- 密度 [g/cm3]: 1.28
- 吸水率 [%]: 1.1
Physical Properties | Metric | English | Comments | ||
---|---|---|---|---|---|
Density | 1.28 g/cc | 0.0462 lb/in³ | ISO 1183 | ||
Water Absorption | 1.1 % | 1.1 % | ISO 62 | ||
Moisture Absorption | 0.600 % | 0.600 % | ISO 62 | ||
Linear Mold Shrinkage, Flow | 0.0010 cm/cm | 0.0010 in/in | ISO 294-4, 2577 | ||
Linear Mold Shrinkage, Transverse | 0.0080 cm/cm | 0.0080 in/in | ISO 294-4, 2577 | ||
Mechanical Properties | Metric | English | Comments | ||
Hardness, Shore D | 81 | 81 | conditioned, 15s; ISO 868 | ||
83 | 83 | dry, 15s; ISO 868 | |||
Tensile Strength at Break | 110 MPa | 16000 psi | conditioned; ISO 527-1/-2 | ||
125 MPa | 18100 psi | dry; ISO 527-1/-2 | |||
Elongation at Break | 5.0 % | 5.0 % | dry; ISO 527-1/-2 | ||
7.0 % | 7.0 % | conditioned; ISO 527-1/-2 | |||
Tensile Modulus | 7.00 GPa | 1020 ksi | conditioned; ISO 527-1/-2 | ||
7.80 GPa | 1130 ksi | dry; ISO 527-1/-2 | |||
Charpy Impact Unnotched | 8.00 J/cm² | 38.1 ft-lb/in² | conditioned; ISO 179/1eU | ||
8.50 J/cm² | 40.4 ft-lb/in² | dry; ISO 179/1eU | |||
6.50 J/cm² @Temperature 30.0 °C | 30.9 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
7.00 J/cm² @Temperature 30.0 °C | 33.3 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
Charpy Impact, Notched | 1.50 J/cm² | 7.14 ft-lb/in² | dry; ISO 179/1eA | ||
1.50 J/cm² | 7.14 ft-lb/in² | conditioned; ISO 179/1eA | |||
1.00 J/cm² @Temperature 30.0 °C | 4.76 ft-lb/in² @Temperature 86.0 °F | dry; ISO 179/1eU | |||
1.00 J/cm² @Temperature 30.0 °C | 4.76 ft-lb/in² @Temperature 86.0 °F | conditioned; ISO 179/1eU | |||
Electrical Properties | Metric | English | Comments | ||
Volume Resistivity | 1.00e+6 ohm-cm | 1.00e+6 ohm-cm | dry; IEC 60093 | ||
1.00e+6 ohm-cm | 1.00e+6 ohm-cm | conditioned; IEC 60093 | |||
Surface Resistance | 1.00e+6 ohm | 1.00e+6 ohm | IEC 60093 | ||
Thermal Properties | Metric | English | Comments | ||
CTE, linear, Parallel to Flow | 50.0 µm/m-°C | 27.8 µin/in-°F | ISO 11359-1/-2 | ||
CTE, linear, Transverse to Flow | 120 µm/m-°C | 66.7 µin/in-°F | ISO 11359-1/-2 | ||
Melting Point | 178 °C | 352 °F | 10°C/min; ISO 11357-1/-3 | ||
Maximum Service Temperature, Air | 90.0 - 120 °C | 194 - 248 °F | long term; EMS | ||
150 °C | 302 °F | short term; EMS | |||
Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | ISO 75-1/-2 | ||
Deflection Temperature at 8.0 MPa | 90.0 °C | 194 °F | ISO 75-1/-2 | ||
Flammability, UL94 | HB | HB | IEC 60695-11-10 | ||
Descriptive Properties | |||||
Automotive | Fuel systems | ||||
Form | Granules | ||||
Processing | Injection Molding | ||||
Product Attributes | Hydrolysis resistant | ||||
Special Characteristics | Anti-static | ||||
High impact or impact modified | |||||
Improved heat resistance | |||||
Improved UV resistance (outdoor use) |