- 熔体流动速率 [g/10min]: 1.1
- 密度 [g/cm3]: 1.41
- 弯曲强度 [MPa]: 145.0
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.41 g/cc | 0.0509 lb/in³ | |
| Melt Flow | 1.1 g/10 min @Load 2.16 kg, Temperature 235 °C | 1.1 g/10 min @Load 4.76 lb, Temperature 455 °F | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Ultimate | 145 MPa | 21000 psi | 5 mm/min |
| Elongation at Break | 4.0 % | 4.0 % | 5 mm/min |
| Tensile Modulus | 14.8 GPa | 2150 ksi | 1 mm/min |
| Charpy Impact Unnotched | 8.58 J/cm² | 40.8 ft-lb/in² | |
| 9.29 J/cm² @Temperature -30.0 °C | 44.2 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 2.29 J/cm² | 10.9 ft-lb/in² | |
| 1.72 J/cm² @Temperature -30.0 °C | 8.19 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 1.00e+12 ohm-cm | 1.00e+12 ohm-cm | |
| Surface Resistance | 1.00e+11 ohm | 1.00e+11 ohm | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | 30.0 µm/m-°C @Temperature 20.0 °C | 16.7 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 170 °C | 338 °F | |