- 密度 [g/cm3]: 1.08
- 拉伸强度 [MPa]: 47.0
- 热变形温度 [℃]: 140.0
| Physical Properties | Metric | English | Comments |
|---|---|---|---|
| Density | 1.08 g/cc | 0.0390 lb/in³ | ISO 1183 |
| Mechanical Properties | Metric | English | Comments |
| Hardness, Shore D | 75 | 75 | ISO 868 |
| Tensile Strength, Yield | 47.0 MPa | 6820 psi | ISO 527-1/2 |
| Elongation at Break | 37 % | 37 % | ISO 527-1/2 |
| Elongation at Yield | 5.4 % | 5.4 % | ISO 527-1/2 |
| Tensile Modulus | 2.35 GPa | 341 ksi | ISO 527-1/-2 |
| Charpy Impact Unnotched | 9.00 J/cm² @Temperature -30.0 °C | 42.8 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eU |
| 9.50 J/cm² @Temperature 23.0 °C | 45.2 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eU | |
| Charpy Impact, Notched | 0.400 J/cm² @Temperature -30.0 °C | 1.90 ft-lb/in² @Temperature -22.0 °F | ISO 179/1eA |
| 0.570 J/cm² @Temperature 23.0 °C | 2.71 ft-lb/in² @Temperature 73.4 °F | ISO 179/1eA | |
| Electrical Properties | Metric | English | Comments |
| Volume Resistivity | 1.00e+14 ohm-cm | 1.00e+14 ohm-cm | IEC 60093 |
| Surface Resistance | 1.00e+13 ohm | 1.00e+13 ohm | IEC 60093 |
| Dielectric Constant | 5.0 @Frequency 1e+6 Hz | 5.0 @Frequency 1e+6 Hz | IEC 60250 |
| 6.0 @Frequency 100 Hz | 6.0 @Frequency 100 Hz | IEC 60250 | |
| Dielectric Strength | 22.0 kV/mm | 559 kV/in | K20/P50; IEC 60243-1 |
| Comparative Tracking Index | 275 V | 275 V | 100 drops value; IEC 60112 |
| 300 V | 300 V | Test Solution A CTI; IEC 60112 | |
| Thermal Properties | Metric | English | Comments |
| CTE, linear | 91.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 50.6 µin/in-°F @Temperature 73.4 - 131 °F | Longitudinal; ISO 11359, DIN 53752 |
| CTE, linear, Transverse to Flow | 87.0 µm/m-°C @Temperature 23.0 - 55.0 °C | 48.3 µin/in-°F @Temperature 73.4 - 131 °F | ISO 11359, DIN 53752 |
| Deflection Temperature at 0.46 MPa (66 psi) | 140 °C | 284 °F | ISO 75-1/-2 |
| Deflection Temperature at 1.8 MPa (264 psi) | 50.0 °C | 122 °F | ISO 75-1/-2 |
| Vicat Softening Point | 160 °C | 320 °F | Method B, 50 N; ISO 306 |
| 175 °C | 347 °F | Method A, 10 N; ISO 306 | |
| Flammability, UL94 | HB @Thickness 1.60 mm | HB @Thickness 0.0630 in | IEC 60695 |
| HB @Thickness 3.20 mm | HB @Thickness 0.126 in | IEC 60695 | |