 GPa
@Temperature 190 °C		74.0 ksi
@Temperature 374 °F		DAM; ISO 6721
 0.545 GPa
@Temperature 180 °C		79.0 ksi
@Temperature 356 °F		DAM; ISO 6721
 0.569 GPa
@Temperature 170 °C		82.5 ksi
@Temperature 338 °F		DAM; ISO 6721
 0.586 GPa
@Temperature 160 °C		85.0 ksi
@Temperature 320 °F		DAM; ISO 6721
 0.600 GPa
@Temperature 150 °C		87.0 ksi
@Temperature 302 °F		DAM; ISO 6721
 0.610 GPa
@Temperature 140 °C		88.5 ksi
@Temperature 284 °F		DAM; ISO 6721
 0.619 GPa
@Temperature 130 °C		89.8 ksi
@Temperature 266 °F		DAM; ISO 6721
 0.629 GPa
@Temperature 120 °C		91.2 ksi
@Temperature 248 °F		DAM; ISO 6721
 0.639 GPa
@Temperature 110 °C		92.7 ksi
@Temperature 230 °F		DAM; ISO 6721
 0.655 GPa
@Temperature 100 °C		95.0 ksi
@Temperature 212 °F		DAM; ISO 6721
 0.683 GPa
@Temperature 90.0 °C		99.1 ksi
@Temperature 194 °F		DAM; ISO 6721
 0.728 GPa
@Temperature 80.0 °C		106 ksi
@Temperature 176 °F		DAM; ISO 6721
 0.817 GPa
@Temperature 70.0 °C		118 ksi
@Temperature 158 °F		DAM; ISO 6721
 0.991 GPa
@Temperature 60.0 °C		144 ksi
@Temperature 140 °F		DAM; ISO 6721
 1.374 GPa
@Temperature 50.0 °C		199.3 ksi
@Temperature 122 °F		DAM; ISO 6721
 1.666 GPa
@Temperature 40.0 °C		241.6 ksi
@Temperature 104 °F		DAM; ISO 6721
 1.784 GPa
@Temperature 30.0 °C		258.8 ksi
@Temperature 86.0 °F		DAM; ISO 6721
 1.857 GPa
@Temperature 20.0 °C		269.3 ksi
@Temperature 68.0 °F		DAM; ISO 6721
 1.913 GPa
@Temperature 10.0 °C		277.5 ksi
@Temperature 50.0 °F		DAM; ISO 6721
 1.948 GPa
@Temperature 0.000 °C		282.5 ksi
@Temperature 32.0 °F		DAM; ISO 6721
 1.964 GPa
@Temperature -10.0 °C		284.9 ksi
@Temperature 14.0 °F		DAM; ISO 6721
 1.975 GPa
@Temperature -20.0 °C		286.5 ksi
@Temperature -4.00 °F		DAM; ISO 6721
 1.993 GPa
@Temperature -30.0 °C		289.1 ksi
@Temperature -22.0 °F		DAM; ISO 6721
 2.026 GPa
@Temperature -40.0 °C		293.9 ksi
@Temperature -40.0 °F		DAM; ISO 6721
 2.081 GPa
@Temperature -50.0 °C		301.8 ksi
@Temperature -58.0 °F		DAM; ISO 6721
Izod Impact, Notched  1.33 J/cm
@Temperature 23.0 °C		2.49 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D256
 2.13 J/cm
@Temperature 23.0 °C		3.99 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D256
Izod Impact, Unnotched  10.66 J/cm
@Temperature 23.0 °C		19.97 ft-lb/in
@Temperature 73.4 °F		DAM; ASTM D4812
 13.3 J/cm
@Temperature 23.0 °C		24.9 ft-lb/in
@Temperature 73.4 °F		50%RH; ASTM D4812
Izod Impact, Notched (ISO)  11.0 kJ/m²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1A
 11.0 kJ/m²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 180/1A
 15.0 kJ/m²
@Temperature 23.0 °C		7.14 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1A
 20.0 kJ/m²
@Temperature 23.0 °C		9.52 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 180/1A
Izod Impact, Unnotched (ISO)  90.0 kJ/m²
@Temperature -30.0 °C		42.8 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 180/1U
 100 kJ/m²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 180/1U
Charpy Impact Unnotched  8.00 J/cm²
@Temperature -30.0 °C		38.1 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eU
 8.40 J/cm²
@Temperature -30.0 °C		40.0 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eU
 9.70 J/cm²
@Temperature 23.0 °C		46.2 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eU
 10.0 J/cm²
@Temperature 23.0 °C		47.6 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eU
Charpy Impact, Notched  1.10 J/cm²
@Temperature -40.0 °C		5.23 ft-lb/in²
@Temperature -40.0 °F		DAM; ISO 179/1eA
 1.10 J/cm²
@Temperature -30.0 °C		5.23 ft-lb/in²
@Temperature -22.0 °F		DAM; ISO 179/1eA
 1.60 J/cm²
@Temperature 23.0 °C		7.61 ft-lb/in²
@Temperature 73.4 °F		DAM; ISO 179/1eA
 2.10 J/cm²
@Temperature -30.0 °C		9.99 ft-lb/in²
@Temperature -22.0 °F		50%RH; ISO 179/1eA
 2.30 J/cm²
@Temperature 23.0 °C		10.9 ft-lb/in²
@Temperature 73.4 °F		50%RH; ISO 179/1eA
Tensile Creep Modulus, 1 hour 5500 MPa
@Temperature 23.0 °C		798000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.0770 %,
Temperature 90.0 °C		522 psi
@Strain 0.0770 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.0930 %,
Temperature 90.0 °C		522 psi
@Strain 0.0930 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 5.50 MPa
@Strain 0.0800 %,
Temperature 23.0 °C		798 psi
@Strain 0.0800 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 5.50 MPa
@Strain 0.0890 %,
Temperature 23.0 °C		798 psi
@Strain 0.0890 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.166 %,
Temperature 60.0 °C		870 psi
@Strain 0.166 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.145 %,
Temperature 60.0 °C		870 psi
@Strain 0.145 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.155 %,
Temperature 90.0 °C		1040 psi
@Strain 0.155 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.187 %,
Temperature 90.0 °C		1040 psi
@Strain 0.187 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 10.8 MPa
@Strain 0.283 %,
Temperature 90.0 °C		1570 psi
@Strain 0.283 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 10.8 MPa
@Strain 0.235 %,
Temperature 90.0 °C		1570 psi
@Strain 0.235 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 11.0 MPa
@Strain 0.181 %,
Temperature 23.0 °C		1600 psi
@Strain 0.181 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 11.0 MPa
@Strain 0.163 %,
Temperature 23.0 °C		1600 psi
@Strain 0.163 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.334 %,
Temperature 60.0 °C		1740 psi
@Strain 0.334 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.290 %,
Temperature 60.0 °C		1740 psi
@Strain 0.290 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 14.4 MPa
@Strain 0.320 %,
Temperature 90.0 °C		2090 psi
@Strain 0.320 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 14.4 MPa
@Strain 0.382 %,
Temperature 90.0 °C		2090 psi
@Strain 0.382 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 16.5 MPa
@Strain 0.280 %,
Temperature 23.0 °C		2390 psi
@Strain 0.280 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 16.5 MPa
@Strain 0.252 %,
Temperature 23.0 °C		2390 psi
@Strain 0.252 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.409 %,
Temperature 90.0 °C		2610 psi
@Strain 0.409 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.485 %,
Temperature 90.0 °C		2610 psi
@Strain 0.485 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.504 %,
Temperature 60.0 °C		2610 psi
@Strain 0.504 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.437 %,
Temperature 60.0 °C		2610 psi
@Strain 0.437 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 21.6 MPa
@Strain 0.592 %,
Temperature 90.0 °C		3130 psi
@Strain 0.592 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 21.6 MPa
@Strain 0.506 %,
Temperature 90.0 °C		3130 psi
@Strain 0.506 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 22.0 MPa
@Strain 0.389 %,
Temperature 23.0 °C		3190 psi
@Strain 0.389 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 22.0 MPa
@Strain 0.351 %,
Temperature 23.0 °C		3190 psi
@Strain 0.351 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.677 %,
Temperature 60.0 °C		3480 psi
@Strain 0.677 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.586 %,
Temperature 60.0 °C		3480 psi
@Strain 0.586 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 25.2 MPa
@Strain 0.611 %,
Temperature 90.0 °C		3650 psi
@Strain 0.611 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 25.2 MPa
@Strain 0.705 %,
Temperature 90.0 °C		3650 psi
@Strain 0.705 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 27.5 MPa
@Strain 0.514 %,
Temperature 23.0 °C		3990 psi
@Strain 0.514 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 27.5 MPa
@Strain 0.465 %,
Temperature 23.0 °C		3990 psi
@Strain 0.465 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 28.8 MPa
@Strain 0.725 %,
Temperature 90.0 °C		4180 psi
@Strain 0.725 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 28.8 MPa
@Strain 0.824 %,
Temperature 90.0 °C		4180 psi
@Strain 0.824 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.856 %,
Temperature 60.0 °C		4350 psi
@Strain 0.856 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.737 %,
Temperature 60.0 °C		4350 psi
@Strain 0.737 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 32.4 MPa
@Strain 0.852 %,
Temperature 90.0 °C		4700 psi
@Strain 0.852 %,
Temperature 194 °F		50%RH; 1h; Isochronous; ISO 899
 32.4 MPa
@Strain 0.952 %,
Temperature 90.0 °C		4700 psi
@Strain 0.952 %,
Temperature 194 °F		50%RH; 10h; Isochronous; ISO 899
 33.0 MPa
@Strain 0.659 %,
Temperature 23.0 °C		4790 psi
@Strain 0.659 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 33.0 MPa
@Strain 0.597 %,
Temperature 23.0 °C		4790 psi
@Strain 0.597 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 36.0 MPa
@Strain 0.990 %,
Temperature 90.0 °C		5220 psi
@Strain 0.990 %,
Temperature 194 °F		50%RH; 1h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 0.892 %,
Temperature 60.0 °C		5220 psi
@Strain 0.892 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 36.0 MPa
@Strain 1.04 %,
Temperature 60.0 °C		5220 psi
@Strain 1.04 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 36.0 MPa
@Strain 1.09 %,
Temperature 90.0 °C		5220 psi
@Strain 1.09 %,
Temperature 194 °F		50%RH; 10h; Break; Isochronous; ISO 899
 38.5 MPa
@Strain 0.829 %,
Temperature 23.0 °C		5580 psi
@Strain 0.829 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 38.5 MPa
@Strain 0.752 %,
Temperature 23.0 °C		5580 psi
@Strain 0.752 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 42.0 MPa
@Strain 1.05 %,
Temperature 60.0 °C		6090 psi
@Strain 1.05 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 42.0 MPa
@Strain 1.24 %,
Temperature 60.0 °C		6090 psi
@Strain 1.24 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 44.0 MPa
@Strain 1.03 %,
Temperature 23.0 °C		6380 psi
@Strain 1.03 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 44.0 MPa
@Strain 0.938 %,
Temperature 23.0 °C		6380 psi
@Strain 0.938 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 48.0 MPa
@Strain 1.21 %,
Temperature 60.0 °C		6960 psi
@Strain 1.21 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 48.0 MPa
@Strain 1.44 %,
Temperature 60.0 °C		6960 psi
@Strain 1.44 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 49.5 MPa
@Strain 1.27 %,
Temperature 23.0 °C		7180 psi
@Strain 1.27 %,
Temperature 73.4 °F		50%RH; 10h; Isochronous; ISO 899
 49.5 MPa
@Strain 1.16 %,
Temperature 23.0 °C		7180 psi
@Strain 1.16 %,
Temperature 73.4 °F		50%RH; 1h; Isochronous; ISO 899
 54.0 MPa
@Strain 1.38 %,
Temperature 60.0 °C		7830 psi
@Strain 1.38 %,
Temperature 140 °F		50%RH; 1h; Isochronous; ISO 899
 54.0 MPa
@Strain 1.65 %,
Temperature 60.0 °C		7830 psi
@Strain 1.65 %,
Temperature 140 °F		50%RH; 10h; Isochronous; ISO 899
 55.0 MPa
@Strain 1.56 %,
Temperature 23.0 °C		7980 psi
@Strain 1.56 %,
Temperature 73.4 °F		50%RH; 10h; Break; Isochronous; ISO 899
 55.0 MPa
@Strain 1.43 %,
Temperature 23.0 °C		7980 psi
@Strain 1.43 %,
Temperature 73.4 °F		50%RH; 1h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 1.56 %,
Temperature 60.0 °C		8700 psi
@Strain 1.56 %,
Temperature 140 °F		50%RH; 1h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 1.88 %,
Temperature 60.0 °C		8700 psi
@Strain 1.88 %,
Temperature 140 °F		50%RH; 10h; Break; Isochronous; ISO 899
Tensile Creep Modulus, 1000 hours 4400 MPa
@Temperature 23.0 °C		638000 psi
@Temperature 73.4 °F		50%RH; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 23.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 90.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 0.000 MPa
@Strain 0.000 %,
Temperature 60.0 °C		0.000 psi
@Strain 0.000 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.121 %,
Temperature 90.0 °C		522 psi
@Strain 0.121 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.114 %,
Temperature 90.0 °C		522 psi
@Strain 0.114 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 3.60 MPa
@Strain 0.106 %,
Temperature 90.0 °C		522 psi
@Strain 0.106 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 5.50 MPa
@Strain 0.120 %,
Temperature 23.0 °C		798 psi
@Strain 0.120 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 5.50 MPa
@Strain 0.0980 %,
Temperature 23.0 °C		798 psi
@Strain 0.0980 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 5.50 MPa
@Strain 0.109 %,
Temperature 23.0 °C		798 psi
@Strain 0.109 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.233 %,
Temperature 60.0 °C		870 psi
@Strain 0.233 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.210 %,
Temperature 60.0 °C		870 psi
@Strain 0.210 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 6.00 MPa
@Strain 0.188 %,
Temperature 60.0 °C		870 psi
@Strain 0.188 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.229 %,
Temperature 90.0 °C		1040 psi
@Strain 0.229 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.242 %,
Temperature 90.0 °C		1040 psi
@Strain 0.242 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 7.20 MPa
@Strain 0.213 %,
Temperature 90.0 °C		1040 psi
@Strain 0.213 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 10.8 MPa
@Strain 0.322 %,
Temperature 90.0 °C		1570 psi
@Strain 0.322 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 10.8 MPa
@Strain 0.365 %,
Temperature 90.0 °C		1570 psi
@Strain 0.365 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 10.8 MPa
@Strain 0.345 %,
Temperature 90.0 °C		1570 psi
@Strain 0.345 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 11.0 MPa
@Strain 0.200 %,
Temperature 23.0 °C		1600 psi
@Strain 0.200 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 11.0 MPa
@Strain 0.221 %,
Temperature 23.0 °C		1600 psi
@Strain 0.221 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 11.0 MPa
@Strain 0.243 %,
Temperature 23.0 °C		1600 psi
@Strain 0.243 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.422 %,
Temperature 60.0 °C		1740 psi
@Strain 0.422 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.466 %,
Temperature 60.0 °C		1740 psi
@Strain 0.466 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 12.0 MPa
@Strain 0.378 %,
Temperature 60.0 °C		1740 psi
@Strain 0.378 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 14.4 MPa
@Strain 0.464 %,
Temperature 90.0 °C		2090 psi
@Strain 0.464 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 14.4 MPa
@Strain 0.491 %,
Temperature 90.0 °C		2090 psi
@Strain 0.491 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 14.4 MPa
@Strain 0.432 %,
Temperature 90.0 °C		2090 psi
@Strain 0.432 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 16.5 MPa
@Strain 0.373 %,
Temperature 23.0 °C		2390 psi
@Strain 0.373 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 16.5 MPa
@Strain 0.341 %,
Temperature 23.0 °C		2390 psi
@Strain 0.341 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 16.5 MPa
@Strain 0.309 %,
Temperature 23.0 °C		2390 psi
@Strain 0.309 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.572 %,
Temperature 60.0 °C		2610 psi
@Strain 0.572 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.586 %,
Temperature 90.0 °C		2610 psi
@Strain 0.586 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.638 %,
Temperature 60.0 °C		2610 psi
@Strain 0.638 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.621 %,
Temperature 90.0 °C		2610 psi
@Strain 0.621 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.703 %,
Temperature 60.0 °C		2610 psi
@Strain 0.703 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 18.0 MPa
@Strain 0.546 %,
Temperature 90.0 °C		2610 psi
@Strain 0.546 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 21.6 MPa
@Strain 0.663 %,
Temperature 90.0 °C		3130 psi
@Strain 0.663 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 21.6 MPa
@Strain 0.755 %,
Temperature 90.0 °C		3130 psi
@Strain 0.755 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 21.6 MPa
@Strain 0.711 %,
Temperature 90.0 °C		3130 psi
@Strain 0.711 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 22.0 MPa
@Strain 0.430 %,
Temperature 23.0 °C		3190 psi
@Strain 0.430 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 22.0 MPa
@Strain 0.471 %,
Temperature 23.0 °C		3190 psi
@Strain 0.471 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 22.0 MPa
@Strain 0.514 %,
Temperature 23.0 °C		3190 psi
@Strain 0.514 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.943 %,
Temperature 60.0 °C		3480 psi
@Strain 0.943 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.770 %,
Temperature 60.0 °C		3480 psi
@Strain 0.770 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 24.0 MPa
@Strain 0.857 %,
Temperature 60.0 °C		3480 psi
@Strain 0.857 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 25.2 MPa
@Strain 0.842 %,
Temperature 90.0 °C		3650 psi
@Strain 0.842 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 25.2 MPa
@Strain 0.894 %,
Temperature 90.0 °C		3650 psi
@Strain 0.894 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 25.2 MPa
@Strain 0.784 %,
Temperature 90.0 °C		3650 psi
@Strain 0.784 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 27.5 MPa
@Strain 0.670 %,
Temperature 23.0 °C		3990 psi
@Strain 0.670 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 27.5 MPa
@Strain 0.617 %,
Temperature 23.0 °C		3990 psi
@Strain 0.617 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 27.5 MPa
@Strain 0.565 %,
Temperature 23.0 °C		3990 psi
@Strain 0.565 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 28.8 MPa
@Strain 0.978 %,
Temperature 90.0 °C		4180 psi
@Strain 0.978 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 28.8 MPa
@Strain 1.04 %,
Temperature 90.0 °C		4180 psi
@Strain 1.04 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 28.8 MPa
@Strain 0.911 %,
Temperature 90.0 °C		4180 psi
@Strain 0.911 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.19 %,
Temperature 60.0 °C		4350 psi
@Strain 1.19 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 30.0 MPa
@Strain 1.08 %,
Temperature 60.0 °C		4350 psi
@Strain 1.08 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 30.0 MPa
@Strain 0.975 %,
Temperature 60.0 °C		4350 psi
@Strain 0.975 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 32.4 MPa
@Strain 1.12 %,
Temperature 90.0 °C		4700 psi
@Strain 1.12 %,
Temperature 194 °F		50%RH; 1000h; Isochronous; ISO 899
 32.4 MPa
@Strain 1.19 %,
Temperature 90.0 °C		4700 psi
@Strain 1.19 %,
Temperature 194 °F		50%RH; 10000h; Isochronous; ISO 899
 32.4 MPa
@Strain 1.04 %,
Temperature 90.0 °C		4700 psi
@Strain 1.04 %,
Temperature 194 °F		50%RH; 100h; Isochronous; ISO 899
 33.0 MPa
@Strain 0.845 %,
Temperature 23.0 °C		4790 psi
@Strain 0.845 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 33.0 MPa
@Strain 0.783 %,
Temperature 23.0 °C		4790 psi
@Strain 0.783 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 33.0 MPa
@Strain 0.721 %,
Temperature 23.0 °C		4790 psi
@Strain 0.721 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 36.0 MPa
@Strain 1.27 %,
Temperature 90.0 °C		5220 psi
@Strain 1.27 %,
Temperature 194 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 1.32 %,
Temperature 60.0 °C		5220 psi
@Strain 1.32 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 36.0 MPa
@Strain 1.44 %,
Temperature 60.0 °C		5220 psi
@Strain 1.44 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 36.0 MPa
@Strain 1.36 %,
Temperature 90.0 °C		5220 psi
@Strain 1.36 %,
Temperature 194 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 1.18 %,
Temperature 90.0 °C		5220 psi
@Strain 1.18 %,
Temperature 194 °F		50%RH; 100h; Break; Isochronous; ISO 899
 36.0 MPa
@Strain 1.19 %,
Temperature 60.0 °C		5220 psi
@Strain 1.19 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 38.5 MPa
@Strain 1.05 %,
Temperature 23.0 °C		5580 psi
@Strain 1.05 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 38.5 MPa
@Strain 0.974 %,
Temperature 23.0 °C		5580 psi
@Strain 0.974 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 38.5 MPa
@Strain 0.903 %,
Temperature 23.0 °C		5580 psi
@Strain 0.903 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 42.0 MPa
@Strain 1.56 %,
Temperature 60.0 °C		6090 psi
@Strain 1.56 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 42.0 MPa
@Strain 1.70 %,
Temperature 60.0 °C		6090 psi
@Strain 1.70 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 42.0 MPa
@Strain 1.41 %,
Temperature 60.0 °C		6090 psi
@Strain 1.41 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 44.0 MPa
@Strain 1.20 %,
Temperature 23.0 °C		6380 psi
@Strain 1.20 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 44.0 MPa
@Strain 1.28 %,
Temperature 23.0 °C		6380 psi
@Strain 1.28 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 44.0 MPa
@Strain 1.12 %,
Temperature 23.0 °C		6380 psi
@Strain 1.12 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 48.0 MPa
@Strain 1.82 %,
Temperature 60.0 °C		6960 psi
@Strain 1.82 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 48.0 MPa
@Strain 1.97 %,
Temperature 60.0 °C		6960 psi
@Strain 1.97 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 48.0 MPa
@Strain 1.65 %,
Temperature 60.0 °C		6960 psi
@Strain 1.65 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 49.5 MPa
@Strain 1.46 %,
Temperature 23.0 °C		7180 psi
@Strain 1.46 %,
Temperature 73.4 °F		50%RH; 1000h; Isochronous; ISO 899
 49.5 MPa
@Strain 1.54 %,
Temperature 23.0 °C		7180 psi
@Strain 1.54 %,
Temperature 73.4 °F		50%RH; 10000h; Isochronous; ISO 899
 49.5 MPa
@Strain 1.37 %,
Temperature 23.0 °C		7180 psi
@Strain 1.37 %,
Temperature 73.4 °F		50%RH; 100h; Isochronous; ISO 899
 54.0 MPa
@Strain 2.09 %,
Temperature 60.0 °C		7830 psi
@Strain 2.09 %,
Temperature 140 °F		50%RH; 1000h; Isochronous; ISO 899
 54.0 MPa
@Strain 2.26 %,
Temperature 60.0 °C		7830 psi
@Strain 2.26 %,
Temperature 140 °F		50%RH; 10000h; Isochronous; ISO 899
 54.0 MPa
@Strain 1.90 %,
Temperature 60.0 °C		7830 psi
@Strain 1.90 %,
Temperature 140 °F		50%RH; 100h; Isochronous; ISO 899
 55.0 MPa
@Strain 1.77 %,
Temperature 23.0 °C		7980 psi
@Strain 1.77 %,
Temperature 73.4 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 55.0 MPa
@Strain 1.85 %,
Temperature 23.0 °C		7980 psi
@Strain 1.85 %,
Temperature 73.4 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 55.0 MPa
@Strain 1.68 %,
Temperature 23.0 °C		7980 psi
@Strain 1.68 %,
Temperature 73.4 °F		50%RH; 100h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.37 %,
Temperature 60.0 °C		8700 psi
@Strain 2.37 %,
Temperature 140 °F		50%RH; 1000h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.55 %,
Temperature 60.0 °C		8700 psi
@Strain 2.55 %,
Temperature 140 °F		50%RH; 10000h; Break; Isochronous; ISO 899
 60.0 MPa
@Strain 2.17 %,
Temperature 60.0 °C		8700 psi
@Strain 2.17 %,
Temperature 140 °F		50%RH; 100h; Break; Isochronous; ISO 899
 
Electrical PropertiesMetricEnglishComments
Comparative Tracking Index  600 V
@Temperature 23.0 °C		600 V
@Temperature 73.4 °F		DAM; UL 746A
 >= 600 V
@Temperature 23.0 °C		>= 600 V
@Temperature 73.4 °F		DAM; UL 746A
 
Thermal PropertiesMetricEnglishComments
CTE, linear, Parallel to Flow  500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 500 µm/m-°C
@Temperature -40.0 - 23.0 °C		278 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 23.0 - 55.0 °C		278 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 500 µm/m-°C
@Temperature 55.0 - 160 °C		278 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
CTE, linear, Transverse to Flow  71.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		39.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ASTM E 831
 71.0 µm/m-°C
@Temperature -40.0 - 23.0 °C		39.4 µin/in-°F
@Temperature -40.0 - 73.4 °F		DAM; ISO 11359-1/-2
 102 µm/m-°C
@Temperature 23.0 - 55.0 °C		56.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ASTM E 831
 102 µm/m-°C
@Temperature 23.0 - 55.0 °C		56.7 µin/in-°F
@Temperature 73.4 - 131 °F		DAM; ISO 11359-1/-2
 119 µm/m-°C
@Temperature 55.0 - 160 °C		66.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ASTM E 831
 119 µm/m-°C
@Temperature 55.0 - 160 °C		66.1 µin/in-°F
@Temperature 131 - 320 °F		DAM; ISO 11359-1/-2
Deflection Temperature at 0.46 MPa (66 psi) 220 °C428 °FDAM; ISO 75-1/-2
 220 °C428 °FDAM; ASTM D648
Deflection Temperature at 1.8 MPa (264 psi) 210 °C410 °FDAM; ISO 75-1/-2
 210 °C410 °FDAM; ASTM D648
Glass Transition Temp, Tg 65.0 °C149 °F10°C/min; DAM; ISO 11357-1/-2
UL RTI, Electrical  65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
UL RTI, Mechanical with Impact  65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
 65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
UL RTI, Mechanical without Impact  65.0 °C
@Thickness 3.00 mm		149 °F
@Thickness 0.118 in		DAM; UL 746B
 65.0 °C
@Thickness 1.50 mm		149 °F
@Thickness 0.0591 in		DAM; UL 746B
 65.0 °C
@Thickness 0.750 mm		149 °F
@Thickness 0.0295 in		DAM; UL 746B
Flammability, UL94  HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; IEC 60695-11-10
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; IEC 60695-11-10
 HB
@Thickness 3.00 mm		HB
@Thickness 0.118 in		DAM; UL94
 HB
@Thickness 1.50 mm		HB
@Thickness 0.0591 in		DAM; UL94
 HB
@Thickness 0.750 mm		HB
@Thickness 0.0295 in		DAM; UL94
Oxygen Index 21 %21 %DAM; ISO 4589-1/-2
 
Processing PropertiesMetricEnglishComments
Melt Temperature 221 °C430 °F10°C/min; DAM; ISO 11357-1/-3
 270 °C518 °FDAM; Optimum
 260 - 280 °C500 - 536 °FDAM
Mold Temperature 70.0 - 120 °C158 - 248 °FDAM
 100 °C212 °FDAM; optimum
Drying Temperature 80.0 °C176 °FDAM
Dry Time 2.00 - 4.00 hour2.00 - 4.00 hourDAM
Moisture Content <= 0.20 %<= 0.20 %DAM
 
Descriptive Properties
AdditiveLubricantDAM
AppearanceNatural ColorDAM
Drying RecommendedYes, if moisture content of resin exceeds recommended levelDAM
FeaturesGeneral PurposeDAM
 Gloss, HighDAM
 Stiffness, GoodDAM
 Strength, GoodDAM
 Surface Finish, GoodDAM
FillerGlass fiber reinforcementDAM
FormsPelletsDAM
GenericNylon 6DAM
Material StatusCurrentDAM
Part Marking Code>PA6-GF30<ISO 11469; DAM
Polymer FamilyPolyamideDAM
Polymer TypePA6DAM
Processing MethodInjection MoldingDAM
Product CategoryGlass Reinforced ResinsDAM
Region Available - GlobalYesDAM
Resin IdentificationPA6-GF30ISO 1043; DAM
RoHS ComplianceContact ManufacturerDAM
Ultrasonic WeldableYesDAM
UsesAppliance ComponentsDAM
 High Gloss ApplicationsDAM
 Industrial ApplicationsDAM
 Sporting GoodsDAM

转载请注明: 转自中国塑胶原料之家 http://www.su-jiao.com/wuxingbiao/

本文链接: http://www.su-jiao.com/yuanliaoku/show-46746.html

免责声明: 本文 DuPont Performance Polymers Zytel® 73G30L NC010 Nylon 6 仅代表作者个人观点，中国塑胶原料之家无关。中国塑胶原料之家网所转载的内容，其版权均由原作者和资料提供方所拥有！如因作品版权问题需要处理，请与我们联络

该类别其他物性信息

塑胶原料之家，专业塑料网站、原料报价网站，免费发布塑胶供求信息。塑胶原料之家为您提供塑料供应、塑料求购、塑料行情、塑料展会、塑料原料资讯服务。

2008-2015 塑料|塑胶原料|物性表大全|UL黄卡|SGS报告查询|最新价格--塑胶原料之家

沪ICP备15027283号-4