- 密度 [g/cm3]: 1.097
- 缺口冲击强度: 5.3
- 弯曲模量 [MPa]: 7.338
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Density | 1.097 g/cc | 0.03963 lb/in³ | |||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 83.84 MPa | 12160 psi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Elongation at Break | 3.8 % | 3.8 % | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Tensile Modulus | 8.928 GPa | 1295 ksi | UNI EN ISO 527-1(97) and UNI EN ISO 527-2(97) | ||
| Flexural Strength | 133.0 MPa | 19290 psi | UNI EN ISO 14125: 2000 | ||
| Flexural Modulus | 7.338 GPa | 1064 ksi | UNI EN ISO 14125: 2000 | ||
| Izod Impact, Notched (ISO) | 5.30 kJ/m² | 2.52 ft-lb/in² | ISO 180:2000 | ||
| Izod Impact, Unnotched (ISO) | 19.26 kJ/m² | 9.165 ft-lb/in² | ISO 180:2000 | ||
| Charpy Impact Unnotched | 2.243 J/cm² | 10.67 ft-lb/in² | ISO 179-1:2007 | ||
| Charpy Impact, Notched | 0.472 J/cm² | 2.25 ft-lb/in² | ISO 179-1:2007 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | <= 1e+8 ohm-cm | <= 1e+8 ohm-cm | ASTM D257-93 | ||
| Surface Resistance | <= 1e+8 ohm | <= 1e+8 ohm | ASTM D257-93 | ||
| Thermal Properties | Metric | English | Comments | ||
| Melting Point | 179.3 °C | 354.7 °F | ISO 11357-2 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 173.4 °C | 344.1 °F | ISO 75-2 TYPE A | ||
| Vicat Softening Point | 176.1 °C | 349.0 °F | 10 N; ISO 306 TYPE A50 | ||
| Descriptive Properties | |||||
| Color | Black | ||||
| Surface Finish | 1.8 Ra µm | After Finishing | |||
| 6.0 Ra µm | After SLS Process | ||||