- 熔体流动速率 [g/10min]: 2.5
- 密度 [g/cm3]: 1.01
- 拉伸强度 [MPa]: 41.0
- 热变形温度 [℃]: 135.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.01 g/cc | 0.0365 lb/in³ | |
| Melt Flow | 2.5 g/10 min @Load 2.16 kg, Temperature 235 °C | 2.5 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 41.0 MPa | 5950 psi | 50 mm/min |
| Elongation at Break | >= 50 % | >= 50 % | Nominal Strain; 50 mm/min |
| Elongation at Yield | 8.0 % | 8.0 % | 50 mm/min |
| Tensile Modulus | 1.38 GPa | 200 ksi | 1 mm/min |
| Charpy Impact Unnotched | NB | NB | |
| NB | NB | Low Temp | |
| Charpy Impact, Notched | 2.50 J/cm² | 11.9 ft-lb/in² | |
| 0.770 J/cm² @Temperature -30.0 °C | 3.66 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | |
| Surface Resistance | 1.00e+14 ohm | 1.00e+14 ohm | |
| Dielectric Strength | 30.0 kV/mm | 762 kV/in | |
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 100 µm/m-°C @Temperature 20.0 °C | 55.6 µin/in-°F @Temperature 68.0 °F | |
| Melting Point | 174 °C | 345 °F | (Dry) |
| Deflection Temperature at 0.46 MPa (66 psi) | 135 °C | 275 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 55.0 °C | 131 °F | |
| Vicat Softening Point | 142 °C | 288 °F | 50°C/hr; 50N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| V-2 @Thickness 3.20 mm | V-2 @Thickness 0.126 in | ||