- 密度 [g/cm3]: 1.96
- 拉伸强度 [MPa]: 90.0
- 热变形温度 [℃]: 175.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.96 g/cc | 0.0708 lb/in³ | |
| Mechanical Properties | Metric | English | Comments |
| Tensile Strength, Yield | 90.0 MPa | 13100 psi | |
| Elongation at Break | 6.0 % | 6.0 % | |
| Elongation at Yield | 3.0 % | 3.0 % | |
| Modulus of Elasticity | 8.00 GPa | 1160 ksi | |
| Charpy Impact Unnotched | 5.00 J/cm² | 23.8 ft-lb/in² | |
| 5.00 J/cm² @Temperature -30.0 °C | 23.8 ft-lb/in² @Temperature -22.0 °F | ||
| Charpy Impact, Notched | 1.10 J/cm² | 5.24 ft-lb/in² | |
| 0.900 J/cm² @Temperature -30.0 °C | 4.28 ft-lb/in² @Temperature -22.0 °F | ||
| Electrical Properties | Metric | English | Comments |
| Electrical Resistivity | 6.00e+14 ohm-cm | 6.00e+14 ohm-cm | |
| Surface Resistance | >= 1.00e+15 ohm | >= 1.00e+15 ohm | |
| Dielectric Constant | 4.0 @Frequency 100 Hz | 4.0 @Frequency 100 Hz | |
| 4.0 @Frequency 1e+6 Hz | 4.0 @Frequency 1e+6 Hz | ||
| Dissipation Factor | 0.038 @Frequency 1e+6 Hz | 0.038 @Frequency 1e+6 Hz | |
| 0.055 @Frequency 100 Hz | 0.055 @Frequency 100 Hz | ||
| Comparative Tracking Index | 600 V | 600 V | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear, Parallel to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C | <= 27.8 µin/in-°F @Temperature 68.0 °F | |
| CTE, linear, Transverse to Flow | <= 50.0 µm/m-°C @Temperature 20.0 °C | <= 27.8 µin/in-°F @Temperature 68.0 °F | |
| Deflection Temperature at 0.46 MPa (66 psi) | 175 °C | 347 °F | |
| Deflection Temperature at 1.8 MPa (264 psi) | 160 °C | 320 °F | |
| Vicat Softening Point | 170 °C | 338 °F | 50°C/hr/50 N |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | ||