- 吸水率 [%]: 0.1
- 缺口冲击强度: 1.44
- 拉伸强度 [MPa]: 121.0
- 弯曲模量 [MPa]: 10.7
- 热变形温度 [℃]: 176.0
| Physical Properties | Metric | English | Comments | ||
|---|---|---|---|---|---|
| Specific Gravity | 1.27 g/cc | 1.27 g/cc | ASTM D792 | ||
| Water Absorption | 0.10 % @Time 86400 sec | 0.10 % @Time 24.0 hour | ASTM D570 | ||
| Linear Mold Shrinkage, Flow | 0.00020 - 0.0010 cm/cm | 0.00020 - 0.0010 in/in | ASTM D955 | ||
| Linear Mold Shrinkage, Transverse | 0.010 - 0.020 cm/cm | 0.010 - 0.020 in/in | ASTM D955 | ||
| Mechanical Properties | Metric | English | Comments | ||
| Tensile Strength at Break | 121 MPa | 17500 psi | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Strength, Yield | 121 MPa | 17500 psi | ASTM D638 | ||
| Elongation at Break | 4.1 % | 4.1 % | Type I, 5.1 mm/min; ASTM D638 | ||
| Tensile Modulus | 16.5 GPa | 2390 ksi | ASTM D638 | ||
| Flexural Strength | 190 MPa | 27600 psi | ASTM D790 | ||
| Flexural Modulus | 10.7 GPa | 1550 ksi | ASTM D790 | ||
| Izod Impact, Notched | 1.44 J/cm @Thickness 6.35 mm, Temperature 23.0 °C | 2.70 ft-lb/in @Thickness 0.250 in, Temperature 73.4 °F | Injection Molded; ASTM D256A | ||
| Coefficient of Friction, Dynamic | 0.13 | 0.13 | vs. Steel; ASTM D1894 | ||
| Coefficient of Friction, Static | 0.24 | 0.24 | vs. Steel; ASTM D1894 | ||
| Electrical Properties | Metric | English | Comments | ||
| Volume Resistivity | 100 - 10000 ohm-cm | 100 - 10000 ohm-cm | ASTM D257 | ||
| Surface Resistance | 100 - 10000 ohm | 100 - 10000 ohm | ASTM D257 | ||
| Thermal Properties | Metric | English | Comments | ||
| Deflection Temperature at 0.46 MPa (66 psi) | 176 °C | 349 °F | Unannealed; ASTM D648 | ||
| Deflection Temperature at 1.8 MPa (264 psi) | 166 °C | 331 °F | Unannealed; ASTM D648 | ||
| Processing Properties | Metric | English | Comments | ||
| Mold Temperature | 65.6 - 93.3 °C | 150 - 200 °F | |||
| Drying Temperature | 71.1 - 82.2 °C @Time 7200 sec | 160 - 180 °F @Time 2.00 hour | |||
| Descriptive Properties | |||||
| Appearance | Natural Color | ||||
| Features | Electrically Conductive | ||||
| Good Wear Resistance | |||||
| High Stiffness | |||||
| Lubricated | |||||
| Forms | Pellets | ||||
| Generic Name | Polyamide 12 (Nylon 12) | ||||
| Processing Method | Injection Molding | ||||
| Regional Availability | Africa & Middle East | ||||
| Asia Pacific | |||||
| Europe | |||||
| North America | |||||
| South America | |||||
| RoHS Compliance | RoHS Compliant | ||||
| Uses | Appliance Components | ||||
| Automotive Applications | |||||
| Bearings | |||||
| Business Equipment | |||||
| Consumer Applications | |||||
| Conveyor Parts | |||||
| Gears | |||||
| Industrial Applications | |||||
| Printer Parts | |||||
| Pulleys | |||||
| Rollers | |||||
Materials flagged as discontinued () are no longer part of the manufacturer’s standard product line according to our latest information. These materials may be available by special order, in distribution inventory, or reinstated as an active product. Data sheets from materials that are no longer available remain in MatWeb to assist users in finding replacement materials.