- 熔体流动速率 [g/10min]: 1.9
- 拉伸强度 [MPa]: 76.0
- 透光率 [%]: 80.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Melt Flow | 1.9 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.9 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 76.0 MPa | 11000 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 7.0 % | 7.0 % | 50 mm/min |
| Tensile Modulus | 2.23 GPa | 323 ksi | 1 mm/min |
| Electrical Properties | Metric | English | Comments |
| Dissipation Factor | 0.000304 @Frequency 100 Hz | 0.000304 @Frequency 100 Hz | |
| 0.000307 @Frequency 1e+6 Hz | 0.000307 @Frequency 1e+6 Hz | ||
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 92.0 µm/m-°C @Temperature 20.0 °C | 51.1 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 88.0 °C | 190 °F | |
| Glass Transition Temp, Tg | 130 °C | 266 °F | 10°C/min |
| Flammability, UL94 | V-2 @Thickness 1.60 mm | V-2 @Thickness 0.0630 in | |
| Optical Properties | Metric | English | Comments |
| Transmission, Visible | 80 % | 80 % | Mfr. reports 'Transparent' but doesn't quantify. |