- 缺口冲击强度: 0.176
- 弯曲强度 [MPa]: 36.4
- 弯曲模量 [MPa]: 19.42
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.763 g/cc | 1.763 g/cc | ASTM D792 | ||
| Linear Mold Shrinkage | 0.0045 cm/cm | 0.0045 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength, Ultimate | 36.4 MPa | 5280 psi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Elongation at Break | 0.35 % | 0.35 % | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Tensile Modulus | 18.22 GPa | 2643 ksi | Type 1 - Rigids, 0.2 in/min; ASTM D638 | ||
| Flexural Strength | 68.40 MPa | 9921 psi | ASTM D790 | ||
| Flexural Modulus | 19.42 GPa | 2816 ksi | ASTM D790 | ||
| Izod Impact, Notched | 0.176 J/cm @Thickness 3.17 mm, Temperature 23.0 °C | 0.329 ft-lb/in @Thickness 0.125 in, Temperature 73.4 °F | Method A, Injection Molded; ASTM D256 | ||
| Electrical Properties | Metric | English | Comments | ||
| Surface Resistivity per Square | 22000 ohm | 22000 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Thermal Conductivity | >= 16.0 W/m-K | >= 111 BTU-in/hr-ft²-°F | ASTM C177 | ||
| Descriptive Properties | |||||
| Product Form | Pellets | ||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.