- 熔体流动速率 [g/10min]: 4.6
- 密度 [g/cm3]: 1.1
- 弯曲强度 [MPa]: 132.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.10 g/cc | 0.0397 lb/in³ | |
| Melt Flow | 4.6 g/10 min @Load 2.16 kg, Temperature 235 °C | 4.6 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 132 MPa | 19100 psi | 5 mm/min |
| Elongation at Break | 5.0 % | 5.0 % | 5 mm/min |
| Tensile Modulus | 12.6 GPa | 1830 ksi | 1 mm/min |
| Charpy Impact Unnotched | 5.90 J/cm² | 28.1 ft-lb/in² | |
| 5.90 J/cm² @Temperature -30.0 °C | 28.1 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.70 J/cm² | 8.09 ft-lb/in² | |
| 1.00 J/cm² @Temperature -30.0 °C | 4.76 ft-lb/in² @Temperature -22.0 °F | ||
| Thermal Properties | Metric | English | Comments |
| Melting Point | 174 °C | 345 °F | 10°C/min |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.10 mm | HB @Thickness 0.122 in | ||